Title: Estudo "in vitro" da resistencia da união entre resina acrilica e materiais reembasadores resilientes submetidos ou não a termociclagem
Author: Sanchez, Jose Luiz Lopes
Advisor: Mesquita, Marcelo Ferraz, 1967-
Abstract: Resumo: Este trabalho teve como objetivo comparar a resistência da união entre bases resilientes (Dentuflex, Ufi-Gel e Eversoft) e resina acrílica (QC-20), submetidas ou não à termociclagem. Foram utilizadas 60 amostras divididas em 6 grupos de variáveis, com 10 repetições cada. Para a confecção das amostras, foram utilizadas matrizes metálicas incluídas em mufla, cujo molde impresso na silicona de condensação e no gesso foi preenchido com resina acrílica. Após polimerizadas, as amostras foram unidas duas a duas em seu eixo longitudinal por uma base resiliente. Em seguida, metade das amostras foi levada ao termociclador MCT2 AMM Instrumental onde foram realizados 3000 ciclos de 1 minuto em água à 5° C '+ ou -'1° C) e 1 minuto em água a 65° C ( '+ ou -'1°C). A outra metade das amostras foi armazenada em água à 37° C durante 24 horas. Após cada período, as amostras foram submetidas a um tracionamento no equipamento EMIC-DL500MF com velocidade de 5mm/minuto. Os dados obtidos foram submetidos à análise estatística pelo Teste de Tukey, ao nível e 5% de probabilidade e as amostras foram analisadas quanto ao tipo de falha ocorrida. O material Dentuflex apresentou os maiores valores de resistência à tração, independentemente do tratamento recebido, apresentando diferença estatística em relação aos demais materiais. O material Eversoft quando termo ciciado apresentou superioridade estatística em relação ao material Ufi-Gel. Para os materiais Dentuflex e Eversoft, a termociclagem aumentou os valores de resistência à tração, apresentando diferença estatística em relação ao controle, entretanto, para o material Ufi-Gel, o comportamento não foi alterado

Abstract: The purpose of this study was to compare the tensile bond strength between soft-liners (Dentuflex, Ufi-Gel and Eversoft) and the acrylic resin (QC-20), submitted or not to the thermal cycling (of 1 minute in water at 5°C and 1 minute in water at 65°C). Twenty samples were made of each soft-liner. Half of each group received thermal cycling, and the other half, did not. For making the samples, metal matrixes were invested in flasks, the molds was packed with acrylic resin and a spacer was used to divided tbe samples in the middle. After the resin curing, the spacer was taken out and the acrylic resins were joint with soft-liner material. Half of the samples were submitted to 3.000 thermal cycles, and the other half, were not. Afterwards, the samples were submitted to the tensile bond strength test in a universal testing machine (EMIC-DL500MF) with a crosshead speed of 5 mm/min. The results, after Tukey test at 5% of probability, showed that the highest values were obtained to the Dentuflex (3:32 MPa), and the lowest values were observed with Ufi-Gel (0.18 MPa), both when submitted to the thermal cycling. According to the results it was observed that: the Dentuflex material presented the highest values of tensile bond strength, independent of the received treatment, presenting statistical differences related to the Eversoft and Ufi-Gel. The Eversoft material when submitted to the thermal cycling presented values statistically higher than the Ufi Gel. For the Dentuflex and Eversoft materials, the thermal cycling increased the tensile bond strength values presenting statistical differences related to the no cycled, and for the Ufi-Gel the behavior was not altered.
Subject: Prótese dentária completa
Materiais dentários
Language: Português
Editor: [s.n.]
Date Issue: 1999
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Sanchez_JoseLuizLopes_M.pdf7.28 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.