Title: Effect Of Acid Etching, Silane And Thermal Cycling On The Bond Strength Of Metallic Brackets To Ceramic
Author: Matos
Natália Regina Santos de; Costa
Ana Rosa; Valdrighi
Heloísa Cristina; Correr
Américo Bortolazzo; Vedovello
Silvia Amélia; Santamaria Jr
Milton; Correr-Sobrinho
Abstract: The aim of this study was to evaluate the effect of silanes, thermal cycling and acid etching on the shear bond strength (SBS) of metallic brackets to feldspathic ceramic. Feldspathic ceramic cylinders (Groups 1, 2, 5 and 6) were etched for 60 s with 10% hydrofluoric acid and Groups 3, 4, 7 and 8, without acid etching. Two layers of silane Clearfil Ceramic Primer (CCP, Groups 1 to 4) and two layers of RelyX Ceramic Primer (RCP, groups 5 to 8) were applied and dried for 60 s. Brackets were bonded to the cylinders with Transbond XT and light-activated for 40 s with Bluephase G2. All specimens were stored in deionized water at 37 °C for 24 h, and the specimens of groups 1, 3, 5 and 7 were submitted to 7,000 thermal cycles (5 °C/55 °C). After storage, the SBS test was performed at a crosshead speed of 1 mm/min. Data were subjected to three-way ANOVA and Tukey's post hoc test (α=0.05). The adhesive remnant index (ARI) was evaluated at 8x magnification. The SBS of CCP was significantly greater than of RCP (p<0.05), with or without thermal cycling. Thermal cycling significantly reduced the SBS (p<0.05). The groups submitted to acid etching showed significantly higher SBS than those without acid etching (p<0.05). In conclusion, thermal cycling reduced SBS for all groups. The best ceramic surface treatment for bracket bonding was achieved by acid etching and CCP silane. The ARI results showed predominance of score 0 for all groups.
Subject: Ceramic
Etching Acid
Thermal Cycling
Shear Bond Strength
Editor: Fundação Odontológica de Ribeirão Preto
Citation: Brazilian Dental Journal. Fundação Odontológica De Ribeirão Preto, v. 27, n. 6, p. 734 - 738
Rights: aberto
Date Issue: 2016
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File SizeFormat 
S0103-64402016000600734.pdf126.86 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.