Title: Influência das temperaturas de cocção de porcelanas no desajuste cervical de copings em titânio comercialmente puro e ligas titânio-alumínio-vanádio e paládio-prata
Author: Fonseca, Johnson Campideli
Advisor: Henriques, Guilherme Elias Pessanha, 1968-
Abstract: Resumo: A utilização do titânio e suas ligas em prótese tem aumentado nos últimos anos do conjunto de propriedades físico-químicas que exibem, sendo escassas as >rmaçôes a respeito da adaptação cervical de restaurações fundidas. Este estudo objetivou: 1) determinar o desajuste cervical de copings fundidos em comercialmente puro (Ti c.p.) e iigas titánio-aiumínio-vanádio (ÏÎ-6AI-4V) e paládio-prata (Pd-Ag); 2) avaliar a influência do ciclo de cocção das porcelanas preconizadas sobre o desajuste cervical dos copings fundidos em Ti c.p. e ligas TÍ-6A1-4V e Pd-Ag; 3) avaliar a aneíusão) sobre o desajuste cervical dos copings fundidos em Ti c.p. e bga TÏ-6A1-4V. s típicos para restaurações as {altura de 5mm; término cervical em ombro 90° e largura de l,5mm; erimentais Ti-óAMV, TÍ-6A1-4V com tratamento térmico (TÍ-6A1-4V TT), Ti c.p.. Ti érmico (Ti c.p. TT) e Pd-Ag. Os copings em Ti c.p. e liga TÍ-6A1-4V pelo sistema Rematitan (Dcntaurum). O tratamento térmico experimental s TÍ-6A3-4V TT e Ti c.p. TT) foi realizado nas inclusões originais à temperatura do aquecimento da porcelana (800°C). O desajuste cervical tbi medido com auxilio metidos à Análise de Variância (ANOVA) e teste de Tukey, com nível de probabilidade 5%. Os valores médios de desajuste cervical obtidos ao final dos ciclos de cocção 78um para TÍ-6A1-4V, 86,02 urn para TÍ-6A1-4V TT, 117,22um para Ti c.p., para Ti c.p. TT e 9S,70um para Pd-Ag, sem que houvesse diferença significativa entre tais valores. O desajuste cervical dos grupos m Ti c.p. e TÍ-6AÍ-4V não foi influenciado de forma significante pelo ciclo de cocção da porcelana Vitatitankramic. O grupo Pd-Ag mostrou alternação estatisticamente significativa apos a cocção da porcelana para dentina e glaze

Abstract: The application of titanium and titanium alloys in prosthetic dentistry has increased in the past few years because of their physical and chemical properties; however, few studies have investigated the marginal fit of cast restorations. This study evaluated: 1) the marginal fit of copings obtained in commercially pure titanium (c.p. Ti), thanium-aluminurn-vanadiurn (Ti-6A1-4V) and palladium-silver (Pd-Ag) alloys; 2) the influence of firing cycle of recommended porcelains in the marginal fit of c.p. Ti, Ti-6A1-4V and Pd-Ag alloys; 3) the effectiveness of additional heating at the first temperature of firing cycle in the marginal fit of Ti c.p. and Ti-6A1-4V copings. Fifty bovine teeth with standardized preparations for metal-ceramic crowns (length of 5mm; axial taper of 8°; shoulder of 1,5mm) were used and divided in T1-6A1-4V, Ti-6A1-4V with additional heat (Ti-6A1-4V TT), Ti c.p., Ti c.p. with additional heat (Ti c.p. TT) and Pd-Ag experimental groups. The copings for commercially pure titanium and titanium-aluminum-vanadium alloy were obtained in Rematitan System (Dentaurum). The experimental additional heat (Ti-6Ai-4V TT and Ti c.p. TT) was performed in original invested castings at first tiring porcelain temperature (800°C). The marginal fit was measured with the use of a measuring microscope (Olympus STM). The mean values of copings marginal fit were subjected lo analysis of variance (AN OVA) and Tukey's test with statistical significance set at the 5% probability level. The mean values of marginal fit after the complete firing cycle were: 106,78nm to Ti-6AI-4V, 86,02um to Ti-6AI-4V TT. 117,22fim to Ti c.p,, 115,71 um Ti c.p. TT and 98,70um to Pd-Ag, with no significant differences between these experimental groups. The marginal fit of Ti c.p. and Ti-6A1-4V was not significant influenced by Vitalitankeramic firing cycle. The Pd-Ag group revealed significant changes in marginal fit after firing of dentin porcelain and glaze
Subject: Fundição
Ligas de titânio
Metais
Adaptação
Metais - Tratamento térmico
Language: Português
Editor: [s.n.]
Date Issue: 2001
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Fonseca_JohnsonCampideli_M.pdf11.93 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.