Type: | DISSERTAÇÃO |
Degree Level: | Mestrado |
Title: | Supercondutividade em materiais à base de carbono |
Title Alternative: | Superconductivity in the carbon-based materials |
Author: | Merlo, Rafael Borges, 1983- |
Advisor: | Kopelevitch, Iakov Veniaminovitch, 1959- |
Abstract: | Resumo: Evidências experimentais e teóricas recentes de que a supercondutividade nas várias formas alotrópicas do carbono pode ocorrer em temperaturas próximas ou até acima da temperatura ambiente, desencadearam um grande interesse científico. Resultados do presente trabalho demonstraram a ocorrência de supercondutividade em compósitos de carbono vítreo-enxofre (CV-S) a T = 3 K. Nossas medidas revelaram que a supercondutividade ocorre em uma pequena fração da amostra, e que a grafitização do carbono amorfo parece ser uma condição necessária para disparar a supercondutividade. Apresentamos também evidências de supercondutividade à temperatura ambiente em sanduíches de grafite/Si, e demonstramos que a supercondutividade está associada à interface grafite/silício. O comportamento encontrado é semelhante ao conhecido para estruturas supercondutoras de baixadimensionalidade. Em particular, observamos oscilações do tipo Josephson em curvas características de corrente-tensão (I-V), bem como sua supressão pela aplicação de campo magnético. Além disso, o campo magnético perpendicular transforma as curvas características I-V do tipo supercondutor para tipo isolante, assemelhando-se à transição supercondutor-isolante induzida por campo magnético em redes de junções Josephson. Todos estes resultados indicam que a interface grafite/silício pode ser um material promissor para o desenvolvimento de dispositivos microeletrônicos sem dissipação à temperatura ambiente Abstract: Recent both experimental and theoretical evidence that superconductivity in various allotropic forms of carbon can occur at temperatures near or even above room temperature, triggered a broad scientific interest. Results of the present work demonstrated the occurrence of superconductivity in carbon glassy-sulfur composites (CV-S) at T = 3 K. Our measurements revealed that the superconductivity occurs in a small fraction of the sample, and that the graphitization of the amorphous carbon seems to be a necessary condition to trigger the superconductivity. We also present evidence for the room temperature superconductivity in graphite/Si sandwiches and demonstrate that the superconductivity is associated with the graphite/silicon interface. The found behavior is similar to that known for low-dimensional superconducting structures. In particular, we have observed Josephson-type oscillations in current-voltage (I-V) characteristics as well as their suppression by applied magnetic field. Moreover, the perpendicular magnetic field transforms the superconducting-like to insulating-like I-V characteristics resembling the magnetic-field-driven superconductor-insulator transition in Josephsonjunction-arrays. All these results indicate that graphite-silicon interface can be a promising material for the development of microelectronic devices without dissipation at room temperature |
Subject: | Supercondutividade Carbono vítreo Enxofre Grafita Silício |
Language: | Português |
Editor: | [s.n.] |
Citation: | MERLO, Rafael Borges. Supercondutividade em materiais à base de carbono. 2011. 111 p. Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/277964>. Acesso em: 19 ago. 2018. |
Date Issue: | 2011 |
Appears in Collections: | IFGW - Tese e Dissertação |
Files in This Item:
File | Size | Format | |
---|---|---|---|
Merlo_RafaelBorges_M.pdf | 2.8 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.