Title: Influencia da pigmentação na força de tração desenvolvida por cadeias elastomericas brasileiras
Author: Almeida, Renato Castro de
Advisor: Consani, Simonides, 1939-
Abstract: Resumo: Este trabalho teve como objetivo verificar, "i n vitro", as forças de tração, exercidas por 11 cadeias elastoméricas de fabricação brasileiras (Tecnident), nas diferentes cores encontradas no mercado, em função do tempo de distensão. As amostras foram constituídas de 10 módulos, de 4 anéis, para cada cor, selecionados ao acaso. Os módulos foram distendidos a distância (Suíça), constante de força de tração, dinamômetro Correx intervalos de tempo: inicial, 1 hora, 6 horas, 12 horas, 24 horas, 72 horas, 1 semana, 2 semanas, 3 semanas e 4 semanas. Os resultados mostraram que as cadeias elastoméricas se comportaram, diferentemente entre si quanto à força de tração, varia.ndo de intensidade conforme a sua cor. Assim, a força ini.cial variou de 471,0 gramas (azul escuro) a. 317,0 gramas (verde claro) e a força remanescente, ao final de 4 semanas de teste, variou de 279,5 gramas (verde escuro) a 119,5 gramas (verde claro). 54 de 25 mm e as leituras efetuadas com um obedeceram a 10 Ao final de 4 semanas de teste, a maior porcentagem de força remanescente foi apresentada pelo elastômero de cor cinza, com 76,69%, enquanto a menor foi apresentada pelo elastômero de cor verde claro, com apenas 37,69% de força remanescente.Portanto, após a análise estatística dos resultados, foi possível concluir, que a pigmentação adicionada às cadeias elastoméricas interferiu, diretamente, no desempenho de força de tração após distenção

Abstract: This work has as goal to check "ia vitro" the traction force performed by 11 Brazilian elastomeric chains (Tecnident) in different colors met in the market, in function of distension time. The samples were made from 10 modules of 4 rings for each calor, selected by chance. The modules were pulled to a constant distance of 25 mm and the traction force readings, perfomed as a Correx (Swiss) dynamometer, obeyed the 10 time break: initial, 1 hour, 6 hours, 12 hours, 24 haurs, 72 hours, 1 week, 2 weeks, 3 weeks and 4 weeks. The results showed that the elastomeric chains behawed differently among themselves, as the traction force, varying from intensity, depending of its colar. In this way, the initial force varied 57 from 471,0 gram (light blue) to 317,0 gram (light green) and the remainig force in the end of 4 week's test varied fram 279,5 gram (dark green) to 119,5 gram (light green). At the end of 4 week's test, the percentage of remaining force was introduced by the elastomer of grey color with 76,96% while smallest was introduced by the elastomer of light green color, with just 37,69% of remaining force. Therefore soon after the statistical analyse of results was possible to conclude that the added pigmentation to the elastomeric chain interfered directly in the development of traction force after distension
Subject: Elastômeros na odontologia
Ortodontia
Language: Português
Editor: [s.n.]
Date Issue: 1993
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Almeida_RenatoCastrode_M.pdf2.58 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.