Title: Nanotecnologia aplicada ao cimento de ionômero de vidro convencional = avaliação das propriedades físico-químicas e biológicas = Nanotechnology applied to conventional glass ionomer cement: physical-chemical and biological assesment
Title Alternative: Nanotechnology applied to conventional glass ionomer cement : physical-chemical and biological assesment
Author: Cibim, Daniela Dellosso, 1990-
Advisor: Kantovitz, Kamila Rosamilia
Abstract: Resumo: O dióxido de titânio (TiO2) tem sido sugerido como material promissor em diversas aplicações, incluindo materiais restauradores odontológicos. O presente estudo in vitro investigou a influência da incorporação de diferentes concentrações de nanotubos de TiO2 nas propriedades físico-químicas e biológicas do cimento de ionômero de vidro (CIV) convencional. Para essa finalidade, ao CIV (Ketac Molar EasyMix ¿ (KM)) foi incorporado diferentes concentrações de nanotubos de TiO2 (3%; 5%; 7% em peso) e a avaliação das propriedades físico-químicas foram realizadas por meio dos ensaios de: 1. Espectroscopia por energia dispersiva (EDS) (n=4) ¿ identificar as porcentagens atômicas de Ti dos corpos-de-prova (cdp=2x4 mm), quatro regiões foram selecionadas e visualizadas em aumento de 100X, distância de trabalho = 20 mm; 2. Rugosidade de superfície (RS) (n=8/cdp=2x4 mm) ¿ média de três leituras efetuadas em rugosímetro (1,25 mm de extensão/ cut-off de 0,25 mm); 3. Dureza de superfície (DS) (n=8/cdp=2x4 mm) ¿ cdp foi polido com lixa de 800-grit/1 minuto e três indentações realizadas em microdurômetro Knoop (50 g/10 s); 4. Análise da liberação de flúor (F) (n=12/cdp=2x4 mm) ¿ cdp foi imerso em diferentes soluções (Remineralizadora ¿ RE; pH=7 e Desmineralizadora ¿ DES; pH=4,3) a 37oC por 15 dias, e eletrodo específico realizou a leitura da concentração de flúor (ppm F-) nos 1o, 2o, 3o, 5o, 7o, 9o, 12o, 15o dias. As propriedades biológicas: 1. Citotoxicidade por meio do ensaio de MTT (n=3/cdp=2x8 mm) em quatro períodos de avaliação (6, 24, 48 e 72 h); 2. Morfologia celular por microscopia eletrônica de varredura (MEV) (n=2/cdp=2x8 mm); 3. Quantificação de fibras colágenas e não colágenas (n=3/cdp=2x8 mm) por coloração Sirius Red. Para essas análises foram utilizadas células de fibroblastos gengivais humanos, nas concentrações de: 1,5 x 104, 104 e 5 x 104, respectivamente. Dados de EDS, RS e DS foram submetidos à ANOVA e Tukey (p<0,05). Dados da quantificação de fluoretos e de fibras colágenas e não colágenas foram submetidos aos testes de Kruskal-Wallis e Friedman (p?0,05). ANOVA 2 fatores foi aplicada para os dados de MTT (p?0,05). A avaliação por meio de EDS detectou Ti nos grupos contendo 5 e 7% de TiO2, 6,13 ± 0,45 e 11,16 ± 0,55, respectivamente. KM + 5% de TiO2 demonstrou maiores valores de dureza de superfície (118,25 ± 4,21) e viabilidade celular quando comparados com KM sem adição de nanotubos. No entanto, KM contendo 7% de TiO2 apresentou o menor valor de dureza de superfície (75,13 ± 6,61). A liberação de flúor foi dependente do tempo analisado e observaram-se maiores resultados nos grupos com 5 e 7% de TiO2. A adição de TiO2, independente da concentração não afetou os valores de rugosidade. Pode se concluir que o uso da nanotecnologia associada ao CIV convencional afetou positivamente as suas propriedades físico-químicas, sem comprometer as propriedades biológicas

Abstract: Titanium dioxide (TiO2) has been suggested as a promising material in various applications including dental restorative materials. This in vitro study investigated the influence of the addition of different concentrations of TiO2 nanotubes in physical-chemical and biological properties of conventional glass ionomer cement (GIC). To this, GIC (Ketac Molar EasyMix) was associated with three different concentrations of TiO2 nanotubes (3%, 5%, 7% by weight) that were assessed regarding its physical-chemical properties: 1. Spectroscopy energy dispersive (EDS) (n=4) ¿ was used to identify the atomic percentages of Ti of specimens (2x4 mm), four regions were selected and viewed in increase of 100X, work distance of 20 nm; 2. Superficial roughness (SR) (n=8/specimens=2x4 mm) ¿ mean of three readings taken in surface roughness tester ¿ 1,25 mm in length/cut-off of 0,25 mm); 3. Surface Hardness (SH) (n=8/specimens=2x4 mm) ¿ Specimens were polished with 800-grit paper form/1 minute and three indentations made in Knoop microhardness (50 g/10 s); 4. Fluoride analysis (F) (n=8/specimens=2x4 mm) - specimens were immersed in different storage media: RE - remineralization solution - pH = 7,0; DE - demineralization solution - pH = 4,3) at 37oC for 15 days, and specific electrodes will be used to determine fluoride concentration (ppm F-) at 1st, 2nd, 3rd, 5th, 7th, 9th, 12th, 15th days. The biological properties: 1. Cell metabolism by MTT assay (n=3/specimens=2x8 mm) in four evaluation times (6, 24, 48 and 72 h); 2. Cell morphology by scanning electron microscopy (SEM) (n=2/specimens=2x8 mm); 3. Sirius Red (n=3/specimens=2x8 mm) ¿ stains collagenous and non-collagenous fibers. To these analyses were used human gingival fibroblasts cells, at concentrations: 1.5 x 104; 104 and 5 x 104, respectively. Data to EDS, SR and SH were submitted to ANOVA and Tukey¿s test (p<0.05). Data from fluoride release and quantification of collagen and non-collagen fibers were submitted to the Kruskal-Wallis and Friedman tests (p?0.05). For the MTT assay, data were analyzed by two-way ANOVA (p?0.05). Evaluation by EDS, detected Ti in groups containing 5 and 7% TiO2, 6.13 ± 0.45 and 11.16 ± 0.55, respectively. GIC containing 5% (w/w) TiO2 nanotubes increase the surface hardness (118.25 ± 4.21) and cell viability compared to the unmodified GIC. However, to GIC-containing 7% TiO2 nanotubes were found a decrease in the surface hardness (75.13 ± 6.61). Fluoride release was dependent on the analysis time and was observed higher results in groups 5 and 7% TiO2. The addition of TiO2, independent of concentration no affects roughness values. According to the results obtained, it can be concluded that the use of nanotechnology associated with conventional GIC positively influenced the physico-chemical properties without compromising the biological properties
Subject: Cárie dentária
Cimentos de ionômeros de vidro
Nanotecnologia
Titânio
Propriedades físicas e químicas
Language: Multilíngua
Editor: [s.n.]
Date Issue: 2016
Appears in Collections:FOP - Dissertação e Tese

Files in This Item:
File SizeFormat 
Cibim_DanielaDellosso_M.pdf1.83 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.