Title: Influencia da escovação mecanica sobre a infiltração marginal de restaurações de amalgama de prata associadas a agentes resinosos e condensadas com diferentes metodos
Author: Berger, Roberta da Silva Nunes
Advisor: Sinhoreti, Mário Alexandre Coelho, 1969-
Abstract: Resumo: o objetivo deste estudo foi avaliar a infiltração marginal de restaurações de amálgama de prata confeccionadas com diferentes métodos de condensação, associadas ou não a diversos agentes resinosos e submetidas ou não à escovação. Para isso utilizou-se 144 dentes molares e pré-molares, divididos em 18 grupos de 8 dentes cada, nos quais foram confeccionadas cavidades classe V (2 mm de profundidade x 3mm de extensão mésio-distal x 1,5 mm de extensão oc1uso-cervical) nas superfícies vestibulares. As cavidades foram restauradas com a liga encapsulada Duralloy (Degussa, SI A) através de 3 maneiras: somente com amálgama de prata ( controle); amálgama associado ao sistema de união Scotchbond Multi-Uso Plus (3M); e amálgama associàdo ao Scotchbond Cimento Resinoso (3M). O amálgama foi condensado utilizando 3 técnicas: manual, mecânica e ultrassônica. Após restauradas e polidas, metade das amostras foram submetidas à escovação mecânica (30.000 ciclos) utilizando uma máquina de escovação Equilabor. Após, todas amostras foram termocicladas 500 vezes, sendo em seguida imersas em solução de azul de metileno a 2% por 4 horas. Os dentes foram seccionados para análise da infiltração e analisados numa lupa estereoscópica (63X). Foi utilizada também microscopia eletrônica de varredura para observação da margem dente-restauração. Os resultados foram analisados estatisticamente, aplicando o teste exato de Fisher. De acordo com os resultados obtidos, conclui-se que de um modo geral as restaurações de amálgama associadas à agentes resinosos apresentaram menor nível de infiltração. Quando realizou-se o pFocedimento de escovação mecânica, nenhum grupo foi influenciado, com exceção do grupo restaurado com amálgama associado ao Scotchbond Multi-Uso Plus com condensação mecânica, que apresentou maior nível de infiltração marginal, quando escovado. As fotomicrografias eletrôRicas de varredura mostraram que nos grupos escovados mecanicamente houve formação de valamento na margem dente/restauração

Abstract: The object of this study was to evaluate the marginal leakage of amalgam restoration associated or not to resinous agents, when they are submitted to brushing using differents resinous agents and differents condensation methods. With this purpose, 144 molar and pre-molar teeth were used and divided into 18 groups of 8 teeth each. Class V cavities preparation (2mm of deep x 3mm of length x 1,5 mm of width) were performed on buccal surface. The cavities were filled with Duralloy capsuled silver alloy (Degussa, SI A) by following different ways: only silver amalgam (control); amalgam associated with SBMU Plus (3M) adhesive system and amalgam associated to the Scotchbond Resin Cement (3M). The amalgam was condensed using 3 differehts technics: manual, mechanic and ultrasonic. After restored and polished, half ofthe samples were submitted to the mechanic brushing (30.000 cycles) using a Equilabor machine and after thermocycled to 500 times, being also immersed into 2% metilene blue solution for microleakage analysis and examined in a stereoscopic loupe (63x). Scanning electronic microscopy was used to analyse the toothlrestoration margin. The results were statistically analysed applying Fisher exact test. According to the results obtained we can conclude that generally, the amalgam restoration associated to resinous agents showed the smaller leveI of microleakage. When the mechanic brushing procedure was performed, any group was influenced, except the group restored with amalgam associated to SBMU Plus with mecharnc condensation, which showed the greatest leveI of microleakage, when brushed. The scanning electronic photomicrography showed that in groups mechanically brushed, noted a gap in the tooth/restoration margin
Subject: Adesivos dentários
Amalgama dentário
Condensação
Language: Português
Editor: [s.n.]
Citation: BERGER, Roberta da Silva Nunes. Influencia da escovação mecanica sobre a infiltração marginal de restaurações de amalgama de prata associadas a agentes resinosos e condensadas com diferentes metodos. 1999. 125p. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/288114>. Acesso em: 24 jul. 2018.
Date Issue: 1999
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Berger_RobertadaSilvaNunes_M.pdf4.59 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.