Please use this identifier to cite or link to this item: http://repositorio.unicamp.br/jspui/handle/REPOSIP/289852
Type: DISSERTAÇÃO
Degree Level: Mestrado
Title: Efeito do digluconato de clorexidina na estabilidade da união de sistemas adesivos e dentina sadia ou afetada por carie
Title Alternative: Effect of clorhexidine digluconate on the bond strength of etch-and-rinse adhesives to normal/caries-affected dentin
Author: Komori, Paula Carolina de Paiva
Advisor: Carrilho, Marcela Rocha de Oliveira
Abstract: Resumo: O objetivo deste trabalho foi avaliar o efeito da aplicação da solução aquosa de digluconato de clorexidina a 2% (CHX) na estabilidade da união de sistemas adesivos convencionais e dentina sadia (DS) ou afetada por cárie (DAC). Neste estudo foram testadas as hipóteses de que a CHX não teria efeito prejudicial na resistência de união entre DS ou DAC e que em longo prazo a CHX poderia minimizar o mecanismo de degradação da interface dentina-resina. Vinte molares humanos cariados tiveram o esmalte e dentina superficial removidos para exposição de uma superfície plana de DS e DAC. Os substratos foram condicionados com gel de ácido fosfórico 35% por 15s, lavados e secos com leve jato de ar. Os dentes foram distribuídos em dois grupos para o tratamento da superfície dentinária, o controle: foi re-umedecido com água deionizada; e o experimental: com CHX, a solução umidificadora permaneceu em contato com o substrato durante 60s e o excesso de umidade removido com papel absorvente. Sobre o substrato foi aplicado o adesivo Scotchbond Multi-Purpose (MP) ou Single Bond 2 (SB) e confeccionado um bloco com incrementos de resina composta Z-250. Após 7 dias de armazenagem em solução fosfato tamponada (PBS, pH 7,4) a 37ºC, as amostras foram submetidas a cortes seriados, gerando espécimes em forma de palitos com área de interface de união de aproximadamente 0,8mm2. Metade dos espécimes foi imediatamente submetida ao teste de microtração e a outra metade permaneceu armazenada por 6 meses. Os resultados obtidos foram submetidos à análise de variância e teste de Holm-Sidak para contraste das médias em nível de significância (a=0,05). A primeira hipótese testada foi confirmada, o uso da CHX após o condicionamento ácido não interferiu na resistência mecânica imediata da interface formada por um compósito de resina e DS ou DAC. A segunda hipótese foi parcialmente confirmada, o uso da CHX após o condicionamento ácido minimizou o processo de degradação das interfaces de união constituídas por DS. A utilização da CHX em associação aos sistemas adesivos convencionais de 2 e 3 passos durante a hibridização pode atuar como potencial agente retardador da degradação das interfaces adesivas promovendo maior longevidade às restaurações adesivas

Abstract: The aim of this study was to evaluate the effect of 2% chlorhexidine digluconate on the bond strength of etch-and-rinse adhesives applied to sound (SD) and caries-affected dentin (CAD). It is hypothesized that CHX does not have a detrimental effect on the bond strength to sound and caries-affected dentin, as well as that CHX may decelerate the mechanical degradation of resin-dentin bonds over time. Twenty, carious, extracted molars were included in this study. The occlusal enamel of all teeth was removed with a slowspeed diamond saw, under copious water-cooling, in order to expose a flat surface, where the CAD was surrounded by SD. The CAD and SD surfaces were etched with 35% phosphoric acid gel for 15 s, rinsed for 30 s with tap water and dried with oil/water-free air. In the control groups, the dentin substrates were re-hydrated with distilled water, while in the experimental groups were re-hydrated with 2 wt% chlorhexidine digluconate (CHX). After a dwell time of 60 s, excess solution was removed with absorbent paper. The dentin surfaces were then bonded with one of the etch-and-rinse adhesives, Schotchbond Multi- Purpose (MP) or Single Bond 2 (SB). Composite build-up was performed with Z250 and stored in phosphate-buffered saline (PBS, pH 7.4) at 37ºC for 7 days. After this period, the restored teeth were longitudinally sectioned across the bonded interface to produce a series of 0.8 mm2 beams. Part of those specimens was immediately subjected to a microtensile test. The remaining specimens were stored in PBS at 37°C for six months and then tested in tension under the same protocol. Data were analyzed by ANOVA and Holm-Sidak test for multiple comparisons (a = 0.05). The first anticipated hypothesis was confirmed, the use of CHX after acid-etching did not have detrimental effect on the immediate bond strength to both normal and caries-affected dentin and the second anticipated hypothesis was partially confirmed, the mechanical degradation of resin-dentin bonds may be delayed by the application of chlorhexidine (CHX) to sound dentin after phosphoric acid-etching. Attempts to use chlorhexidine adjunctively with conventional acid-and-rinse adhesives may play a clinically-relevant role on the preservation of resin-dentin bonds
Subject: Adesivos dentários
Clorexidina
Cárie dentária
Resistência de materiais
Language: Português
Editor: [s.n.]
Citation: KOMORI, Paula Carolina de Paiva. Efeito do digluconato de clorexidina na estabilidade da união de sistemas adesivos e dentina sadia ou afetada por carie. 2007. 86f. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/289852>. Acesso em: 8 ago. 2018.
Date Issue: 2007
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Komori_PaulaCarolinadePaiva_M.pdf1.15 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.