Title: Influência das condições de fresamento na integridade superficial do aço inoxidável 15-5PH
Title Alternative: Influence of milling conditions on surface integrity of 15-5PH stainless steel
Author: Pereira, Luis Antonio, 1978-
Advisor: Hassui, Amauri, 1967-
Abstract: Resumo: O fresamento consiste em um processo de usinagem no qual a peça a ser usinada é efetua os movimentos de avanço contra uma ferramenta cilíndrica rotativa com várias arestas de corte. No processo de fresamento o corte é considerado crítico, pois neste momento as variações de temperatura e força resultam em danos nas superfícies das peças, podendo comprometer o seu desempenho. Com isso, vários estudos buscam alternativas que visam explicar as ocorrências desses defeitos. Esse campo é conhecido também como Integridade Superficial. Este trabalho tem por objetivo avaliar as influências das condições de usinagem na integridade de superficial do aço inoxidável 15-5PH. Para isso foram feitos ensaios de fresamento utilizando fresa de facear com pastilhas redondas, geometria neutra e positiva, novas e em fim de vida. O fresamento foi discordante, com dois níveis de avanço por dente (fz = 0,15 e 0,25 mm/dente) e dois de velocidade de corte (vc = 170 e 195 m/min). Posteriormente foi avaliada a rugosidade 3D, dureza e feita a microscopia eletrônica da superfície e subsuperfície da peça usinada. Os resultados obtidos demonstram que utilizando uma ferramenta da classe (M40), com a geometria M-MM (positiva) com cobertura de MTCVD, obteve-se uma rugosidade melhor que a (M25). Foi possível também evidenciar os defeitos gerados na superfície usinada com a utilização do (MEV), microcavidades, sulcos gerados por microcavacos, repasse da ferramenta e resto de material

Abstract: Milling is a machining process in which the workpiece makes feed movements against a rotating cylindrical tool with multiple cutting edges. In the milling process the cut is considered critical because at this time the temperature and force variations result in damage to the surfaces of the workpiece, which can compromise their performance. Consequently, several studies aim to explain the occurrences of failures. This field is also known as Surface Integrity. This work aims to evaluate the influence of machining conditions on the surface integrity of stainless steel 15-5PH. In order to do so, milling tests were carried on using face mills with round inserts, neutral and positive geometry (new and in the end of tool life). Up milling condition along with two levels of feed per tooth (fz = 0.15 and 0.25 mm/tooth) and two cutting speeds (vc = 170 and 195 m/min). Later, the 3D roughness and hardness were evaluated and scanning electron microscopy (SEM) was carried on the workpiece¿s surface and subsurface. The results obtained show that using (M40) class tool, and M-MM geometry (positive) with MTCVD coating provided a better surface finish than the (M25) class tool. Using the (SEM), it was also possible to highlight the defects generated in the machined surface such as microcavities, grooves generated by microchips, tool backcutting and the remaining material
Subject: Usinagem
Fresamento
Aspereza de superfície
Integridade estrutural
Aço inoxidável
Editor: [s.n.]
Citation: PEREIRA, Luis Antonio. Influência das condições de fresamento na integridade superficial do aço inoxidável 15-5PH. 2014. 101 p. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica , Campinas, SP. Disponível em: http://www.repositorio.unicamp.br/handle/REPOSIP/265865. Acesso em: 15 Jul. 2020.
Date Issue: 2014
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Pereira_LuisAntonio_M.pdf7.15 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.