Title: Efeito da aplicação de vernizes fluoretados com diferentes formulações nas lesões iniciais de cárie artificiais em dentes decíduos = Effect of fluoride varnishapplication with different formulations on Effect of fluoride varnishapplication with different formulations on
Title Alternative: Effect of fluoride varnishapplication with different formulations on early artificial carious lesions in primary teeth
Author: Soares, Aline Laignier, 1989-
Advisor: Pascon, Fernanda Miori, 1977-
Abstract: Resumo: O objetivo neste estudo foi avaliar, in vitro, o efeito de três vernizes de fluoreto de sódio a 5% (NaF), sendo dois deles com formulação modificada (RECALDENT¿ - CPP-ACP e Tri-Cálcio Fosfato - TCP), em lesões de cárie iniciais em dentes decíduos, submetidas ao desafio cariogênico. Sessenta e quatro blocos de esmalte (4x4 mm) de dentes decíduos foram selecionados e as lesões iniciais foram produzidas utilizando-se solução desmineralizadora sub-saturada em relação à hidroxiapatita, por 16 horas. Estes blocos foram distribuídos aleatoriamente em 4 grupos (n=16): Controle Negativo ¿ água deionizada; Controle Positivo - Duraphat®(verniz de NaF a 5%); MI VarnishTM (verniz de NaF a 5% com RECALDENT¿ - CPP-ACP) e VanishTM (verniz de NaF a 5% com TCP). Em seguida, os materiais foram aplicados sob os blocos e armazenados em saliva artificial por 12 horas, e após remoção, os blocos foram submetidos à ciclagem de pH por 7 dias (solução desmineralizadora ¿ 2 horas; solução remineralizadora ¿ 22 horas). Os blocos foram seccionados e analisados quanto: perda mineral (dureza Knoop), à profundidade das lesões (microscopia de luz polarizada - MLP) e quantidade de cálcio (Ca) e fósforo (P) (espectroscopia por energia dispersiva - EDS). Para a dureza Knoop foram realizadas três fileiras de 12 impressões (10, 20, 30, 40, 50, 60, 80, 100, 120, 140, 160 e 180 µm) (25g/5s). Valores de dureza Knoop (KHN) foram obtidos e a variação do KHN (?S) foi calculada. Para a profundidade foram realizadas 3 medidas em cada lesão (em µm) e calculada a média. Para EDS, os espécimes foram observados em microscopia eletrônica de varredura e a quantidade de Ca, P e a relação Ca/P foi calculada nas regiões superficiais. Os resultados foram submetidos ao teste de normalidade Kolmogorov¿Smirnov. Os dados de ?S foram submetidos à ANOVA e ao teste de Tukey. Os dados da MLP, para comparação das áreas pré e pós-tratadas, foram submetidos ao teste-t pareado. Para a comparação entre os grupos, os dados da MLP e EDS foram submetidos ao teste de Kruskal-Wallis (?=5%). Não foi observada diferença significativa nos valores de ?S entre Duraphat®, MI Varnish¿ e Varnish¿, mas foi observada diferença entre os vernizes fluoretados e controle negativo (p<0,05), indicando efeitos positivos de tratamento com vernizes fluoretados. Os resultados de MLP não mostraram diferença significativa para o pré-tratamento (p=0,1548). O controle negativo apresentou aumento na profundidade da lesão e os grupos tratados apresentaram diminuição na profundidade da lesão (p=0,004). No entanto, não houve diferença significativa na porcentagem de alteração entre os grupos tratados com os vernizes (p=0,764). Em relação à análise EDS, não foi observada diferença significativa nas taxas de Ca, P e Ca/P entre os grupos (p>0,05). Pode-se concluir que todos os vernizes fluoretados, sejam apenas com fluoreto de sódio ou com adição de CPP-ACP ou TCP foram eficazes para promover a remineralização em lesões iniciais de cárie de dentes decíduos

Abstract: The aim of this study was evaluate the effect of three fluoride varnishes (5% NaF), two of them with modified formulation (Recaldent ¿ - CPP-ACP and Tri-Calcium Phosphate) in early caries lesion in primary teeth, submitted to cariogenic challenge. Sixty-four enamel blocs (4x4 mm) of primary teeth were selected and were produced using demineralizing sub-saturated solution concerning hydroxyapatite for 16h. This blocs were randomly divided into 4 groups (n = 16): Negative Control - deionized water; Positive Control - Duraphat® (5% NaF varnish); MI VarnishTM (NaF varnish with 5% Recaldent ¿ - CPP-ACP) and VanishTM (5% NaF varnish Tri-Calcium Phosphate - TCP). Then, the materials were applied in the blocks and stored in artificial saliva for 12 hours, were removed and subjected to pH cycling for 7 days (demineralizing solution - 2 hours; remineralizing solution - 22 hours). The specimens were sectioned and analyzed: mineral loss (Knoop hardness), the depth of lesions (polarized light microscopy - MLP) and the amount of calcium (Ca) and phosphorus (P) (energy dispersive spectroscopy - EDS). For Knoop hardness were performed three rows of 12 print (10, 20, 30, 40, 50, 60, 80, 100, 120, 140, 160 and 180 uM) (25g / 5s). Knoop hardness (KHN) was obtained and the variation of KHN (?S) was calculated. For depth were carried out 3 measures each lesion (in µm) and averaged. For SDS, the samples were observed by SEM and the amount of calcium and phosphorus was calculated in surface regions. The results were submitted to the Kolmogorov-Smirnov normality test. The data ?S were submitted to ANOVA and Tukey test. Data from the MLP, to compare the pre and post-treated areas were submitted to paired t-test. For comparison between groups, data from the MLP and EDS were submitted to the Kruskal-Wallis test (? = 5%). There was no significant difference in values between ?S Duraphat®, MI Varnish ¿ and Varnish ¿ but was difference between fluoride varnishes and negative control (p <0.05), demonstrating positive effects of treatment with fluoride varnishes. The results of MLP showed no significant difference to the pre-treatment (p = 0.1548). The negative control showed an increase in the depth of the lesion and treated groups showed decrease in the lesion depth (p = 0.004). However, there was no significant difference in the percentage change between the groups treated with varnish (p = 0.764). Regarding the EDS analysis, there was no significant difference in the Ca, P and Ca / P rates between groups (p> 0.05). It can be concluded that all fluoride varnishes, are only fluoride varnishes, sodium fluoride or CPP-ACP or TCP were effective to promote remineralization of initial carious lesions of deciduous teeth
Subject: Remineralização dentária
Compostos de flúor
Cárie dentária
Language: Inglês
Editor: [s.n.]
Date Issue: 2016
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Soares_AlineLaignier_M.pdf1.51 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.