Type: DISSERTAÇÃO
Degree Level: Mestrado
Title: Influência do preaquecimento nas propriedades físicas de agentes cimentantes fotoativados através de diferentes espessuras de cerâmica = Influence of pre-heating on the physical properties of luting agents photoactivated through different ceramic thicknesses
Title Alternative: Influence of pre-heating on the physical properties of luting agents photoactivated through different ceramic thicknesses
Author: Lima, Michele de Oliveira, 1991
Advisor: Aguiar, Flávio Henrique Baggio, 1977-
Abstract: Resumo: O propósito deste estudo "in vitro" foi avaliar a influência do preaquecimento e ativação de agentes de fixação através de blocos cerâmicos sobre suas propriedades físicas. Para tanto, os agentes cimentantes RelyX Arc (RXA; 3M/ESPE), RelyX Ultimate (RXU; 3M/ESPE), RelyX Veneer (RXV; 3M/ESPE) e Filtek Z350 Flow (FLK; 3M/ESPE) foram manipulados com diferentes temperaturas (23ºC ou 54ºC), inseridos em matrizes de silicone específicas (cilíndricas: 5x0,5mm ou ampulheta: 0,5mm de espessura, 8mm de comprimento, 4mm de largura e 1,5mm de constrição, de acordo com a metodologia dos testes realizados) e fotoativados sob discos cerâmicos de dissilicato de lítio (IPS e.max; Ivoclar Vivadent, Barueri, SP, Brasil), cor A2, nas espessuras de 0,75mm ou 1,5mm.?A fotoativação foi realizada posicionando a extremidade do aparelho fotoativador sobre o disco cerâmico, para tal foi utilizado o LED Bluephase 16i (Vivadent, B?rs, Austria), com irradiância de 1519 mW/cm², por 40 segundos. Foram confeccionadas 128 amostras cilindricas (n=8) e realizados os testes de grau de conversão (GC) por meio da espectroscopia FT-IR. Estes mesmos espécimes foram levados ao microdurômetro para a mensuração da dureza Knoop (DK) na superfície de topo e logo após, foram imersos em solução de álcool absoluto por 24 h, e então foi realizada uma nova leitura de DK para a obtenção do percentual de redução de dureza e mensuração indireta da densidade de ligações cruzadas (DLC) dos materiais. Foram confeccionadas novas amostras em formato de ampulheta (n=8) que foram utilizadas para o teste de resistência coesiva à tração (RCT), realizado em máquina de ensaio universal. Para os testes de sorção de água (SA) e solubilidade (S) dos agentes de fixação, foram necessários novos espécimes cilíndricos (n=8) que foram pesados em balança analítica até obtenção de massa constante. Os dados foram analisados utilizando-se ANOVA três fatores e teste de tukey (?=0,05). Com relação às espessuras de cerâmica testadas, a menor espessura de cerâmica proporcionou maiores valores de DK (p=0.027). A menor temperatura (23°C) proporcionou maiores valores de SA (p=0.0229) e S (p=0.0257). Também houve diferença estatística para o fator cimento, sendo que para GC, RXA apresentou os maiores valores, seguido dos agentes cimentantes RXV, RXU e FLK. Para o teste de DK e DLC, RXU apresentou os maiores valores, seguido de RXA, RXV e FLK. Para o teste de RCT, RXA apresentou os maiores valores, seguido por RXV, RXU e FLK. Para SA e S, RXV apresentou os maiores valores, seguido por RXA, RXU e FLK. Pode-se concluir que o preaquecimento diminuiu nos resultados de sorção de água e solubilidade; a maior espessura de cerâmica diminuiu apenas a microdureza superficial, e que as propriedades físicas dos materiais são dependentes da composição dos mesmos

Abstract: The purpose of this "in vitro" study was to evaluate the influence of preheating on the physical properties of a luting agent photoactivated through ceramic discs. The cements: RelyX Arc (RXA, 3M / ESPE), RelyX Ultimate (RXU; 3M / ESPE), RelyX Veneer (RXV; 3M / ESPE), and Filtek Z350 Flow (FLK; 3M / ESPE) were manipulated using different temperatures (23°C or 54°C), inserted in specific silicone matrices (cylindrical: 5x0.5mm or hourglass: thickness 0.5 mm, 8 mm in length, 4mm wide and a 1.5mm constriction, according to the methodology of testing) and photoactived under lithium disilicate ceramic discs (IPS e.max, Ivoclar Vivadent, Barueri, SP, Brazil) color A2, in thicknesses of 0.75 mm or 1.5 mm. Photoactivation was carried out by positioning the end of the curing unit on the ceramic disk. A Bluephase 16i (Vivadent, B?rs, Austria), with an irradiance of 1519 mW / cm2, was used for 40 seconds to cure the specimens. One hundred twenty-eight cylindrical samples were prepared (n=8) and the degree of conversion tests (DC) were performed using FT-IR spectroscopy. The samples were taken to a Knoop hardness tester (KHN) for microhardness testing on the top surface. After the initial testing, the specimens were dipped in absolute ethanol solution for 24 h, and then a new KHN reading was performed to obtain the hardness reduction percentage and the crosslink density (CLD) indirect measurement of the material. New samples were prepared with an hourglass shape (n=8) and were used for the ultimate tensile strength (UTS) testing, performed in a universal testing machine. For the water sorption test (WS) and solubility (S) of the luting agents, new cylindrical specimens (n=8) were required which were weighed on an analytical balance until a constant mass was obtained. The data was analyzed using three-way ANOVA and Tukey¿s test (?=0.05). Regarding the tested ceramic thicknesses, the thinnest ceramic gave higher values of KHN (p=0.027). The lowest temperature (23°C) gave higher S (p=0.0257) and WS (p=0.0229) values. There was also a statistically significant difference for cement factor, where RXA showed the highest values for DC, followed by RXV, RXU and FLK. For the KHN and CLD tests, RXU showed the highest values, followed by RXA, RXV and FLK. For the UTS test, RXA showed the highest values, followed by RXV, RXU and FLK. For WS and S, RXV showed the highest values, followed by RXA, RXU and FLK. It can be concluded that pre-heating decreased the results of water sorption and solubility; the biggest ceramic thickness decreased only superficial microhardness, and the physical properties of the material are dependent on the composition thereof
Subject: Temperatura ambiente
Cimentos de resina
Polimerização
Testes de dureza
Language: Multilíngua
Editor: [s.n.]
Citation: LIMA, Michele de Oliveira. Influência do preaquecimento nas propriedades físicas de agentes cimentantes fotoativados através de diferentes espessuras de cerâmica = Influence of pre-heating on the physical properties of luting agents photoactivated through different ceramic thicknesses. 2015. 38 f. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/288862>. Acesso em: 27 ago. 2018.
Date Issue: 2015
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Lima_MicheledeOliveira_M.pdf1.17 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.