Please use this identifier to cite or link to this item: http://repositorio.unicamp.br/jspui/handle/REPOSIP/288140
Type: TESE
Degree Level: Doutorado
Title: Biomechanical performance of resin composites relying on biomimetic analogs and calcium phosphates for dentin remineralization = Desempenho biomecânico de compósitos experimentais com análogos biomiméticos e fosfatos de cálcio para a remineralização da dentina
Title Alternative: Desempenho biomecânico de compósitos experimentais com análogos biomiméticos e fosfatos de cálcio para a remineralização da dentina
Author: Felizardo, Klissia Romero, 1978-
Advisor: Sinhoreti, Mário Alexandre Coelho, 1969-
Abstract: Resumo: O objetivo do estudo foi gerar uma nova metodologia restauradora, através de um compósito fluído fotopolimerizável com fosfatos de cálcio e incorporação de tri-metafosfato de sódio em primer autocondicionante para auto-produção de fosfoproteína biomineralizadora da matriz de colágeno na interface de união. A hipótese desse trabalho foi de que a inovadora metodologia irá recuperar as propriedades mecânicas, remineralizará e aumentará a longevidade da interface de união. No Capítulo 1 foi realizado análise qualitativa em relação à presença de fosfato e apatita carbonata nas amostras de dentina desmineralizada e após contato com os compósitos experimentais (VSG1- 0% fosfato, VSG2- 10% fosfato, VSG3- 20% fosfato e VSG4- 30% fosfato) armazenados em água destilada e solução de PBS no período de 24h, 7 dias, 1 e 3 meses. As amostras foram analisadas por espectroscopia (ATR / FTIR) e análise microscópica (ESEM / EDX). Os dados foram submetidos à análise de variância de três fatores e teste de Tukey ('alfa'=0.05). Em 24h os maiores picos referentes às bandas de apatita carbonatada (CO32- - v2) fosfato (PO43- - v1,v3) e bruxita (DCPD- vO-H) foram para os grupos VSG2 (água destilada) e VSG3 (PBS). Em 7 dias esses picos diminuiram e ocorreu aumento dos picos para os grupos VSG1 (água destilada), VSG2 (PBS) e VSG4 (PBS). Após 1 mês, o material VSG2 (PBS) apresentou aumento do pico, por outro lado o grupo VSG4 (PBS) manteve-se similar ao do período de 7 dias. Aos 3 meses, nota-se aumento para o material VSG3 (água destilada) e grupo controle (VSG1) em PBS. A análise em EDX não mostrou diferença estatística entre os grupos no decorrer do tempo. No Capítulo 2, o objetivo foi avaliar a influência de fosfato de cálcio como partículas de carga em relação ao grau de conversão, dureza, resistência flexural e módulo elástico. O material experimental VSG4 mostrou maiores valores de dureza após 6 meses e maior grau de conversão nos períodos de 3 meses e 6 meses. Maiores valores de resistência à flexão foram encontrados para o material experimental VSG2 bem como para o material comercial Wave HV (SDI). Maior módulo de elasticidade foi obtido para o material VSG4, valores estes similares aos obtidos para o material comercial Filtek Z350XT (3M/ESPE). Assim, pode-se concluir que a utilização de fosfatos de cálcio não afetou as propriedades mecânicas após envelhecimento em solução de PBS. No Capítulo 3, o objetivo foi avaliar por microscopia de confocal e microscopia óptica a micropermeabilidade por penetração de corante fluoresceína e nanoinfiltração por nitrato de prata amoniacal na camada híbrida assim como a resistência adesiva nos períodos de 24 h e 6 meses em solução de PBS. Os dados referentes ao teste de união foram submetidos à análise de variância de dois fatores e teste de Tukey ('alfa'=0.05). Os resultados mostraram que em relação à resistência adesiva não houve diferença estatística entre os grupos e período de armazenamento. A inclusão de fosfato de cálcio e o uso de tri-metafosfato de sódio auxiliaram no processo de remineralização para o material experimental VSG3 e VSG4 os quais mostraram melhores resultados, reduzindo a permeabilidade dentinária após 6 meses

Abstract: The aim of this study was to generate a new therapeutic restorative methodology through a flowable composite with bioactive calcium phosphates and incorporation of sodium tri-metaphosphate in self-etching primer will serve as a biomimetic analogs to self-phosphoprotein biomineralization production of collagen within the matrix the bonded interface. The hypothesis is that the revolutionary biomineralisation will recover the biomechanical properties, remineralise and increase the longevity of the bonded interfaces. In the chapter 1 was designed to qualitatively compare the presence of phosphate and carbonated apatite between demineralized dentin samples and experimental composite (VSG1- 0% phosphate, VSG2- 10% phosphate, VSG3- 20% phosphate e VSG4- 30% phosphate) storage in distilled water and PBS solution in 24h, 7 days, 1 e 3 months. The samples were analyzed by (ATR/FTIR) and (ESEM/EDX). Data were subjected to variance analysis with three factors and Tukey ('alfa' = 0.05). The results showed that in 24 hours the higher peak related the bands of carbonated apatite (CO32- - v2), phosphate (PO43- - v1,v3) and brushite (DCPD- vO-H) was found to the experimental material VSG2 (distilled water) and VSG3 (PBS). After 7 days, these same peaks suffered a drop therefore having an increased peak to control group VSG1 (distilled water), VSG2 (PBS) and VSG4 (PBS) groups. At 1 month , the material VSG2 (PBS) showed an increase in their peak, on the other hand VSG4 group (PBS solution) was maintained as compared to results 7 days and after 3 months, was an increase in the peaks to VSG3 materials (distilled water) and control group (VSG1) in PBS solution. The EDX analysis showed no statistical difference between the groups over time. In the chapter 2, the objective was to evaluate the in?uence of calcium phosphate as a filler in experimental composite and their correlation with the degree of conversion, microhardness, flexural resistance and elastic modulus. The experimental material VSG4 showed higher hardness values after 6 months and higher degree of conversion at 3 months and 6 months. Further flexural strength values were found for the experimental material VSG2 well as the commercial material Wave HV (SDI). Higher elasticity modulus was obtained for the experimental material VSG4, similar values to the commercial Filtek Supreme (Z350XT- 3M/ESPE). Thus, it can be concluded that the use of calcium phosphate did not affect the mechanical properties after storage in PBS solution. In the chapter 3, the aim was evaluated by confocal microscopy and optcial microscopy the micropermeability by fluorescein dye penetration and the nanoleakage by ammoniacal silver nitrate as well as the adhesive strength over 24h and 6 months in buffer solution (PBS) by microtensile test. Data on microtensile test were subjected to variance analysis with two factors and Tukey ('alfa'= 0.05). The results showed that the bond strength was not statistically different between the experimental groups. The calcium phosphate inclusion as filler particles and the use of tri-sodium metaphosphate aided in the remineralization process mainly to the experimental material VSG3 and VSG4 which showed better micropermeability and nanoleakage reducing dentin permeability after 6 months.
Subject: Fosfato de cálcio
Resinas compostas
Remineralização dentária
Editor: [s.n.]
Date Issue: 2015
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Felizardo_KlissiaRomero_D.pdf5.41 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.