Title: Avaliação da microdureza de materiais restauradores submetidos ao clareamento com gel de peroxido de carbamida
Author: Campos, Inger Teixeira de
Advisor: Pimenta, Luiz Andre Freire, 1965-
Abstract: Resumo: O objetivo deste trabalho in vitro foi avaliar quantitativa mente os efeitos dos géis de peróxido de carbamida (PC) a 10% e 15% (Opalescence Ultradent Prod.) nos materiais restauradores, utilizando-se análise de microdureza superficial. Matrizes cilíndricas de acrílico (4X2mm) foram preenchidas com os seguintes materiais restauradores: Charisma (Heraeus Kulzer), Durafill V5 (Heraeus Kulzer), Vitremer (3M), Dyract AP (Dentsply) e Permite C (5Dl). Confeccionaram-se sessenta corpos-de-prova para cada material restaurador. Vinte espécimes (n=20) foram destinados para o grupo controle, que permaneceu imerso em saliva artificial substituída diariamente, vinte receberam peróxido de carbamida a 10% e vinte peróxido de carbamida a 15%. O tratamento consistiu na imersão dos espécimes em 1cm3 de PC a 10% e 15%, por seis horas diárias, durante três semanas. Enquanto não estavam sendo tratados com gel clareador, os grupos experimentais permaneceram imersos em saliva artificial durante dezoito horas. Após este período, foi feita a medida da microdureza Knoop (KHN) em cada corpo-de-prova, em cinco locais diferentes, aplicando-se carga de 25g, durante 20 segundos. Os valores obtidos, foram transformados em KHN e a média dos valores foi calculada. Os dados foram submetidos a análise estatística(ANOVA e Teste de Tukey, p<0,05). Através dos resultados obtidos foi possível concluir que o clareamento caseiro com gel de peróxido de carbamida a 10 e 15% provocou diminuição na microdureza dos materiais Dyract AP, Vitremer e Permite C

Abstract: The objective of this in vitro study was to quantitatively assess the effects of bleaching (Opalescence-Ultradent with 10% and 15% carbamide peroxide (CP) Prod.) on restoration materiais by performing superficial microhardness analysis. Acrylic cylindrical containers (4x2mm) were filled with the following restoration products: Charisma (Heraues Kulzer), Durafill VS (Heraeus Kulzer) Vitremer (3M), Dyract (Dentsply) and Permite C (SDI). Sixty samples were prepared of each restoration material. Twenty samples (n=20) received bleaching treatment with PC 10%, twenty received bleaching treatment with PC 15% and twenty were kept submersed in artificial saliva, which was replaced daily. The treatment consisted of immersion of the specimens in 1cm3 of CP at 10% and 15% for six hours per day during three weeks, whereupon the test specimens were washed, dried and kept immersed in artificial saliva for 18 hours. Then the test and control specimens were analyzed using a microhardness gauge. The Knoop Hardness Number (KHN) was taken for each test and control specimen at five different locations by applying a 25g force for 20 seconds. The values obtained were transformed into KHNs and the mean calculated. The data were submitted to statistical analysis by ANOVA and Tukey test, p<0,05. It was observed a decrease in microhardness for the materiais Dyract AP, Vitremer and Permite C after treatment with PC 10% and 15%
Subject: Dentística
Géis
Language: Português
Editor: [s.n.]
Date Issue: 2001
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Campos_IngerTeixeirade_D.pdf3.22 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.