Title: Estudo da resistência da união e da interface adesiva quanto à degradação da união de pinos de fibra de vidro e dentina radicular em função de diferentes materiais obturadores e agentes de limpeza = Study of bond strength and degradation of adhesive interface of glass fiber posts and root dentin regarding different filling materials and cleanning agents
Title Alternative: Study of bond strength and degradation of adhesive interface of glass fiber posts and root dentin regarding different filling materials and cleanning agents
Author: Iwamoto, Alexsandra Shizue, 1987-
Advisor: Pascon, Fernanda Miori, 1977-
Puppin-Rontani, Regina Maria, 1959-
Abstract: Resumo: O objetivo do presente estudo foi avaliar in vitro o efeito de materiais obturadores à base de hidróxido de cálcio e agentes de limpeza na degradação da interface adesiva entre pinos de fibra de vidro/cimento resinoso e dentina radicular nos períodos de armazenamento de 24 horas e 6 meses. Assim, esta tese foi apresentada em artigo único. Para isso, foram preparadas endodonticamente 270 raízes de dentes decíduos bovinos e estas foram distribuídas de acordo com os materiais obturadores: NF-sem material; CZO-Calen®+óxido de zinco; VI-Vitapex®. Após 7 dias, raízes foram desobturadas e subdivididas de acordo com os agentes de limpeza (n=10): NC-sem limpeza; ET-Etanol; TG-Tergenform®. A cimentação do pino de fibra de vidro foi realizada com cimento resinoso RelyX ARCTM após prévio condicionamento com ácido fosfórico a 35% e aplicação do sistema adesivo Adper Single Bond 2TM. As raízes foram seccionadas no terço cervical para obtenção de fatias (±1mm) e estas armazenadas de acordo com os tempos de degradação (24 horas e 6 meses). Após o período de degradação, espécimes foram avaliados quanto à resistência da união, padrão de fratura, infiltração por nitrato de prata e espessura da camada híbrida utilizando teste push-out, microscopia eletrônica de varredura e microscopia confocal de varredura à laser, respectivamente. Os dados foram submetidos à ANOVA três fatores e teste de Tukey (?=5%). Interação entre tempo de degradação x material obturador x agente de limpeza foi observada para a resistência da união e material obturador x agente de limpeza para a espessura da camada híbrida. Observou-se diminuição da resistência da união e espessura da camada híbrida e aumento da infiltração com o passar do tempo. Dados da resistência da união e espessura da camada híbrida não apresentaram diferença estatística entre os grupos de materiais obturadores sem limpeza (NF/NC, CZO/NC e VI/NC). Em 24 horas, CZO/ET apresentou maior resistência da união, com diferença para CZO/NC (24 horas), VI/ET (24 horas e 6 meses), NF/ET (6 meses) e CZO/ET (6 meses). Fraturas adesivas e mistas foram predominantes em 24 horas e 6 meses. TG em 24 horas apresentou menor infiltração com diferença estatística para NC. Em relação à espessura da camada híbrida, maiores espessuras foram encontradas para VI e TG com diferença para os grupos NF e CZO e NC e ET respectivamente. Ainda, CZO/TG e VI/TG apresentaram maior espessura da camada híbrida. Aos 6 meses, não foram encontradas diferenças estatísticas entre os grupos para a resistência da união, infiltração e espessura da camada híbrida. Concluiu-se que: (1) a qualidade e durabilidade da interface adesiva foram influenciadas pelos tempos de degradação; (2) os materiais obturadores não interferiram na interface adesiva ao longo do tempo; (3) agentes de limpeza interferiram na interface adesiva ao longo do tempo, principalmente quando associados aos materiais obturadores; e (4) obturação dos canais radiculares com CZO e limpeza com ET poderia ser indicada quando da indicação do uso de pinos de fibra de vidro em dentes decíduos

Abstract: This study evaluated in vitro the influence of different calcium hydroxide-based filling materials and cleaning agents on the degradation of adhesive interface between glass fiber post/resin cement and root dentin in storage time 24 h and 6 months. Thus, this thesis was presented in one article. Two hundred and seventy roots of bovine primary teeth were endodontically treated and assigned to filling materials groups: NF-no filling material; CZO-Calen®+zinc oxide; VI-Vitapex®. After 7 days, filling materials were removed and subdivided according to the cleaning agents (n=10): NC-no cleaning agent; ET-ethanol; TG-Tergenform®. Glass fiber posts were luted using resin cement RelyX ARCTM after etching with 35% phosphoric acid, rinsing and bonding with an adhesive system Adper Single Bond 2TM. Roots were sectioned in cervical third for obtain slices (± 1 mm) and water storage according the degradation time (24 h and 6 months). After this period, specimens were evaluated to bond strength test, failure pattern, leakage by silver nitrate and hybrid layer thickness using push-out test, scanning electron microscopy and confocal laser scanning microscopy, respectively. Data were submitted to three-way ANOVA and Tukey's test (?=5%). Interaction was observed between water storage time x filling material x cleaning agent for bond strength test and filling material x cleaning agent for hybrid layer thickness. It was observed leakage increased and bond strength and hybrid layer thickness decreased over time. Data from bond strength and hybrid layer thickness showed no significant difference between filling materials group without cleaning agent (NF/NC, CZO/NC and VI/NC). In 24 h, CZO/ET showed higher bond strength, significantly different for CZO/NC (24 h), VI/ET (24 h and 6 months), NF/ET (6 months) and CZO/ET (6 months). Adhesive and mixed failures were frequently observed in 24 h and 6 months. TG showed lower leakage with significant difference for NC in 24 h. In relation to hybrid layer thickness, the highest thickness was found for VI and TG with difference from NF and CZO and NC and ET, respectively. Still, CZO/TG and VI/TG showed higher hybrid layer thickness. In 6 months, it was not found significant difference between the groups for bond strength, leakage and hybrid layer thickness. It was concluded that: (1) quality and durability of the adhesive interface were influenced by the degradation time; (2) filling materials did not affect the adhesive interface over time; (3) cleaning agents affected the adhesive interface over time, mainly when associated with filling materials; and (4) filling root canal with CZO and cleaning with ET can be indicated when glass fiber post is used in primary teeth
Subject: Dentes deciduos
Pinos dentários
Resistencia ao cisalhamento
Infiltração dentária
Microscopia confocal
Editor: [s.n.]
Citation: IWAMOTO, Alexsandra Shizue. Estudo da resistência da união e da interface adesiva quanto à degradação da união de pinos de fibra de vidro e dentina radicular em função de diferentes materiais obturadores e agentes de limpeza = Study of bond strength and degradation of adhesive interface of glass fiber posts and root dentin regarding different filling materials and cleanning agents. 2016. 1 recurso online ( 57 p.). Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/321878>. Acesso em: 30 ago. 2018.
Date Issue: 2016
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Iwamoto_AlexsandraShizue_D.pdf2.07 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.