Title: Influência da irradiância na dureza Knoop, grau de conversão e contração de diferentes compósitos
Title Alternative: Influence of irradiance on Knoop hardness, degree of conversion and shrinkage of the different composites
Author: Fugolin, Ana Paula Piovezan, 1987-
Advisor: Consani, Simonides, 1939-
Abstract: Resumo: O objetivo neste estudo foi investigar a influência de diferentes irradiâncias e de energia emitida pelo fotoativador na dureza Knoop, grau de conversão e contração de polimerização de compósitos odontológicos com diferentes partículas de carga. Anéis de latão de 12 mm de diâmetro externo, 8 mm de diâmetro interno e 2 mm altura foram preenchidos com os compósitos Filtek Supreme XT® (ESPE 3M) e Charisma® (Heraeus Kulzer), ambos na cor A2. O aparelho utilizado foi o LED Bluephase G2 (Ivoclar-Vivadent), com tempo de fotoativação de 20 s e irradiância conforme o protocolo: grupos A e D- 300 mW/cm²; grupos B e E- 650 mW/cm² e grupos C e F- 1200mW/cm², sendo n = 5. Depois da polimerização, cada conjunto (matriz e amostra) foi submetido aos procedimentos de acabamento e polimento com lixas de carboneto de silício. A armazenagem foi em estufa a 37ºC por 24 horas, dispostos em recipiente a seco e no escuro. Após armazenagem, as superfícies de topo e base das amostras foram submetidas ao teste de dureza Knoop em durômetro, onde foram efetuadas 5 penetrações em cada região, com carga de 50 gf por 5 s. As amostras submetidas ao ensaio de dureza Knoop foram analisadas em microscopia eletrônica de varredura para verificar o nível de adaptação material-matriz. Por meio do programa UTHSCSA ImageTool foi mensurada a largura das fendas. Para avaliar o grau de conversão outras amostras foram confeccionadas, as quais foram avaliadas pelo FTIR com ATR. Os dados foram submetidos à ANOVA múltiplos fatores e teste de Tukey (5%). Os resultados mostraram que: A dureza Knoop do Filtek Supreme XT foi significativamente maior que do Charisma, independente do local e irradiância. Independente do material e local, as irradiâncias de 1200 mW/cm² e 650 mW/cm² mostraram valores de dureza estatisticamente similares, sendo ambas significativamente maiores aos de 300 mW/cm². Para Charisma houve diferença estatística significante entre topo e base nas irradiâncias de 300 mW/cm² e 650 mW/cm². No Filtek Supreme XT houve diferença estatística significante entre topo e base somente na irradiância de 300 mW/cm². Independente do local e irradiância, o grau de conversão do Charisma foi estatisticamente maior que do Filtek Supreme XT, exceto na irradiância de 650 mW/cm², onde os valores foram estatisticamente similares. No Charisma, a irradiância de 1200 mW/cm² proporcionou grau de conversão significativamente maior que 300 mW/cm² e 650 mW/cm², ambos similares entre si. No Filtek Supreme XT, a irradiância de 1200 mW/cm² proporcionou valor significativamente maior, 300 W/cm² menor e 650 mW/cm² valor intermediário. Independente da irradiância, para Filtek Supreme XT não houve diferença entre topo e base. Para Charisma, 300 mW/cm² e 650 mW/cm² apresentaram diferença estatística significante entre topo e base, sendo que em 1200 mW/cm² não houve diferença estatística significante. Independente da irradiância, a contração do Charisma foi significativamente maior que do Filtek Supreme XT. Independente do material, a contração promovida pelas irradiâncias foi similar. Os resultados deste estudo mostraram que a irradiância influenciou na dureza Knoop e no grau de conversão, não causando efeito na contração dos compósitos.

Abstract: The aim of this study was to investigate the influence of both energy and power density (of different levels) emitted by light curing unit in the Knoop hardness, conversion degree and polymerization shrinkage of dental composites with different types of filler particles. Brass rings of 12mm outside diameter, 8mm internal diameter and 2mm height were filled with the composites Filtek Supreme XT® (3M ESPE) and Charisma (Heraeus Kulzer), both color A2. The light curing unit Bluephase G2 LED (Ivoclar-Vivadent) was used for 20s with irradiance according to the protocol; groups A and D ¿ 300 mW/cm², groups B and E ¿ 650 mW/cm² and groups C and F ¿ 1200 mW/cm². After polymerization, the sets (matrix and sample) were finished and polished with silicon carbide sandpaper and stored for 24 hours at 37°C in dark and dry container. After his period the specimens were evaluated for their hardness in an indenter, where top and bottom surfaces were submitted to five penetrations, with a load of 50gf for 5 s. Scanning electron microscopy (SEM) of these samples was carried out to check the gap between composite and matrix and the extent of crack were measured using the program UTHSCSA ImageTool. FTIR with ATR techniques assessed the degree of conversion of new samples. The data were analyzed by multiple factors ANOVA and Tukey test (p ? 0.05). In the results Filtek Supreme XT showed hardness values significantly higher than those of Charisma, regardless the location and the irradiance. At irradiances of 1200 mW/cm² and 650 mW/cm² showed hardness values statistically similar and significantly higher at 300 mW/cm², regardless the material and the location. Charisma showed a statistically significant difference between top and bottom in the irradiances 300 mW/cm² and 650 mW/cm². Filtek Supreme XT showed significant difference between top and bottom only in the irradiance of 300 mW/cm². The results for degree of conversion showed that, regardless the location and irradiance, Charisma had statistically higher values than Filtek Supreme XT, except for the irradiance of 650 mW/cm², where the values of the composites were statistically similar. At the power density of 1200 mW/cm², Charisma achieved values significantly higher than 650 mW/cm² and 300 mW/cm². At the power density of 1200 mW/cm² Filtek Supreme XT showed the highest conversion values, while at 300 mW/cm² showed the lowest values, and at 650 mW/cm² intermediate values were found. Regardless the irradiance, Filtek Supreme XT showed no difference between top and bottom. Charisma, at 300 mW/cm² and at 650 mW/cm² showed statistically significant difference between top and bottom, and at 1200 mW/cm² the difference was not statistically significant. Charisma showed significantly higher values of contraction than Filtek Supreme XT, regardless the irradiance. Regardless the material, no statistical difference was found for values of contraction for the evaluated irradiances. The findings of this study showed that the power density influenced the hardness and the degree of conversion, but not the contraction.
Subject: Resinas compostas - Propriedades mecânicas
Resinas compostas - Propriedades físicas
Resinas compostas
Language: Português
Editor: [s.n.]
Date Issue: 2011
Appears in Collections:FOP - Tese e Dissertação