Title: Efeito da adição de nióbio e molibdênio na deformação plástica e decomposição isotérmica da austenita em aços 0,7 %C
Title Alternative: Effect of niobium and molybdenum addition on plastic deformation and isothermal decomposition of austenite in 0.7 %C steels
Author: Finamor, Felipe Pereira, 1986-
Advisor: Mei, Paulo Roberto, 1953-
Abstract: Resumo: O aumento da razão da carga transportada por eixo tem sido fundamental para redução dos custos de transporte, porém é exigido cada vez mais das interações roda-trilho. Neste aspecto para se garantir a segurança dos bens transportados e o menor desgaste da roda é necessário o desenvolvimento de novos aços com maior dureza, porém sem redução de ductilidade. Uma das estratégias é se adicionar aos mesmos microadições (< 0,5 % em massa) de nióbio ou vanádio, os quais, em solução sólida na austenita atrasam sua decomposição em produtos difusionais, elevando a resistência mecânica dos aços. Neste trabalho foram avaliados dois aços com 0,7 %C microligados ou não ao nióbio-molidbênio e produzidos pela MWL Brasil para a fabricação de rodas ferroviárias, segundo a classe D da AAR (Association of American Railroads). Foram realizados ensaios dilatométricos para o levantamento das curvas de transformação isotérmica e o estudo das curvas de escoamento à quente dos aços microligados e não microligados através dos ensaios de compressão à quente de único passe. A adição dos microligantes provocaram atrasos na cinética de transformação austenita/perlita na ordem de 4 vezes e um pequeno aumento da dureza dos produtos de reação no aço microligado ao nióbio e molibdênio para as transformações isotérmicas avaliadas por dilatometria e aumentaram numa razão de 1,3 a 1,4 as tensões de pico e em 1,5 a 3 as deformações de pico para todas as faixas de temperatura e deformação analisadas para o aço microligado

Abstract: The increase in cargo transported by axis has been a critical factor in reducing transportation costs, requiring more and more of the wheel-rail interaction. In this aspect to ensure the safety of transported goods and the a reduction in the wear of the railwheel is necessary to develop new steels with higher hardness without loosing ductility. One strategy is to add small amounts of alloy elements (<0.5 wt%) of niobium or vanadium which in solid solution in austenite retards the diffusional decomposition and raise the mechanical strength of the steels. The object of this study was to evaluate two steels with 0.7 % C microalloyed or not with niobium-molybdenum, which were produced by MWL Brasil for the production of railway wheels, according to Class D of AAR (Association of American Railroads) standards. Dilatometric tests were carried out to evaluate the isothermal transformation of microalloyed or not steels, and the flow curves were evaluated through microalloyed steels or not in a single hot compression tests. The addition of microalloying elements have delayed the kinetics of austenite transformation to pearlite in the order of 4 times and slightly increase the hardness of the reaction products in niobium and molybdenum microalloyed steel for isothermal transformations evaluated by dilatometry and increased in a ratio of 1.3 to 1.4 the peak stresses and 1.5 to 3 the peak strain for all ranges of temperature and strain analyzed for the microalloyed steel
Subject: Aço
Nióbio
Molibdênio
Diagramas de transformação isotérmica
Deformação plástica
Editor: [s.n.]
Citation: FINAMOR, Felipe Pereira. Efeito da adição de nióbio e molibdênio na deformação plástica e decomposição isotérmica da austenita em aços 0,7 %C. 2015. 85 p. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/265758>. Acesso em: 28 ago. 2018.
Date Issue: 2015
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Finamor_FelipePereira_M.pdf6.93 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.