Please use this identifier to cite or link to this item: http://repositorio.unicamp.br/jspui/handle/REPOSIP/289903
Type: TESE
Degree Level: Doutorado
Title: Efeito de tecnicas de envelhecimento acelerado e aplicação de selante sobre a deformação permanente de reembasadores resilientes permanentes
Title Alternative: Effect of accelerated aging and surface sealing on permanent deformation of auto-polymerizing soft liners
Author: Silva, Joaquim Alberto da
Advisor: Mesquita, Marcelo Ferraz, 1967-
Abstract: Resumo: O objetivo neste estudo foi comparar o efeito de dois métodos de envelhecimento acelerado (termociclagem e simulação do intemperismo natural) sobre a propriedade de deformação permanente de dois reembasadores resilientes permanentes usados como forradores de próteses removíveis, um à base de silicone (UP) e outro à base resina acrílica (DF), submetidos ou não à aplicação de selante de superfície. Foram confeccionados 120 corpos-de-prova (12,7 mm de diâmetro, e 19 mm de comprimento), distribuídos aleatoriamente em doze grupos (n=10) e submetidos a envelhecimento acelerado (2.000 ciclos) por meio da termociclagem, ou simulação do intemperismo natural (67 ciclos). Para o ensaio, foi utilizado um aparelho mecânico descrito na especificação no18 da A.D.A., com aplicação de carga compressiva (750 gf) durante 30 segundos. Para comparações do mesmo material com e sem selante e entre os materiais no mesmo intervalo de envelhecimento, foi realizada a análise estatística pelo teste de Mann-Whitney (p=0,05). Os testes de Kruskal-Wallis associado ao método de Dunn foram utilizados para comparação do efeito das técnicas de envelhecimento em cada material (p=0,05). O reembasador à base de silicone apresentou menor deformação permanente que o à base de resina, independente do método de envelhecimento (P<0,05). Foi observado que a aplicação do selante de superfície teve efeito sobre a deformação permanente apenas no grupo do material à base de silicone submetido à termociclagem, e que o envelhecimento acelerado promoveu aumento na deformação permanente apenas para o material à base de resina acrílica.

Abstract: This study was performed in order to compare the effects of two different accelerated aging methods on the property of permanent deformation of two permanent softliners. The softliners selected were an auto-polymerizing acrylic resin based and an auto-polymerizing silicone based. The use of surface sealer was also evaluated on both relining materials. For the permanent deformation test specimens were manufactured with 12.7 mm of diameter and 19 mm length, according to A.D.A. specification number 18. A total of 120 specimens were manufactured, sixty of each relining material. All specimens were randomly distributed into twelve groups (n=10) and later submitted to one of the accelerated aging processes (2000 thermocycling cycles or 67 cycles in an EQUV chamber). The permanent deformation test was performed with a mechanical device described in the specification number 18 of A.D.A. with a compressive load of 750 gf applied during 30 seconds. All data was submitted to statistical analysis. MannWhitney test was performed in order to compare the effect of the surface sealer on each material and to compare the permanent deformation of the materials in the same aging group (p=0.05). Kruskal-Wallis and Dunn tests were performed to compare all aging groups of each material (p=0.05). After analysis of the results it was observed that the silicone based reliner presented lower permanent deformation than the acrylic resin based reliner, regardless of the aging procedure. The surface sealer coating was effective only for the thermocycled silicone group and the accelerated aging processes affected only the permanent deformation of the acrylic resin based material.
Subject: Reembasadores de dentadura
Força compressiva
Elasticidade
Resinas acrílicas
Silicones
Language: Português
Editor: [s.n.]
Date Issue: 2010
Appears in Collections:FOP - Tese e Dissertação