Please use this identifier to cite or link to this item: http://repositorio.unicamp.br/jspui/handle/REPOSIP/321889
Full metadata record
DC FieldValueLanguage
dc.contributor.CRUESPUNIVERSIDADE ESTADUAL DE CAMPINASpt_BR
dc.descriptionOrientador: Marines Nobre dos Santos Uchoapt_BR
dc.descriptionTese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicabapt_BR
dc.format.extent1 recurso online ( 116 p.) : il., digital, arquivo PDF.pt_BR
dc.format.mimetypeapplication/pdfpt_BR
dc.relation.requiresRequisitos do sistema: Software para leitura de arquivo em PDFpt_BR
dc.typeTESE DIGITALpt_BR
dc.titleInvestigação dos efeitos do laser de dióxido de carbono 'lambda' = 10.6 µm, fluoreto e biofilme dentário na desmineralização do esmalte. Estudos in vitro e in situ = Investigation of carbon dioxide laser 'lambda' = 10.6 µm, fluoride and dental biofilm effects on enamel demineralization. In vitro and in situ studiespt_BR
dc.title.alternativeInvestigation of carbon dioxide laser 'lambda' = 10.6 µm, fluoride and dental biofilm effects on enamel demineralization. In vitro and in situ studiespt_BR
dc.contributor.authorZancopé, Bruna Raquel, 1988-pt_BR
dc.contributor.advisorNobre dos Santos, Marinês, 1956-pt_BR
dc.contributor.institutionUniversidade Estadual de Campinas. Faculdade de Odontologia de Piracicabapt_BR
dc.contributor.nameofprogramPrograma de Pós-Graduação em Odontologiapt_BR
dc.subjectLaserspt_BR
dc.subjectBiofilmept_BR
dc.subjectFlúorpt_BR
dc.subject.otherlanguageLasersen
dc.subject.otherlanguageBiofilmsen
dc.subject.otherlanguageFluorineen
dc.description.abstractResumo: O laser de dióxido de carbono (CO2) tem sido usado para modificar morfologicamente e quimicamente a superfície do esmalte dentário, bem como para torná-lo mais resistente à desmineralização. O objetivo geral desta tese foi investigar os efeitos do laser de CO2, associado ao fluoreto (F) e ao biofilme dentário na desmineralização do esmalte. Os estudos desenvolvidos são apresentados em quatro capítulos. O capítulo 1 avaliou os efeitos do biofilme dentário e da irradiação com o laser de CO2 (? = 10.6 µm) na progressão da lesão do esmalte dentário bovino. Para a formação do biofilme, 10 voluntários utilizaram dispositivos palatinos contendo 06 espécimes de esmalte bovino cada. O laser foi aplicado antes ou após a remoção do biofilme. Os espécimes foram submetidos ao teste de microdureza e análise por microscopia eletrônica de varredura (MEV). Este estudo demostrou que o biofilme sobre a superfície do esmalte não reduziu o efeito do laser de CO2 na redução da progressão da lesão de cárie. O Capítulo 2 avaliou, in vitro, os efeitos da irradiação com o laser de CO2 (? = 10,6 µm) sobre a formação de biofilme no esmalte dentário. Neste estudo, 96 espécimes de esmalte bovino foram divididos em 2 grupos: controle e laser de CO2. Os biofilmes foram cultivados sobre as amostras por 1, 3 e 5 dias sob desafio cariogênico intermitente e as superfícies irradiada e não irradiada foram avaliadas quanto ao peso seco, ao número de micro-organismos pela contagem de colônias viáveis, análise de polissacarídeos, análise PCR em tempo real e do ângulo de contato. A morfologia do biofilme foi caracterizada por microscopia de fluorescência e microscopia eletrônica de varredura por emissão de campo. Em conclusão, a irradiação com laser de CO2 modificou a superfície de energia e rompeu a formação do biofilme inicial. O capítulo 3 investigou os efeitos do laser de CO2 (? = 10,6 µm) e de produtos fluoretados na formação de CaF2 na superfície do esmalte e na progressão da lesão subsuperficial. Espécimes de esmalte decíduo desmineralizado foram distribuídos em grupos (n = 15): gel de flúor fosfato acidulado (FFA), fluoreto espuma, verniz fluoretado e laser de CO2. Os espécimes foram submetidos ao teste de microdureza e análise por MEV. A irradiação com o laser isolada ou combinada com produtos fluoretados inibiu a progressão da lesão. No entanto, nenhum efeito sinérgico foi observado. O Capítulo 4 avaliou, in situ, os efeitos do laser de CO2 (? = 10,6 µm) e do FFA na formação de fluoreto de cálcio (CaF2) e fluorapatita (FAp) sobre esmalte humano previamente desmineralizado. Avaliou-se também, os efeitos na progressão de lesão de cárie e na formação de fluoreto no biofilme. Um estudo in situ foi conduzido com 04 fases de 14 dias cada. Espécimes foram submetidos ao teste de microdureza, análise de concentração CaF2 e FAp e de F no biofilme. A maior formação de CaF2 e FAp decorrente da irradiação com laser de CO2 tornou o esmalte mais resistente a progressão da lesão de cárie subsuperficialpt
