Title: Estudo da água não evaporável na hidratação do cimento Portland com escória de alto forno por meio de análise térmica
Title Alternative: Non-evaporable water on hydration of Portland cement with blast furnace slag by means of thermal analysis
Author: Masuela, Fábio Blas, 1986-
Advisor: Camarini, Gladis, 1958-
Abstract: Resumo: O concreto de cimento Portland é um dos materiais mais utilizado no mundo. Neste aspecto é de interesse técnico conhecer os mecanismos da cinética de hidratação do cimento Portland, uma vez que, atualmente, o mercado consome cada vez mais cimento Portland com adições minerais. O presente trabalho teve por objetivo investigar a água não evaporável e o grau de hidratação do cimento Portland com adição de escória de alto forno em temperaturas de cura de 20 °C, 40 °C e 60°C em pastas e argamassas com relações água/cimento 0,3 e 0,5. Os cimentos utilizados foram CP II E, CP III e CP V ARI de dois fabricantes, avaliados nas idades de 7, 28 e 90 dias. Para as pastas de cimento, foram realizados os ensaios de perda ao fogo a 600 °C e a 1000 °C, e análise termogravimetrica, ambos para obtenção da água não evaporável do cimento Portland. Para as argamassas foram ensaiadas a resistência à compressão e permeabilidade ao ar. De acordo com os resultados obtidos, os cimentos Portland com adições de escória de alto-forno apresentaram velocidade de reação inferior aos demais cimentos; entretanto, quando submetidos à cura térmica, apresentaram maior resistência à compressão. A análise estatística mostrou que há pouca divergência entre os dois fabricantes e conclui-se que é possível determinar o grau de hidratação por meio do ensaio de perda ao fogo a 600 °C e a 1000 °C

Abstract: The Portland cement concrete is one of the most commonly used material worldwide. In this sense, it is of technical interest to learn about the mechanisms of hydration kinetics of Portland cement, since the market is currently consuming more and more Portland cement with mineral additions. The purpose of this work was to investigate the contents of non-evaporable water and the degree of hydration of Portland cement with addition of blast furnace slag at curing temperatures of 20°C, 40°C and 60°C for pastes and mortars with water/cement ratios of 0.3 and 0.5. The CP II E, CP III and CP V ARI cements from two manufacturers were studied at the ages of 7, 28 and 90 days. For cement pastes, the tests of loss on ignition were analyzed at 600°C and at 1,000°C, as well as thermogravimetric analysis to get the non-evaporable water contents in Portland cement. For mortars, it were made compressive strength and air permeability tests. According to the obtained results, the speed of reaction of Portland cements with blast furnace slag additions was lower than that the ones without slag. However, when exposed to thermal curing, these cements have higher values of compressive strength. The statistical analysis has shown that there is little divergence between both manufacturers, and the conclusion is that it is possible to determine the degree of hydration by means of loss on ignition test at 600°C and at 1,000°C
Subject: Cimento portland
Hidratação
Análise térmica
Água
Escoria
Editor: [s.n.]
Citation: MASUELA, Fábio Blas. Estudo da água não evaporável na hidratação do cimento Portland com escória de alto forno por meio de análise térmica. 2016. 1 recurso online (124 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil, Arquitetura e Urbanismo, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/325714>. Acesso em: 31 ago. 2018.
Date Issue: 2016
Appears in Collections:FEC - Tese e Dissertação

Files in This Item:
File SizeFormat 
Masuela_FabioBlas_M.pdf3.74 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.