Title: Analise fotoelastica do efeito da eletroerosão e sequencias de apertos de parafusos em infra-estrutura implanto-suportada
Title Alternative: Photoelastic analysis of the effect of spark erosion procedure and screw tightening on implant framework
Author: Baboni, Claudia Rahal
Advisor: Nóbilo, Mauro Antonio de Arruda, 1965-
Abstract: Resumo: O presente estudo avaliou através de análise fotoelástica a passividade de infra-estrutura fundida em titânio, antes e após a aplicação de eletroerosão. Foi confeccionada uma matriz metálica simulando uma mandíbula humana onde foram implantados cinco análogos de pilares Micro-Unit (Conect ¿ AR, Conexão Sistemas de Prótese). A partir de um molde de silicone de duplicação foi confeccionado um modelo em resina fotoelástica com cinco implantes osseointegrados incorporados e pilares Micro-Unit. Sobre a matriz metálica foram realizados os procedimentos de enceramento de seis estruturas metálicas, inclusão, fundição em titânio comercialmente puro e acabamento das mesmas. Em todas as amostras foi realizada a soldagem a laser de cilindros de titânio e posterior avaliação em microscópio mensurador com precisão de 0,0005mm. A estrutura com melhor adaptação foi selecionada e submetida a análise fotoelástica conduzida pelo aperto dos parafusos em três seqüências preconizadas (1,2,3,4,5/ 5,4,3,2,1/ 3,2,4,1,5). A mesma estrutura foi submetida ao refinamento de adaptação pela técnica da eletroerosão (EDM) e subseqüente análise fotoelástica. Os resultados mostraram menor formação e intensidade das franjas fotoelásticas após o refinamento por eletroerosão em todas as seqüências de aperto dos parafusos. A seqüência (3,2,4,1,5), mostrou melhores resultados e a maior quantidade de tensões foram observadas ao redor dos implantes mediais em todas as seqüências em ambos os grupos. Pode-se concluir que o processo de eletroerosão melhora a adaptação marginal da infra-estrutura sendo eficaz para o alcance do assentamento passivo

Abstract: Through the photoelastic analysis, the present study evaluated the passive fit of titanium cast laser welding frameworks before and after the spark erosion procedure (Electrical Discharge Machining). A metallic matrix was made simulating a human mandible and, on top of it, 5 Micro-Unit abutment analogs had been implanted. A impression material mold was made and from it a photoelastic matrix had been created with 5 incorporated osseointegrated implants (Conect AR ¿ Conexão Sistemas de Prótese, São Paulo, Brazil) and with Micro-Unit abutment. Based on the metallic model, the following procedures were tested: closing 6 frameworks, embedding, casting in pure commercial titanium and finishing on them. A laser welding followed by an evaluation with microscope measurement with precision of 0.0005mm has been applied in all samples. The frameworks with best results had been selected and submitted to a photoelastic analysis followed by pressing the screws in 3 predisposed sequences (1,2,3,4,5/ 5,4,3,2,1/3,2,4,1,5). The same framework has been submitted to the adaptation refinement by spark erosion technique followed by the photoelastic analysis. The results demonstrated less photoelastics fringes in quantity and intensity after the spark erosion application in all screw pressing sequences. The sequence (3,2,4,1,5) achieved better results in both groups. A higher quantity of fringes had been observed around the medium implants in all sequences and in both groups. We can conclude that the titanium cast laser welded frameworks processes added to an spark erosion procedure improves significantly the marginal frameworks adaptation, which is effective for the passive fit of it
Subject: Fotoelasticidade
Titânio
Language: Português
Editor: [s.n.]
Date Issue: 2006
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Baboni_ClaudiaRahal_M.pdf1.32 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.