dc.description.abstractAbstract: Carbon Dioxide Laser (CO2) has been used to morphologically and chemically modify the dental enamel surface as well as to make this substrate more resistant to demineralization. The general objective of this thesis was to investigate the CO2 laser, fluoride (F) and dental biofilms effects on enamel demineralization. Four studies were developed and are presented in four chapters. Chapter 1 evaluated the effects of dental biofilm and CO2 laser (? = 10.6 µm) irradiation on enamel lesion progression of bovine tooth enamel. For biofilm formation, 10 volunteers wore palatal appliances containing 06 specimens of bovine enamel each. The laser irradiation was performed before and after biofilm removal. The specimens were submitted to microhardness test and scanning electron microscopy analysis (MEV). This study showed that biofilm covering enamel surface did not reduce the CO2 laser irradiation effect on reduction progression of dental caries lesion. Chapter 2 evaluated, in vitro, the CO2 laser (? = 10.6 µm) irradiation effects on biofilm formation in dental enamel. In this study, 96 bovine enamel specimens were divided into 2 groups: Control and CO2 laser. The biofilms were grown on the enamel specimens for 1, 3 and 5 days under intermittent cariogenic condition in the irradiated and not irradiated surface and were evaluated by dry weigh, counting of the number of microorganisms through viable colonies counting, polysaccharides analysis, quantitative real-time-PCR as well as by contact angle. The biofilms morphology was characterized by fluorescence microscopy and Field Emission Scanning Electron Microscopy. In conclusion CO2 laser irradiation modified the surface energy and disrupted the initial biofilm formation. Chapter 3 investigated the CO2 laser (? = 10.6 µm) effects and of the fluoridated products in calcium fluoride (CaF2) formation on the enamel surface and subsurface lesion progression. Demineralized primary enamel specimens were allocated in groups (n=15): Acidulated Phosphate Fluoride (APF) gel, fluoride foam and fluoride varnish and CO2 Laser. The specimens were submitted to microhardness test and MEV. Laser irradiation alone or combined with fluoridated products inhibited lesion progression However, no synergistic effect was observed, Chapter 1 evaluated, in situ, the CO2 laser (? = 10.6 µm) and APF effects on CaF2 and fluorapatite (FAp) formation on the surface of previously demineralized enamel specimens. It was also the aim of this study to evaluate these effects on carious lesions progression and on fluoride biofilm formation. An in situ study was conducted with 04 double-blind phases of 14 days each. Specimens were subjected to microhardness test, CaF2 and FAp concentration analysis and of the F on biofilm. The higher formation of CaF2 and FAp due to CO2 laser irradiation rendered the enamel more resistant to subsurface caries lesion progressionen
dc.publisher[s.n.]pt_BR
dc.date.issued2016pt_BR
dc.identifier.citationZANCOPÉ, Bruna Raquel. Investigação dos efeitos do laser de dióxido de carbono 'lambda' = 10.6 µm, fluoreto e biofilme dentário na desmineralização do esmalte. Estudos in vitro e in situ: Investigation of carbon dioxide laser 'lambda' = 10.6 µm, fluoride and dental biofilm effects on enamel demineralization. In vitro and in situ studies. 2016. 1 recurso online ( 116 p.). Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/321889>. Acesso em: 30 ago. 2018.pt_BR
dc.description.degreelevelDoutoradopt_BR
dc.description.degreedisciplineOdontopediatriapt_BR
dc.description.degreenameDoutora em Odontologiapt_BR
dc.contributor.committeepersonalnameFilho, Paulo Nelsonpt_BR
dc.contributor.committeepersonalnameFreitas, Patricia Moreira dept_BR
dc.contributor.committeepersonalnamePascon, Fernanda Mioript_BR
dc.contributor.committeepersonalnameVedovello, Silvia Amelia Scudelerpt_BR
dc.description.sponsordocumentnumber2012/02885-7pt_BR
dc.description.sponsordocumentnumber99999.002339/2015-03pt_BR
dc.date.available2018-08-30T12:04:17Z-
dc.date.accessioned2018-08-30T12:04:17Z-
dc.description.provenanceMade available in DSpace on 2018-08-30T12:04:17Z (GMT). No. of bitstreams: 1 Zancope_BrunaRaquel_D.pdf: 11559425 bytes, checksum: 7eadf8e949f7784df910df70c9a62f2f (MD5) Previous issue date: 2016en
dc.identifier.urihttp://repositorio.unicamp.br/jspui/handle/REPOSIP/321889-
dc.description.sponsorFAPESPpt_BR
dc.description.sponsorCAPESpt_BR
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Zancope_BrunaRaquel_D.pdf11.29 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.