Title: Estudo "in vitro" da rugosidade superficial de materiais restauradores submetidos a ensaio de escovação
Author: Samuel, Susana Maria Werner
Advisor: Goes, Mario Fernando de, 1954-
Abstract: Resumo: O objetivo deste trabalho foi avaliar a rugosidade superficial de três marcas comerciais de compósitos (Herculite XR, Prisma APH e P50); dois ionômeros de vidro (Vidrion R e Chelon Fil) e um amálgama (Dispersalloy), submetidos à ação de um dentifrício (Kolynos Super Branco / Anakol), num ensaio de escovação in vitro. Os corpos de prova foram confeccionados em matrizes de plax-glass com dimensões de 20 x 10 x 2 mm, em número de oito, para cada material. Para a realização do ensaio foi utilizada uma máquina de escovação (Equilabor) com escovas extra-macias (Prevent 30 / Anakol) sob a ação de uma carga de 200 g. Cada material foi submetido a 250 escovações por minuto, num período de 2 horas, totalizando 30.000 ciclos por amostra. Com auxílio do perfilômetro Perth-O-Meter M2P (Perthen-Mahr / Alemanha), utilizando o parâmetro Ra (rugosidade média), foram realizadas seis leituras para medida da rugosidade em cada corpo de prova, totalizando 288 leituras no experimento completo. Os resultados da análise estatística mostraram que não houve alteração da textura superficial dos materiais submetidos apenas à ação de uma escova extramacia em água destilada, porém quando foi acrescido o dentifrício, todos os materiais restauradores tiveram a sua topografia alterada. O material que apresentou a superfície-controle com maior rugosidade superficial inicial foi o Dispersalloy (0,6394 µm), seguido pelo Vidrion R (0,2697 µm), Chelon Fil (0,1760 µm), Herculite XR (0,0491 µm), P50 (0,0342 µm) e por último o Prisma APH (0,0338 µm). Porém, esta ordem foi alterada, após o ensaio de escovação, ou seja, o Vidrion R apresentou a maior rugosidade (1,2508 µm), seguido pelo HercuJite XR (1,0300 p,m), Chelon Fil (0,6210 µm), Prisma APH (0,4542 µm), Dispersaloy (0,4082 µm) e por último, o P50 (0,2754 µm). Também foi possível observar que em todos os materiais ocorreu um aumento da rugosidade superficial, exceto para o amálgama, que reduziu a rugosidade inicial para os níveis mais baixos, sem apresentar diferença estatística significativa, a nível de '5% de significância, quando comparado com os materiais menos rugosos após a escovação (APH e P50)

Abstract: The purpose of this study was to evaluate the surface roughness oí direct restorative materiaIs (composite resins, glass ionomers and amalgam) submitted to a in vitro toothbrushing test. Three composite resins (Herculite XR, Prisma APH and P50), two glass ionomers (Vidrion R and Chelon Fil) and an amalgam (Dispersalloy) were studied. Eigth samples of each material were obtained in plaxglass matrices measuring 20 x 10 x 2 mm. The tooth brushing machine had eight containers and the specimens were fixed in the botton of them. The brushes used were the Prevent 30 (Anakol) extra-soft type. These brushes wete glued to the stainless steel brush holder. The load af the brush was 200 g. The toothpaste used for these experimet was Kolynos Super Branco (Anakol), and the slurry was made by mixing 6 ml of distilled water and 6 g of toothpaste. Seven of the eight containers, with the specimens in position, received the slurry, and the last, only distilled water. The eletric motor produced 250 strokes / min and the machine was activated until the counter registered 30,000 strokes. The brushes and the slurry were substituted for each material. Concluded the brushing cycle of two hours the specimens were removed from the machine, washed in tap water and stored at 37ºC and 100% relative umidity of the air until measuring the surface roughness. The specimens were then placed on a profilometer (Perth-O-Meter M2P / Perthen-Mahr) to measure the surface roughness, in micrometers, by the Ra parameter. A total of 288 readings were made in 48 samples. The statistic analyses of the results showed that the brushing with extra-soft brush and water didn't affect the surface topography of the analised materials. But; when the toothpaste was associated to the brushes, all materials showed an alteration of the surface topography. The material with the roughest inicial surface was Dispersalloy (0,6394 µm), followed by Vidrion R (0,2697 µm), Chelon Fil (0,1760 µm), Herculite XR (0,0491 µm), P50 (0,0342 µm) and Prisma APH (0,0338 µm). After the toothbrushing test, the roughest material was Vidrion R (1,2508 µm), followed by Herclliite XR (1,0300 µm), Chelon Fil (0,6210 µm), Prisma APH (0,4542 µm), Dispersalloy (0,4082 µm) and P50 (0,2754 µm). In all materials an increase of the roughness occured except for the amalgam in which the inicial roughness was reduced. There was no statistical difference between the surface of the amalgam when compared with the materiais that showed the less rough surface after brushing (Prisma APH and P50)
Subject: Materiais dentários
Dentes - Cuidado e higiene
Amalgama dentário
Compósitos poliméricos
Language: Português
Editor: [s.n.]
Date Issue: 1993
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Samuel_SusanaMariaWerner_D.pdf3.12 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.