Title: Efeito de agentes anti-erosivos = estudo in situ analisando condições normais e de hiposalivação e estudo in vitro variando a viscosidade de um composto experimental = Effect of anti-erosive agents: in situ study under normal and hyposalivatory conditions and in vitro study changing the viscosity of an experimental compound
Title Alternative: Effect of anti-erosive agents : in situ study under normal and hyposalivatory conditions and in vitro study changing the viscosity of an experimental compound
Author: Pini, Núbia Inocencya Pavesi, 1987-
Advisor: Lima, Débora Alves Nunes Leite, 1978-
Abstract: Resumo: Esse estudo avaliou a eficácia de diferentes agentes anti-erosivos in situ, variando o fluxo salivar (Capítulo 1); e, in vitro, frente aos desafios erosivo e erosivo/abrasivo (Capítulo 2). O estudo In situ, crossover e duplo-cego, utilizou amostras de esmalte bovino (4x4mm) em 4 fases experimentais (4h/cada) de acordo com os dentifrícios: placebo (Controle), fluoreto de sódio (NaF: 1400 ppm), fluoreto de estanho (SnF/NaF: 1100 ppm-SnF2, 300 ppm-NaF) e quitosana (NaF/Sn/Ch: 1450 ppm-NaF, 3500 ppm-SnCl2, 0,5% quitosana). Vinte voluntários foram divididos em 2 amostras (n=10), fluxo salivar normal ou reduzido, sendo cada voluntário um bloco estatístico. Os espécimes foram submetidos à erosão com ácido cítrico 1% (pH 3,5) previamente (Desmineralização 1 ¿ D1) e após (D2) a exposição ao meio bucal. A microdureza foi analisada inicialmente, após D1, após o período in situ e após D2, para análise dos parâmetros %SMH (perda de dureza superficial), %SMR (recobrimento de dureza superficial) e %RER (resistência relativa à erosão). O fluxo, pH e capacidade tampão salivar foram analisados em todas as fases experimentais. No estudo in vitro, espécimes de esmalte humano (3x2mm) foram submetidos a desmineralização (Ácido cítrico 0,5%, 2 min/6x/10 dias) e remineralização, sem (Experimento 1) ou com (Experimento 2) escovação. Após a primeira e última erosão diárias, as amostras foram tratadas com diferentes soluções contendo quitosana ou não ¿ 6 grupos: Ch50, Ch500, Ch1000, Ch2000 (0,5%) associados a flúor (500 ppm¿AmF) e estanho (800 ppm¿SnCl2), controle positivo (sem quitosana) e negativo (sem tratamento). No Experimento 2, as amostras foram escovadas (15s) com dentifrício não fluoretado previamente ao tratamento com soluções. As amostras foram analisadas com perfilometria (n=16), análise por energia dispersiva de raios-X (EDX/n=10) e por microscopia eletrônica de varredura (MEV/n=4). Ambos os estudos foram analisados estatisticamente por análise de variância (ANOVA) e testes post-hoc, além de análise de correlação de Pearson (Estudo in situ) (?=5%). No estudo in situ, o dentifrício SnF/NaF apresentou o melhor desempenho, seguido pelo NaF/Sn/Ch, NaF e placebo, sob fluxo salivar normal (p<0,05). Nos pacientes com hipossalivação, não foram encontradas diferenças estatisticamente significantes entre o SnF/NaF e NaF/Sn/Ch (p>0,05), que apresentaram o melhor resultado, e entre o NaF e o placebo (p>0,05). A análise de Pearson evidenciou correlação entre alguns dentifrícios e o fluxo salivar para %SMR e %RER. No estudo in vitro, as soluções com quitosana foram eficientes em reduzir o desgaste do esmalte. No Experimento 1, o Ch2000 preveniu totalmente a perda de tecido, formando precipitados sobre o esmalte (p<0,05), o que foi evidenciado pelo MEV. O EDX demonstrou a deposição de estanho sobre o tecido nos grupos tratados com soluções, sem diferenças entre eles. No Experimento 2, Ch50 e Ch500 apresentaram os melhores resultados para a perfilometria, o que foi confirmado pelo MEV. As soluções com quitosana, com exceção do Ch500, resultou em maior deposição de estanho sobre o esmalte com diferença em relação ao grupo controle positivo. A quitosana pode ser um componente ativo promissor a ser utilizado, visto que sua ação anti-erosiva foi demonstrada em ambos os estudos

