Title: Estudo da microestrutura e propriedades mecânicas de estruturas porosas de Ti-6Al-4V produzidas por sinterização seletiva a laser
Title Alternative: Study of microstructure and mechanical properties of Ti-6Al-4V porous parts produced by selective laser sintering
Author: Sallica Leva, Edwin, 1982-
Advisor: Fogagnolo, João Batista, 1964-
Abstract: Resumo: Peças fabricadas em titânio com estrutura porosa apresentam vantagens como material para implantes basicamente pela redução do módulo de elasticidade, o que aproxima sua rigidez à de tecidos ósseos, tornando-as mais adequadas á sua função. Neste trabalho apresenta-se um estudo da microestrutura e propriedades mecânicas de peças porosas de Ti-6Al-4V fabricadas por sinterização seletiva a laser, que é uma das técnicas de prototipagem rápida, que consolida, camada a camada, peças com geometria complexa a partir de pó. As estruturas porosas foram modeladas em programa CAD e fabricadas em um equipamento EOSINT M 270. Os modelos computacionais têm forma cúbica com 15 mm de aresta e possuem arquitetura interna de poros interconectados também de forma cúbica. A porcentagem de porosidade foi variada na faixa de 61 a 76%, mudando-se o número e o tamanho dos poros e a espessura das paredes internas. Pó atomizado da liga Ti-6Al-4V foi utilizado como matéria-prima. Utilizaram-se dois níveis de energia fornecida, variando-se alguns parâmetros do processo, como a velocidade de varredura do feixe de laser, a potência do laser e distância entre linhas de sinterização. As amostras sinterizadas foram caracterizadas por microscopia óptica e eletrônica de varredura, ensaios de dureza e compressão. Em uma segunda etapa, foram realizados tratamentos térmicos em amostras com 69% de porosidade projetada. As peças sinterizadas apresentaram microestrutura martensítica, porosidade interconectada na faixa de 63 a 77%, com boa formação de parede, e superfície rugosa com aderência de partículas de pó não sinterizado. Testes de compressão das amostras sinterizadas mostraram que o módulo de Young variou de 5,36±0,01 a 8,73±0,07 GPa, o limite de escoamento variou de 91,5±0,7 a 170±5 MPa e a resistência mecânica à compressão variou de 106±1 a 219±5 MPa, dependendo da porcentagem de porosidade. O aumento da energia do processo resultou em paredes mais finas, para o mesmo modelo, e também uma porosidade não controlada, interna às paredes das peças, o que reduziu a rigidez e a resistência mecânica das peças. Os tratamentos térmicos feitos nas peças porosas com 69 % de porosidade projetada promoveram mudanças microestruturais, mas não resultaram em aumento das propriedades mecânicas

Abstract: Titanium porous parts have advantages as materials for implants due to their lower modulus of elasticity, which approximates their stiffness to the bone tissue stiffness, making them more appropriate to their biofunction. In this work we present a microstructural characterization and a mechanical property evaluation of porous parts of Ti-6Al-4V produced by selective laser sintering, which is a rapid prototyping technique that consolidates, layer by layer, parts with complex geometry from powder. The porous structures were designed in a CAD program and manufactured in the EOSINT 270 laser-sintering system. The computational models have cubic shape with 15 mm edge and an internal architecture of interconnected pores also with cubic shape. The percentage of porosity was varied in the range from 61 to 76 % by changing the number and size of the porous and the thickness the struts. Powder prealloyed of Ti-6Al-4V was using as raw material. Two energy levels were tested, by varying the process parameters, such as laser power, speed of laser and spacing between laser tracks. The as-sintered samples were characterized by optical and scanning electron microscopy, hardness and compressive tests. Further, thermal treatments were performed on samples with 69% of modeled porosity. The sintered parts presented martensitic microstructure, with interconnected porosities varying from 63-77%, with good formation of struts, and rough surface with adhesion of no-sintered powder particles. The compression tests of as- sintered samples showed the Young's modulus values ranging from 5.36 ± 0.01-8.73 ± 0.07 GPa, the yield strength values ranging from 91.5 ± 0,7-170 ± 5 MPa and the compressive strength values ranging from 106 ± 1-219 ± 5 MPa, depending on the percentage of porosity. Increasing the energy of the process resulted in thinner struts for the same model and also a no-controlled porosity in the internal struts of parts, which reduced the stiffness and the mechanical strength of the parts. Heat treatments performed in the porous parts with 69% porosity promoted microstructurals changes, but did not result in an increase of the mechanical properties
Subject: Biomateriais
Prototipagem rápida
Materiais porosos
Metalurgia do pó
Language: Português
Editor: [s.n.]
Citation: SALLICA LEVA, Edwin. Estudo da microestrutura e propriedades mecânicas de estruturas porosas de Ti-6Al-4V produzidas por sinterização seletiva a laser. 2012. 93 p. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/264980>. Acesso em: 20 ago. 2018.
Date Issue: 2012
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
SallicaLeva_Edwin_M.pdf24.93 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.