Title: Efeito do uso de compabilizante e do tempo de processamento sobre as propriedades termicas, morfologicas, reologicas e mecanicas da blenda PET/PP
Author: Kitaoka, Roberto Soji
Advisor: Chang, Tien-Kiang, 1957-
Kiang, Chang Tien, 1957-
Abstract: Resumo: Neste trabalho são estudados os efeitos do tempo de processamento sobre as propriedades do Poli(etileno tereftalato) (PET), Polipropileno (PP) e as misturas PET/PP. Analisou-se ainda a influência da adição de compatibilizante, polipropileno graftizado com anidrido maleico (PP-g-AM), à mistura. As amostras foram processadas no ¿Mini Max Molder CS183MMX¿, à temperatura de '265 GRAUS¿C, com tempos de processamento de: 1 minuto e 20 segundos; 5 minutos; 10 minutos; e 15 minutos, em composição (PET/PP) de: 100/0; 90/10; 80/20; 70/30; 60/40; 50/50; e 0/100, em peso. Também foram preparadas blendas compatibilizadas com 3% de PP-g-AM, em relação ao peso total da mistura. As amostras foram analisadas através de ensaios reológicos, mecânicos, térmicos e morfológicos. A caracterização reológica foi realizada utilizando o reômetro ortogonal de discos paralelos e eixos excêntricos, o ¿Mini Max Dynamic Tester CS-183DY¿. Foram determinados os módulos elásticos (G¿) e de perda (G¿), afim de observar algum tipo de degradação no processamento da mistura e efeito do compatibilizante sobre o comportamento viscoelástico da blenda. As alterações provocadas pelo processo de mistura na cinética de cristalização do PET e na temperatura de cristalização dos componentes na mistura foram estudadas por calorimetria diferencial de varredura (DSC), utilizando dois métodos: cristalização isotérmica e cristalização não isotérmica... Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital

Abstract: This work the study of the effects of the processing time and compatibilizer addition on the properties of poly(ethylene terephthalate) (PET), polypropylene (PP) and PET/PP blends. The samples were prepared by melt blending in the Mini Max Molder CS-183MMX, at '265 DEGREES¿C, with processing time of: 1 min. 20 sec.; 5 min.; and 15 min. The PET/PP blend compositions (wt/wt) used in this work were: 100/0; 90/10; 70/30; 50/40; 50/50; and 0/100; with and without 3% of Polypropylene grafted Maleic Anhydride (PP-g-MA). The samples were studied by thermal, morphological, rheological and mechanical analysis. The rheological characterization was evaluated by eccentric-disk-orthogonal rheometer, ¿Mini Max Dynamic Tester CS-183DY¿. The measurements of the dynamic modulus G¿ and G¿, were used to observe the compatibilization effect and polymer degradation on the viscoelastic behavior of the blends. The modification caused by the blending process in PET¿s crystallization temperature, were studied by Differential Scanning Calorymetry (DSC) using two methods: anisothermal and isothermal crystallization. The morphological analysis were performed by Scanning Electron Microscopy (SEM) in which it was observed a strong influence of compatibilizer and processing time in dispersion grade and phase diameter. The best dispersion was obtained with processing time of 15 minutes and compatibilizer addition... Note: The complete abstract is available with the full electronic digital thesis or dissertations
Subject: Polipropileno
Polímeros - Testes
Mistura (Quimica)
Language: Português
Editor: [s.n.]
Date Issue: 1997
Appears in Collections:FEQ - Tese e Dissertação

Files in This Item:
File SizeFormat 
Kitaoka_RobertoSoji_M.pdf2.84 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.