Abstract: This study evaluated the efficacy of different anti-erosive compounds in situ, varying the salivary flow (Chapter 1); and, in vitro, in front of erosive and erosive/abrasive challenges (Chapter 2). In the in situ study, a crossover and double blind study, it was used enamel samples (4x4mm) from bovine incisors in 4 experimental phases (4h each one) in according to the toothpastes under evaluation: placebo (control); sodium fluoride (NaF: 1400 ppm), stannous fluoride (SnF/NaF: 1100 ppm SnF2, 300 ppm NaF) and chitosan (NaF/Sn/Ch: 1450 ppm NaF, 3500 ppm SnCl2, 0,5% Chitosan). Twenty patients were allocated in 2 groups (n=10) ¿ normal and low salivary flow, and each one was considered as a statistical block. The samples were eroded with citric acid 1% (pH 3.5) previously (Demineralization 1 ¿ D1) and after (D2) the in situ period. Microhardness was measured at baseline, after D1, after in situ exposure and after D2, to assess the parameters %SMH (surface microhardness loss), %SMR (surface microhardness recovery) e %RER (relative resistance to eroson). Salivary flow, pH and buffering were evaluated in all experimental phases. In the in vitro study, samples from human enamel (3x2mm) were submitted to a cyclic treatment with demineralization (Citric acid 0,5%, 2 min/6x/10 days) and remineralisation, (Experiment 1). After the first and last erosive treatment each day, samples were treated with different anti-erosive solutions with chitosan or not ¿ 6 groups: Ch50, Ch500, Ch 1000 and Ch 2000 (0.5%), all of them with fluoride (500 ppm ¿ AmF) and stannous (800 ppm ¿ SnCl2), positive (without chitosan) and negative (no treatment) control. In Experiment 2, samples were additionally brushed (15s) with non-fluoridated toothpastes previously the treatment with solutions. Samples were analyzed with perfilometry (n=16), energy dispersive X-ray spectroscopy (EDX/n=10) and scanning electron microscopy (SEM/n=4). Both studies were statistically analyzed with analysis of variance (ANOVA) and post-hoc tests, besides the Pearson¿s correlation (in situ study) (?=5%). In the in situ study, SnF/NaF showed the best performance, followed by NaF/Sn/Ch and NaF in case of normal flow (p<0.05). In patients with hyposalivation, no significant differences were found between SnF/NaF and NaF/Sn/Ch (p>0.05), which presented the best results; and between NaF and placebo (p>0.05). Pearson¿s analysis showed significant correlations between some toothpastes and salivary flow for %SMR and %RER. In the in vitro study, the Ch-based solutions were efficient in reducing enamel loss. In Experiment 1, Ch2000 totally prevented enamel loss with the formation of some precipitates under the enamel (p<0,05), which was observed by SEM analysis. EDX showed increase in stannous content for the experimental groups, without statistical differences between them. In the Experiment 2, Ch50 and Ch2000 presented the best results for enamel loss, which was also verified in the SEM analysis. The Ch-based solutions, excluding Ch500, resulted in higher deposition of stannous under enamel with differences in relation to the positive control. Chitosan may be a promisor active agent to be used, once it showed its ant-erosive action in both studies
Subject: Dentes - Erosão
Esmalte
Quitosana
Language: Multilíngua
Editor: [s.n.]
Date Issue: 2016
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Pini_NubiaInocencyaPavesi_D.pdf50.3 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.