Title: Analise quimica e topografica da superficie de implantes de titanio comercialmente puro atraves de espectroscopia de fotoeletrons excitada por raios-X (XPS) e microscopia eletronica de varredura (MEV)
Author: Sardinha, Sandra de Cassia Santana
Advisor: Albergaria-Barbosa, José Ricardo de, 1956-
Abstract: Resumo: Este trabalho teve como objetivo analisar, química e topograficamente, a superfície de implantes de titânio comercialmente puro, utilizados atualmente na Odontologia. Foram selecionados oito implantes das seguintes marcas comerciais: Conexão - Sistema de Próteses; Lifecore - Biomedical; AS Technology e S - Serson Internacional. As amostras apresentavam tratamento de superfície, através das técnicas de ataque ácido (Conexão) e plasma sprayde titânio (Lifecore-Biomedical; AS Technology e S - Serson International), sendo divididas em quatro grupos, contendo dois implantes do mesmo lote de cada fabricante. As análises foram realizadas através de Espectroscopia de Fotoelétrons Excitada por Raios-X (XPS) e Microscopia Eletrônica de Varredura (MEV). Os resultados da análise química mostraram os elementos titânio (Ti), oxigênio (O), silício (Si), zinco (Zn), alumínio (AI) e carbono (C). O estudo através do MEV revelou a topografia rugosa da superfície e uniformidade entre as roscas dos implantes. Pode-se concluir, deste modo, que houve impurezas na superfície dos implantes, que todas as amostras apresentaram rugosidade de superfície, mas que há necessidade de outros trabalhos que relacionem a presença desses compostos e sua interferência na osseointegração

Abstract: The aim of this study was to analyze the chemical and topography of the surface of currently utilized implants of commercially pure titanium. A total of eight implants were studied (Conexão - Sistema de Próteses, Lifecore Biomedical, AS Technology, and S - Serson International). Ali samples had treatment of surface. The samples were divided into four groups, containing two implants from the same lot of each manufacturer. The analysis of the samples was performed utilizing spectroscopy and electromicroscopy. Results showed predominance of the elements of titanium, oxygen, zinc, aluminum, silicon, and carbon in ali samples studied. The electromicroscopy showed the rough topography of the surface and uniformity between the implants. In conclusion, there were impurities in the surface of the implants. However, further studies are required to investigate the relationship between these chemical components in the surface of implants and their influence in the process of bony integration
Subject: Implantes dentários endoósseos
Titânio
Microscopia eletrônica de varredura
Language: Português
Editor: [s.n.]
Date Issue: 2003
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Sardinha_SandradeCassiaSantana_D.pdf6.62 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.