Title: Avaliação in-vitro da microinfiltração em cavidades classe II restauradas com composito de alta viscosidade submetidas a carregamento oclusal ciclico
Author: Campos, Paulo Eduardo Gomes de Almeida
Advisor: Martins, Luís Roberto Marcondes, 1960-
Abstract: Resumo: Objetivou-se neste trabalho avaliar a microinfiltração cervical em restaurações diretas classes II com variação de 4 materiais e a influência do carregamento oclusal cíclico. 80 terceiros molares humanos recém extraídos, foram armazenados em Timol a 0,5% até o início do experimento. Todos os dentes receberam o mesmo tipo de preparo, ¿slot¿ vertical proximal, com as mesmas dimensões, exceto no limite das paredes cervicais, que em uma proximal localizou-se em esmalte (1mm acima da junção esmalte cemento - JEC) e em dentina (1mm abaixo da JEC), sem biselamento das margens. Utilizou-se o sistema adesivo Single Bond (3M) e compósito restaurador Filtek P60 em todas os espécimes com variação de 3 materias restauradores somente à parede cervical (Filtek Flow, Dyract AP e Vitremer). Os 80 dentes foram divididos de acordo com o tipo de tratamento: 4 grupos controles (sem receber carregamento oclusal) e 4 grupos testes (recebendo carregamento oclusal). Concluídas as restaurações, os dentes foram armazenados em água deionizada por 7 dias. Em seguida 40 espécimes receberam 4000 mil ciclos de carregamento oclusal de 150 N com duração de 1segundo. Após este procedimento os dentes foram imersos em solução de nitrato de prata a 50% por um período de 24 horas. Em seguida foi avaliado o grau de microinfiltração pelo corante com auxílio de lupa estereoscópica com aumento de 40 vezes por 2 examinadores treinados, de acordo com o seguinte escore pré-definido: 0- ausência de penetração, 1- penetração até a metade da extensão da parede cervical (considerada leve), 2- penetração em toda a extensão da parede cervical sem alcançar a parede axial (considerada moderado) e 3- penetração em toda a extensão da parede cervical alcançando a parede axial (considerada severa). Os dados foram submetidos à 3 testes não paramétrico. No teste Wilcoxon encontrou-se diferenças estatisticamente significativas (p<0,05). No teste Mann-Whitney, encontrou-se diferenças estatisticamente significativas (p<0,05) do grau de infiltração no esmalte; na dentina, só não foi encontrada diferença estatisticamente significativa em relação ao grupo no material Flow. No teste de Kruskal-Wallis não detectou-se nenhuma diferença estatisticamente significativa do grau de infiltração entre os 4 materiais estudados. Com base nos dados coletados, concluiu-se que as restaurações que tiveram suas margens localizadas em dentina tiveram maior grau de microinfiltração que as localizadas em esmalte. Quando os espécimes foram submetidos ao carregamento oclusal, os índices de microinfiltração tanto em esmalte quanto em dentina aumentaram. Quando comparou-se o desempenho dos 4 materiais restauradores diretos às paredes em esmalte e em dentina não encontrou-se diferenças estatisticamente significantes entre os matérias estudados

Abstract: The objective of this work was to evaluate the cervical microleakage in class II direct restorations with four direct restoration materials, and the influence of occlusal cyclic loading over these restorations. Eighty recently extracted third molar human teeth, were stored in 0,5% Timol until the experiment. All the teeth received the same kind of cavity preparation, proximal slot, with the same dimensions, except in the limit of the cervical walls which in a proximal was located in enamel (1mm above the enamel-dentin junction ) and in the other was located in dentine (1mm below the enamel-dentin junction). None of the margins of the prepare were beveled. It was used the Single Bond (3M-ESPE) dentinal adhesive system and the Filtek P60 composite resin in all samples and the material used to restore the cervical wall were changed into the groups (Filtek Flow, Dyract AP, Vitremer). The samples were then divided according to the kind of treatment: four control groups (without cyclic occlusal loading) and four experimental groups (with cyclic occlusal loading). After all the restorations were concluded, samples were stored in distilled water for a week. After that, forty samples received 4000 one second cycles of 150 N occlusal loading . After this procedure the samples were immersed in silver nitrate solution for twenty-four hours. Then, microleakage degree was evaluated by means of a 40X stereoscopic magnifying glass by two pre-calibrated examiners, according to the following score: 0= No penetration, 1= penetration until the half of the extension of the cervical wall, considered light, 2= penetration in all the extension of the cervical wall without reaching the axial wall, considered medium and 3= penetration in every extension of the cervical wall, reaching the axial wall, considered severe. Results were statistically analyzed by three non-parametric tests. The Wilcoxon test showed that the groups were statistically differents (p< 0,05). The Mann-Whitney test found, in enamel, for all kinds of materials, statistically significant differences (p< 0,05) of the leakage degree, regarding the group (control and loading). In dentine, it was not found a statistically significant difference regarding the group only in the flow material. The Kruskal-Wallis test did not detect any statistically significant difference of the leakage degree between the four studied materials. Based in this collected data, it was concluded that the restorations that had its margins located in dentine had larger microleakage degree than the located in enamel. When the samples were submitted to the occlusal loading, they were negatively influenced, increasing microleakage values in enamel and in dentine. Comparing itself the performance of the four tested materials, it was not detected any statistically significant difference among them
Subject: Dentística
Resinas compostas
Language: Português
Editor: [s.n.]
Citation: CAMPOS, Paulo Eduardo Gomes de Almeida. Avaliação in-vitro da microinfiltração em cavidades classe II restauradas com composito de alta viscosidade submetidas a carregamento oclusal ciclico. 2005. 129p. Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/289809>. Acesso em: 4 ago. 2018.
Date Issue: 2005
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Campos_PauloEduardoGomesdeAlmeida_D.pdf8.55 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.