Title: Desenvolvimento de catalisadores massicos de aluminio, niquel e cobre para a sintese de alcoois superiores
Author: Fachini, Adriano
Advisor: Jordão, Elizabete, 1956-
Abstract: Resumo: Neste trabalho foi desenvolvido um catalisador mássico à base de óxidos mistos de Alumínio, Níquel e Cobre com vistas à utilização em sínteses de álcoois superiores a partir de gás de síntese (CO/H2). Para tanto foi realizado um estudo da preparação tendo por base patentes desenvolvidas pelo Instituto Francês do Petróleo (IFP) e outros trabalhos anteriormente desenvolvidos. Os resultados experimentais obtidos para os sistemas AINiCu demonstraram, através dos perfis de redução gravimétricos, a presença de uma liga Ni-Cu, confirmada pelos ensaios termogravimétricos. Por sua vez, a caracterização do catalisador preparado revela a obtenção de um sólido com propriedades fisico-químicas muito semelhantes às de um sólido industrial de referência, sugerindo que as condições adotadas para a preparação conduzem a um catalisador produtivo na reação de síntese de álcoois superiores. Os testes catalíticos, realizados a 2500 C e 50 atm, com o sistema AlNiCu N mostraram um alta conversão a álcoois,particularmentea metanol, ao contrário do observado para o catalisador industrial, AICoCu, que apresentou alta conversão a alcanos, especialmente a metano, nas mesmas condições reacionais

Abstract: A new massic catalyst based upon Aluminum, Nickel and Copper oxides was prepared to be used in higher alcohol synthesis, by the same method previously developed by Institut Français du Pétrole (IFP), where Cobalt was used instead of Nickel in a commercial catalyst. Results obtained by Atomic Absorption, Superficial Area Measurements and X-Ray Diffraction (XRD) showed that the nickel catalysts have physical properties similar to those found for the commercial catalyst. The reducibility study was performed using Thermal Analysis Technics, as Thermogravimetric Analysis (TGA) and Temperature Programmed Reduction (TPR) and the analysis of reduction profiles indicated a decrease in the reduction temperature of catalysts from 6000C to 2200C when Copper was added to AI-Ni systems. This was caused due to the formation of a Ni-Cu alloy that enhances the reducible ability of the catalyst precursor. The kinetic tests performed at 2500C and 50 atm for the AINiCuN catalyst showed a high conversion rate to alcohols, particularly methanol, contrary to those obtained for the industrial catalyst, AICoCu, where mainly alcanes have been obtained, under the same reaction conditions
Subject: Catalisadores de niquel
Catalisadores de cobre
Alcoois
Language: Português
Editor: [s.n.]
Date Issue: 1995
Appears in Collections:FEQ - Dissertação e Tese

Files in This Item:
File SizeFormat 
Fachini_Adriano_M.pdf2.8 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.