Please use this identifier to cite or link to this item: http://repositorio.unicamp.br/jspui/handle/REPOSIP/321873
Type: DISSERTAÇÃO DIGITAL
Degree Level: Mestrado
Title: Efeito preventivo e resistência da união de compósito contendo metacrilato de triclosan para colagem de bráquetes
Title Alternative: Preventive effectiveness and bond strength of an orthodontic composite whit triclosan metacrylate
Author: Nima, Gabriel, 1981-
Advisor: Paula, Andreia Bolzan de
Abstract: Resumo: O objetivo neste estudo foi avaliar o potencial inibitório do crescimento bacteriano, a área de desmineralização e a resistência da união ao cisalhamento (RU) bráquete-esmalte, colados com compósito contendo metacrilato de triclosan (MT). Para avaliar a atividade antimicrobiana foram confeccionadas amostras de compósito com MT (CMT) e sem MT (SMT) (n=4). Cepas de Streptococcus mutans foram reativadas por 24 horas e ajustadas à densidade óptica de 1.0 (DO550nm) e diluídas em BHI suplementado com 1% de sacarose. Biofilmes foram estaticamente formados sobre a superfície dos materiais durante 24 horas. Em seguida, as amostras foram lavadas e os biofilmes formados sonicados em solução salina. As células dispersas foram diluídas serialmente e cultivadas em Mitis Salivarius Agar. Após 48 horas de incubação, as células foram contabilizadas. Quatro experimentos independentes foram realizados em quadruplicada. Os dados foram submetidos ao teste t de Student com significância de 5%. Para avaliar a desmineralização ao redor dos bráquetes, 20 blocos de esmalte bovino (6mmx4mm) foram distribuídos em dois grupos (n=10) de acordo com o material para colagem (CMT e SMT). Após a colagem dos bráquetes, os blocos de esmalte foram submetidos ao desafio cariogênico com biofilme de S. mutans por 24 horas. A dureza Knoop do esmalte foi mensurada com microdurômetro usando carga de 50 gf durante 5 segundos. Trinta penetrações foram feitas em cada amostra, em 5 regiões, 6 profundidades diferentes e os valores submetidos à análise de variância de três fatores para medidas repetidas (?=0,05). Para avaliar a RU, 60 dentes bovinos foram distribuídos em três grupos (n=20) de acordo com os materiais para colagem (CMT, SMT e Transbond XT). Os bráquetes metálicos foram colados no esmalte e fotoativados com aparelho Bluephase. As amostras foram armazenadas em água destilada a 37oC por 24 horas e submetidas a 1500 ciclos térmicos. A RU foi avaliada em máquina de ensaio com velocidade de 0,5 mm/min até ocorrer falha. Os dados foram submetidos à análise de variância de um fator e ao teste de Tukey (?=0,05). O Índice de Remanescente do Adesivo (IRA) foi avaliado e os valores submetidos ao teste de Mann-Whitney. O compósito CMT apresentou menor acúmulo de biofilme quando comparado ao SMT, em todos os experimentos realizados. Não foram encontradas diferenças significativas nos valores da dureza do esmalte ao redor dos bráquetes colados com os compósitos SMT e CMT. Maiores valores de RU foram obtidos pelo grupo Transbond XT (18,38 ± 5,74). Não foram encontradas diferenças estáticas entre os grupos SMT (12,16 ± 4,74) e CMT (10,22 ± 3,80). Pode-se concluir que o compósito CMT foi efetivo na inibição do crescimento de S. mutans; porém, não reduziu a desmineralização do esmalte ao redor dos bráquetes. A incorporação do antimicrobiano no compósito não causou influência negativa nos valores de RU

Abstract: The aim of this study was to evaluate the effect on the inhibition of bacterial growth, reduction enamel demineralization around orthodontic brackets and shear bond strength (SBS) of bracket bonding on enamel, using a composite resin modified by the addition of triclosan methacrylate (MT). To evaluate the antimicrobial effect, composite samples were prepared with MT (CMT) and without MT (SMT) (n = 4). Overnight-Incubated Streptococcus mutans culture was adjusted to 1.0 optical density (OD550nm) and diluted in BHI with 1% sucrose. Biofilms were grown for 24 hours on the samples. All the samples were washed in saline solution to remove loosely adherent cells, the viable cells in the solution were quantified. Twelve dilutions were made from this initial suspension in MSA. The petri dishes were incubated for 48 hours. After incubation the colonies were counting. Four independent experiments were performed in quadruplicate. The data were analyzed using Student's t-test. To evaluate enamel demineralization around orthodontic brackets, 20 bovine enamel blocks (6mmx4mm) were divided into two groups (CMT e SMT). Brackets were bonding in the blocks, then the specimens were exposed to a cariogenic challenge using Streptococcus mutans for 24 hours. A microhardness tester with a Knoop diamond under a 50-g load for 5 seconds was used for the microhardness analysis. Thirty indentations were made in a half block, in five positions and six different depths and values subjected to analysis of variance of three factors for repeated measures (? = 0.05). ANOVA and Tukey post-hoc test were used. For the SBS test, 60 bovine teeth were divided into three groups in accordance with the materials (CMT, SMT and Transbond XT). The brackets were positioned at the buccal surface and cured for 20 seconds by a Bluephase light curing unit. The groups were thermocycled 1500 times and then were tested. The SBS was determined with a universal testing machine. After brackets failure, the Adhesive Remnant Index (ARI) score was verified. The data were analyzed using ANOVA one way, Tukey post-hoc test and Mann-Whitney test. The CMT composite exhibited an inhibitory effect on S. mutans growth when compared to SMT in all experiments. No significant differences were found in the microhardness around the bracket, the MT was not efficient in the reducing enamel demineralization. Transbond XT (18.38 ± 5.74) had a significant difference when compared with SMT (12, 16 ± 4.74) and CMT (10.22 ± 3.80). The MT was effective to inhibit of S. mutans grown, however it was not effective to prevent the enamel demineralization around the brackets. The incorporation of the antimicrobial in the composite did not influence negatively on the SBS on enamel
Subject: Triclosan
Anti-infecciosos
Cárie dentária
Editor: [s.n.]
Citation: NIMA, Gabriel. Efeito preventivo e resistência da união de compósito contendo metacrilato de triclosan para colagem de bráquetes. 2016. 1 recurso online ( 70 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/321873>. Acesso em: 30 ago. 2018.
Date Issue: 2016
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Nima_Gabriel_M.pdf4.1 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.