Title: Efeito do tempo de aplicação de gel antioxidante sobre a resistencia de união ao esmalte dental clareado
Title Alternative: Effect that elapsed time of antioxidant gel onto the bond strenght to bleached enamel
Author: Silva, Ana Paula Brito da
Advisor: Marchi, Giselle Maria, 1970-
Abstract: Resumo: O objetivo deste estudo in vitro foi avaliar o efeito do tempo de aplicação de gel de ascorbil a 3% (AE) sobre a resistência de união ao esmalte bovino tratado previamente com peróxido de carbamida a 10% (PC), estabelecendo o padrão de fratura através de microscopia eletrônica de varredura (MEV). Sessenta incisivos bovinos foram selecionados, limpos e armazenados em solução salina de timol a 0,1%. Sessenta fragmentos de 25mm2 foram obtidos da superfície vestibular, utilizando-se discos diamantados de dupla-face, em baixa rotação, sob constante irrigação. Os fragmentos foram cobertos com fina camada de cera 7 e embebidos em cilíndro por resina autopolimerizável de poliestireno. Posteriormente, foram divididos aleatoriamente em seis grupos, sendo dois controles: GS (saliva, durante todo o experimento) e GP (PC, por seis horas, durante 14 dias) e quatro experimentais, que após a utilização diária do PC, foram submetidos à aplicação de gel antioxidante por 15, 30, 60 ou 120 minutos, respectivamente (GPA15, GPA30, GPA60 e GPA120). Imediatamente após o tratamento, os fragmentos foram condicionados com ácido fosfórico a 37% (Dentsply) e restaurados com sistema adesivo Adper Single Bond (3M-ESPE) e três incrementos horizontais de resina TPH (Dentsply). Finalizado o tratamento restaurador, os fragmentos foram preparados para o ensaio de microtração. Cortes seriados foram realizados em cada amostra para obtenção de duas fatias centralizadas de, aproximadamente, 1mm de espessura. Posteriormente, com auxílio de uma broca 1093FF, foi confeccionado em cada fatia, uma constrição, com área adesiva de, aproximadamente, 1mm2, em forma de ampulheta. Os testes de microtração foram realizados em máquina de ensaio EMIC, com velocidade de 0,5mm/min. A ANOVA e o Teste de Dunnet indicaram haver diferença estatisticamente significativa entre os grupos testados. Comparando-se o controle positivo (GS) com os demais, verificou-se que apenas o controle negativo (GP) diferiu estatisticamente. Quando se comparou o GP com os outros grupos, foi observada diferença estatística com o GS e o GPA120. Para comparação apenas entre os grupos experimentais (GPA15, GPA30, GPA60 e GPA120), foi aplicado o teste ANOVA e análise de regressão polinomial, que revelaram não haver diferença estatisticamente significativa para o fator tempo, de forma isolada. Foi detectada, através de observações em microscopia eletrônica de varredura, presença de pequenas bolhas no grupo clareado. Os padrões de fratura demonstraram maior número de falhas mistas, para todos os grupos testados. O gel de ascorbil a 3%, aplicado no tempo de duas horas, parece ser o mais indicado, para recuperar os valores de resistência de união ao esmalte clareado com peróxido de carbamida a 10%

Abstract: The purpose of this in vitro study was to evaluate the effect that elapsed time (15 min, 30 min, 1 hour e 2 hours) of a 3% ascorbil gel (AE) onto the bond strength to bovine enamel previously treated with carbamide peroxide at 10%, defining the fracture pattern through electronic scanning microscopy. Sixty bovine incisors were selected, cleaned, and stored in saline solution of timol at 0.1%. Sixty fragments of 25mm2 were obtained by the use of double-face diamond discs, in low rotation, under constant irrigation, perpendicularly to buccal surfaces. The fragments were relieved with a thin layer of wax n° 7 and steep in a cylinder by a self-curing polyester resin. Afterwards, they were random divided into six groups according to the type of treatment to be employed (GS- Positive Control- Saliva, during experiment; GP- Negative Control- PC, 14 days/6hours, GPA15- PC, 14days/6hours + AE, 15 min; GPA30- PC, 14days/6hours + AE, 30 min; GPA60-PC, 14days/6hours + AE, 1 hour; GPA120- PC, 14days/6hours + AE, 2 hours). After treatments, the groups were etched with fosforic acid 35% (Dentsply) and restored with adhesive system Adaper Single Bond (3M-ESPE) and three horizontal increments of resin TPH (Dentsply). Concluded the restorative treatment, the fragments were immediately prepared for microtensile procedure. Serial cuts were performed in each sample to obtain two centralized slices 1mm thick. Afterwards, using a 1093 FF drill, an hourglass was done in each slice, with adhesive area of approximately 1mm2. The microtensile tests were performed in an mechanical test machine, at 0.5 mm/min speed. ANOVA and Dunnett test indicated that there was statistical difference between groups tested. When compared positive control group (GS) with the other groups, it was observed that only the negative control group (GP) was statistically different. These results were confirmed, when the negative control group was compared with others, in which it was observed statistic diference to GS and GPA120. When the experimental groups were compared though regressive polinominal analise it was not found statistical difference only to the time factor. On Electronic Scanning Microscopy observations, were detected the presence of bubbles of the bleached group. The fracture standards demonstrated higher number of mixed failures to all the groups. The 3% ascorbil gel (AE) used for two hours seems to be the most recommended to reverse the strength to bleached enamel with carbamide peroxide 10%
Subject: Dentes - Clareamento
Resistência dos materiais
Antioxidantes
Language: Português
Editor: [s.n.]
Date Issue: 2006
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Silva_AnaPaulaBritoda_M.pdf4.56 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.