dc.descriptionOrientador: Itamar Ferreirapt_BR
dc.descriptionDissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanicapt_BR
dc.format.extent153p. : il.pt_BR
dc.format.mimetypeapplication/pdfpt_BR
dc.languagePortuguêspt_BR
dc.typeDISSERTAÇÃOpt_BR
dc.titleUma metodologia para a avaliação dos gradientes de tenacidade a fratura ao longo da camada cementada do aço SAE 5115pt_BR
dc.title.alternativeA model for fracture toughness evaluation of the carburized layer for SAE 5115 steelpt_BR
dc.contributor.authorSandor, Leonardo Tabordapt_BR
dc.contributor.advisorFerreira, Itamar, 1952-pt_BR
dc.contributor.institutionUniversidade Estadual de Campinas. Faculdade de Engenharia Mecânicapt_BR
dc.subjectMecânica da fraturapt_BR
dc.subjectFractografiapt_BR
dc.subjectMetalografiapt_BR
dc.subjectAço - Fadigapt_BR
dc.subjectProcesso de endurecimento superficialpt_BR
dc.subjectAço de alta resistenciapt_BR
dc.subject.otherlanguageFracture mechanicsen
dc.subject.otherlanguageFractographyen
dc.subject.otherlanguageMetallographyen
dc.subject.otherlanguageSteel fadigueen
dc.subject.otherlanguageCase hardeningen
dc.subject.otherlanguageHigh strength steelen
dc.description.abstractResumo: Este trabalho propõe um modelo para avaliar pontualmente as variações de tenacidade à fratura ao longo da camada cementada de um aço SAE 5115. A pequena espessura dessas camadas impede a retirada de corpos de prova nas dimensões especificadas pelas normas de ensaios de tenacidade à fratura. Assim, para simular uma camada cementada retirou-se corpos de prova de tração e de tenacidade à fratura de amostras de aços SAE 5115, 5140, 5160 e 52100 assumindo a influência local apenas da variação do teor de carbono e considerando que os teores dos demais elementos de liga são essencialmente constantes. Os corpos de prova após eletrodeposição de cobre foram tratados termicamente numa carga industrial de cementação, têmpera e revenimento para serem submetidos aos efeitos térmicos sem absorção de carbono. Os resultados da análise microestrutural, dos ensaios de microdureza, de tração e de tenacidade à fratura foram agrupados em um único gráfico e comparados com o perfil de cementação de peças de aço SAE 5115 tratadas nas mesmas condições. Foi confirmado que a tenacidade à fratura varia inversamente proporcional à microdureza (HV1) e que a previsão do comportamento de uma trinca numa camada cementada pode ser feita por meio de equação ou diagrama que relacionam a miicrodureza HV1 com a tenacidade à fratura (K1c ou CTODc)pt
dc.description.abstractAbstract: The purpose of this work is to propose a model for evaluating the fracture toughness along the SAE 5115 steel carburized layer. Due to the small thickness of those layers, it is impossible to machine specimens from those layer in accordance with standards. For simulating the microstructures of the carburized layer in order to get samples for tensile and the fracture toughness testing, specimens of SAE 5115, 5140, 5160, and 52100 steels assuming the local influence just of the variation of the content of carbon and considering that the contents of the other alloy elements are essentially constant. The specimens after electroplated copper layer were heat treated in an industrialload of carburizing, quenching, and tempering for they be submitted to the thermal effects without absorption of carbono The results of the microstructure analysis and microhardness, tension, and fracture toughness tests were placed in a single graph and compared with the profile of the carburizing of the steel SAE 5115 heat treated in the same conditions. It was confirmed that the fracture toughness varies inversely proportional to the microhardness (HV1) and that the forecast of the behavior of a crack in a carburized layer can be made through equation or it designs that relate the microhardness (HV1) with the fracture toughness (KIC or CTODc)en
dc.publisher[s.n.]pt_BR
dc.date.issued2005pt_BR
dc.identifier.citationSANDOR, Leonardo Taborda. Uma metodologia para a avaliação dos gradientes de tenacidade a fratura ao longo da camada cementada do aço SAE 5115. 2005. 153p. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/264971>. Acesso em: 4 ago. 2018.pt_BR
dc.description.degreelevelMestradopt_BR
dc.description.degreedisciplineMateriais e Processos de Fabricaçãopt_BR
dc.description.degreenameMestre em Engenharia Mecânicapt_BR
dc.contributor.committeepersonalnameButton, Sergio Toninipt_BR
dc.contributor.committeepersonalnameTarpani, Jose Ricardopt_BR
dc.date.defense2005-03-28T00:00:00Zpt_BR
dc.date.available2018-08-04T09:29:09Z-
dc.date.accessioned2018-08-04T09:29:09Z-
dc.description.provenanceMade available in DSpace on 2018-08-04T09:29:09Z (GMT). No. of bitstreams: 1 Sandor_LeonardoTaborda_M.pdf: 9634671 bytes, checksum: 3b7603db85e265d8bd0e3fc244928942 (MD5) Previous issue date: 2005en
dc.identifier.urihttp://repositorio.unicamp.br/jspui/handle/REPOSIP/264971-
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Sandor_LeonardoTaborda_M.pdf9.41 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.