Title: Influência do período de condicionamento e concentração de ácido hidrofluorídrico na resistência de união e morfologia de superfície cerâmica vítrea ao cimento resinoso = Influence of etching period and hydrofluoric acid concentration on the bond strength and morphology of the surface of glass ceramic to a resin cement
Title Alternative: Influence of etching period and hydrofluoric acid concentration on the bond strength and morphology of the surface of glass ceramic to a resin cement
Author: Puppin-Rontani, Julia, 1990-
Advisor: Correr Sobrinho, Lourenço, 1960-
Abstract: Resumo: O objetivo do presente estudo foi avaliar a influência de diferentes concentrações do ácido hidrofluorídrico (AHF) e diferentes tempos de condicionamento na superfície/morfologia e na resistência de união ao microcisalhamento (µSBS) de uma cerâmica vítrea à base de dissilicato de lítio, IPS e.max Press (EMX) (Ivoclar Vivadent) ao cimento resinoso (Variolink II). Foram confeccionados 250 blocos cerâmicos de dimensões 8 mm x 8 mm x 3mm de espessura, e distribuídos em 25 grupos (n=10). Foram avaliados cinco concentrações de AHF (1%, 2,5%, 5%, 7,5% e 10%) em cinco tempos de condicionamento (20, 40, 60, 120 e 20 + 20 s). Após o condicionamento, todos os blocos foram tratados com o agente de união silano e uma camada de resina sem carga (Scotchbond Multipurpose ¿ 3M). Em cada bloco com a superfície tratada foram confeccionados três cilindros de cimento resinoso de dimensões de 1 mm de diâmetro e 3 mm de espessura. As amostras foram armazenas em água destilada a 37oC por 24 horas. O teste de µSBS foi realizado numa máquina de ensaio universal (Instron) à velocidade de 1,0 mm/min até falha com carga de 50 N. Os valores da resistência da união de cada bloco de EMX foram obtidos pela média aritmética dos três cilindros. Os dados de µSBS foram submetidos à ANOVA dois fatores e múltipla comparação foi feita pelo teste de Tukey pos hoc (?=0,05). Foram analisados os padrões de fratura de todas as amostras com microscópio óptico com aumento de 40x, classificados como coesivo em cerâmica, coesivo no cimento resinoso, adesivo ou misto (envolvendo cimento resinoso e cerâmica). Foram confeccionados 25 amostras para análise e caracterização da morfologia do condicionamento da superfície com Microscópio Eletrônico de Varredura, com 2000x de aumento. Os grupos de concentração de AHF de 5%, 7,5% e 10% tiveram os maiores valores de µSBS (p<0,05) e nenhuma diferença estatística foi encontrada para os tempos de condicionamento de 20, 40, 60, 120 e 20 +20 s (p>0,05). Os grupos de concentração de AHF de 1% e 2,5% tiveram os menores valores de µSBS (p<0,05). Quanto ao tempo de condicionamento, os grupos de 120 s tiveram os maiores valores de µSBS (p<0,05); porém, não diferiu estatisticamente dos tempos de 20, 40, 60 e 20 + 20 s para as concentrações de 5% e 10% (p>0,05). O tempo de condicionamento e a concentração de AHF influenciaram a µSBS e a morfologia da superfície da EMX

Abstract: The aim of this study was to evaluate the influence of different concentrations of hydrofluoric acid (HF) and different etching times on the surface/morphology and on the microshear bond strength (µSBS) of a lithium dissilicate glass-ceramic IPS e.max Press (EMX) (Ivoclar Vivadent) and resin cement (Variolin II). Two-hundred and fifty ceramics blocks of 8 mm x 8 mm x 3 mm width, were divided in 25 groups (n=10). Five different HF concentrations (1%, 2.5%, 5%, 7.5% and 10%) and five etching times were evaluated (20, 40, 60, 120 and 20 + 20 s). After etching all blocks were treated with a silane-coupling agent and received a thin layer of unfilled resin (Scotchbond Multipurpose ¿ 3M).. Three resin cement cylinders were made in each block on the treated surface with dimensions of 1 mm in diameter and 3 mm thick. The specimens were stored in dionized water at 37oC for 24 h. The µSBS was carried out in an universal testing machine (Instron) at a crosshead speed of 1 mm/min until failure with 50 N load. The arithmetic average of the three µSBS values was considered as the bond strength for each EMX block. Data of µSBS were submitted to two-way ANOVA and the Tukey¿s post hoc test (?=0.05). The failure modes from all specimens were analyzed under optical microscopy at 40x magnification for failure modes identification, which were classified as cohesive in ceramic, cohesive in resin cement, adhesive or mixed (involving resin cement and ceramic). Another twenty five ceramic blocks were fabricated and divided in 25 (n=1) groups according to etching time and HF concentrations and were evaluated using scanning electron microscopy (SEM) for characterization of the surface morphology with a 2000x magnification. For HF concentration groups of 5% and 10% no significant difference was found for 20, 40, 60, 120 and 20 + 20 s etching times (p>0,05), showing the highest µSBS values. Groups of 1% and 2.5% had the lowest µSBS values (p<0.05), showing no significant difference for 120 s etching time (p>0.05). For etching time groups, 120 s showed the highest µSBS values (p<0.05) but had no significant difference in 20, 40, 60, and 20 + 20 s for 5% and 10% HF concentrations (p>0.05). Etching time and HF concentration influenced the bond strength and surface morphology of EMX
Subject: Cerâmica
Acido fluoridrico
Language: Inglês
Editor: [s.n.]
Date Issue: 2016
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Puppin-Rontani_Julia_M.pdf134.88 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.