Title: Adesão, propriedades mecânicas e microestrutura de materiais CAD/CAM à base de resina = Adhesion, mechanical properties and microstructure of resin-based CAD/CAM materials
Title Alternative: Adhesion, mechanical properties and microstructure of resin-based CAD/CAM materials
Author: Castro, Eduardo Fernandes de, 1993-
Advisor: Giannini, Marcelo, 1969-
Abstract: Resumo: Os objetivos deste trabalho foram investigar o efeito do armazenamento em água e de tratamentos de superfícies na resistência de união por cisalhamento (RUC) de dois cimentos resinosos a materiais CAD/CAM à base de resina (RC) e avaliar as propriedades mecânicas - módulo de elasticidade (ME) e resistência flexural (RF) - dos RCs. Adicionalmente, avaliou-se a composição e microestrutura das RCs. Três RCs (Enamic, Lava Ultimate, Cerasmart) e um compósito convencional indireto (Epricord) foram testados. Para cada material, sessenta placas (14 x 7 x 1 mm) foram preparadas para o ensaio de RUC e submetidas a três diferentes tratamentos de superfície: instruções do fabricante (IF), aplicação de plasma atmosférico não-térmico (NTAP) por 30 s e NTAP + agente de união (AU). Dois cimentos resinosos foram avaliados: RelyX Ultimate (RX) e Panavia V5 (V5). Dois cilindros de cimento resinoso (1,5 mm de diâmetro x 1,5 mm de altura) foram aderidos a cada placa (n = 10), sendo um testado após 24 h de armazenamento em água destilada e o outro após um ano. Vinte barras retangulares (12 x 2 x 1 mm) de cada material indireto foram confeccionadas e submetidas ao ensaio de flexão de três pontos após 24 h ou um ano de armazenamento em água para obtenção de valores de ME e RF (n = 10). As amostras fraturadas foram examinadas em espectroscopia dispersiva de raios-X (EDS) e microscópio eletrônico de varredura (MEV). Dados de RUC foram analisados pela ANOVA quatro fatores e dados de ME e RF por ANOVA dois fatores, seguidos de teste de Tukey ( =0,05). Os grupos IF obtiveram maiores valores de RUC que os grupos NTAP e NTAP + AU para todos os materiais indiretos, cimentos resinosos e tempos de armazenamento avaliados. De forma geral, RX obteve maiores valores de RUC aos materiais indiretos que V5, com exceção de alguns grupos do Epricord (IF). Após um ano, todos grupos mostraram reduções significativas no valor de RUC, exceto alguns grupos de IF. Com relação a ME e RF, Epricord obteve as menores médias. Dentre os materiais CAD/CAM, Cerasmart obteve a menor média de ME e a maior de RF, e Enamic o maior ME e a menor RF, em ambos tempos de armazenamento. As imagens de MEV e análises de EDS revelaram que os materiais apresentam diferentes composições e microestruturas. Alguns materiais indiretos testados mostraram alterações na adesão do cimento resinoso em função dos tratamentos e tempo, o qual também influenciou o ME e RF desses. As diferenças composicionais e estruturais foram determinantes para o comportamento das propriedades estudadas

Abstract: The purpose of this study was to investigate the effect of one-year water storage and surface treatments on shear bond strength (SBS) of two resin cements to resin-based CAD/CAM materials (RC) and evaluate the mechanical properties - elastic modulus (EM) and flexural strength (FS) - of RCs. Additionally, the compositions and microstructures of RCs were analyzed. Three RC materials (Enamic, Lava Ultimate, Cerasmart) and one conventional indirect composite (Epricord) were tested. For each material sixty plates (14 x 7 x 1 mm) were prepared for SBS test and submitted to three different surface treatments: manufacturer's instructions (MI), non-thermal atmospheric plasma (NTAP) application for 30 s and NTAP + bonding agent (BA). Two resin cements were tested: RelyX Ultimate (RX) and Panavia V5 (V5). Two resin cylinders (1.5 mm diameter x 1.5 mm height) were bonded to each plate (n = 10), one tested after 24-h in distilled water-storage and the other after one year. Twenty rectangular bars (12 x 2 x 1 mm) of each indirect material were prepared and submitted to 3-point flexural test after 24-h or one-year water storage to obtain EM and FS values (n = 10). Fractured samples were examined under energy dispersive x-ray spectroscopy (EDS) and scanning electron microscopy (SEM). SBS data were analyzed by four-way ANOVA, and EM and FS data by two-way ANOVA, followed by post-hoc Tukey's test ( =0.05). MI groups obtained higher SBS values than NTAP and NTAP + BA for all indirect materials, resin cements and storage periods tested. In general, RX displayed higher SBS means than V5, except for some groups of Epricord MI. After one year, all groups presented significant reduction of SBS, except for some MI groups. Epricord showed the lowest values of EM and FS. Among CAD/CAM materials, Cerasmart had the lowest EM and highest FS means, while Enamic had the highest EM and lowest FS means, for both storage periods. SEM images and EDS analyses showed that the RCs presented different compositions and microstructures. Some indirect materials tested showed alterations in resin cement adhesion according to surface treatment and storage time, which also influenced EM and FS. Compositional and structural differences were determinant on the performance of properties studied
Subject: Projeto auxiliado por computador
Resinas compostas
Resistencia ao cisalhamento
Gases em plasma
Módulo de Elasticidade
Language: Inglês
Editor: [s.n.]
Citation: CASTRO, Eduardo Fernandes de. Adesão, propriedades mecânicas e microestrutura de materiais CAD/CAM à base de resina = Adhesion, mechanical properties and microstructure of resin-based CAD/CAM materials. 2018. 1 recurso online (51 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/331135>. Acesso em: 3 set. 2018.
Date Issue: 2018
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Castro_EduardoFernandesDe_M.pdf35.83 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.