Title: Estudo de diferentes fotoiniciadores em cimentos resinosos experimentais fotoativados com duas fontes de luz
Title Alternative: Study of diferent photoinitiators in experimental resin cements photoactivated by two light curing units
Author: Segreto, Dario Raimundo
Abstract: Resumo: O objetivo deste estudo foi avaliar o efeito de diferentes fotoiniciadores no grau de conversão e na resistência da união de cimentos resinosos experimentais, utilizados para fixação de uma cerâmica à estrutura dental. Sete cimentos resinosos experimentais foram manipulados de maneira que, na matriz orgânica padrão, o único componente variável fosse o fotoiniciador. Diferentes concentrações e combinações de Canforoquinona (CQ) e Fenilpropanodiona (PPD) foram adicionadas aos cimentos, conforme segue: C5=0,5% p CQ; C8=0,8% p CQ; P5=0,5% p PPD; P8=0,8% p PPD; C1P4=0,1% p CQ e 0,4% p PPD; C4P1=0,4% p CQ e 0,1% p PPD; e C4P4=0,4% p CQ e 0,4% p PPD. O primeiro estudo avaliou o grau de conversão de cimentos resinosos fotoativados através de um disco cerâmico com unidades de fotoativação a base de LED e lâmpada de quartzo-tungstêniohalogênio (QTH). Quarenta e duas amostras foram preparadas para Espectroscopia FTIR (n=3). As amostras foram confeccionadas em molde circular de teflon, sobre o qual foi posicionado um disco de cerâmica feldspática da cor A3 (IPS e.max Ceram, Ivoclar /Vivadent) e a fotoativação realizada através da cerâmica com QTH (XL2500, 3M/ESPE) e LED (Ultralume Led5, Ultradent), por 100 s. Após armazenagem por 24 h a 37oC em ambiente escuro, as amostras foram trituradas, misturadas com Brometo de Potássio (KBr) e prensadas para obtenção de pastilhas para análise por Espectroscopia FTIR. A análise estatística não mostrou diferença significativa entre as fontes de luz (p>0,05), independente dos demais fatores. O cimento P8 apresentou a maior média de grau de conversão. Com QTH, P8 foi maior (60 % ± 1,6) e apresentou diferença estatística significativa em relação à C1P4 (50,7 % ± 1,8), C4P1 (50,4 % ± 1,2) e C5 (47,1 % ±1,2). Com LED, P8 foi maior (58,8 % ± 4,3), porém com diferença estatística significativa apenas em relação à C4P1 (50,9 % ± 3,3) e C5 (48,4 % ± 2,5). O segundo estudo investigou o efeito dos diferentes fotoiniciadores e das fontes de luz na resistência da união de uma cerâmica à dentina bovina. Discos cerâmicos silanizados foram unidos à dentina bovina com os cimentos experimentais, que foram fotoativados com LED (Ultralume Led 5) e QTH (XL 2500), por 100 s. Após 24 h a 37oC e 100% de umidade relativa, foram submetidos ao teste de microtração (µTS) em máquina de ensaios universal Instron (Mod. 4411, USA). Os cimentos P5, C5 e C4P1 mostraram diferença estatística quando ativados pelas duas fontes de luz, sendo que P5 e C5 foram superiores com QTH e C4P1 com o LED. Além disso, P5 obteve a maior média de resistência (19,6 MPa ± 3,51) com QTH, porém foi estatisticamente igual C5 (16,8 MPa ± 1,62), C4P4 (16,2 MPa ±2,93) e P8 (15,4 MPa ± 2,34). Para o LED, C4P1 obteve a maior média de resistência (20,1 MPa ± 3,4) e foi estatisticamente superior aos demais grupos. Portanto, QTH e LED são efetivos na fotoativação de cimentos resinosos mesmo através da cerâmica da cor A3 com 1,4 mm de espessura. O PPD mostrou ser alternativa viável como fotoiniciador em cimentos resinosos e pode ser adequadamente fotoativado com aparelhos LED.

Abstract: The aim of this study was to evaluate the effect of different photoinitiators on the degree of conversion and microtensile bond strength of the photoactivated resin cement used to fix a ceramic veneer on the dental structure. Seven experimental resin cements was manipulated, as the organic matrix was standardized the only variable component was the photoinitiators. Different concentrations and combinations of Canphoroquinone (CQ) and Phenylpropanodione (PPD) were added in cements as following: C5=0.5% wt CQ; C8=0.8% wt CQ; P5=0.5% wt PPD; P8=0.8% wt PPD; C1P4=0.1% wt CQ and 0.4% wt PPD; C4P1=0.4% wt CQ and 0.1% wt PPD; and, C4P4=0.4% wt CQ and 0.4% wt PPD. The first study evaluated the influence of different combinations of photoinitiators in the degree of conversion on the resin cement photoactivated by LED and quartz- tungstenhalogen (QTH) through ceramic veneer. Forty two samples was prepared to Spectroscopy FTIR (n=3). The samples was made in round teflon mold and a feldspatic ceramic disc shade A3 (IPS e.max Ceram, Ivoclar /Vivadent) was placed over the mold and the photoactivation was carried through the ceramic with QTH (XL2500, 3M/ESPE) and LED (Ultralume Led5, Ultradent) for 100s. After 24 h at 37oC of dark storage, the samples were triturate, mixed with 100 mg of KBr powder salt and pressed to obtain a pellet to analyze Spectroscopy FTIR. The statistical analyze showed no significant difference between the light curing units (p>0,05), independent of the other factors. The P8 cement presented the major means of the degree of conversion. With QTH, P8 was major (60 % ± 1,6) and presented significant statistical different when was compared to C1P4 (50,7 % ± 1,8), C4P1 (50,4 % ± 1,2) and C5 (47,1 % ±1,2). With LED, P8 was major (58,8 % ± 4,3), but with significant statistical different only the C4P1 (50,9 % ± 3,3) and C5 (48,4 % ± 2,5) cements (p>0,05). The second work investigated the effect of different photoinitiators on the microtensile bond strength of photoactivated resin cement used to fix a ceramic to the bovine dentin. Silanized Ceramic discs were bonded to the bovine dentin with the experimental cement photoactivated by LED and QTH for 100s. After 24hs at 37oC and 100% relative wetting, the samples was submitted to the microtensile test in universal trail machine Instron (Mod. 4411, USA). The P5, C5 and C4P1 cements showed significant statistical different to the light curing units, however P5 e C5 was superiors with QTH and C4P1 was better with LED. Additionally, P5 obtain the major means of bond strength (19,6 MPa ± 3,51) with QTH, but no statistical difference was observed with C5 (16,8 MPa ± 1,62), C4P4 (16,2 MPa ±2,93) and P8 (15,4 MPa ± 2,34). With LED, C4P1 obtain the major means of bond strength (20,1 MPa ± 3,4) and presented significant statistical different to the other groups. Therefore, QTH and LED are effectives in the photoactivation of the resin cements through the ceramic with 1,4 mm height. More and then, PPD is viable alternative like photoinitiator in resin cements and it can be adequately photoactivated by LED light curing units.
Subject: Materiais dentários
Language: Português
Editor: [s.n.]
Citation: SEGRETO, Dario Raimundo. Estudo de diferentes fotoiniciadores em cimentos resinosos experimentais fotoativados com duas fontes de luz. 2009. 60 f. Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Campinas, SP. Disponível em: http://www.repositorio.unicamp.br/handle/REPOSIP/288113. Acesso em: 13 Jan. 2021.
Date Issue: 2009
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Segreto_DarioRaimundo.pdf5.03 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.