Type: DISSERTAÇÃO
Degree Level: Mestrado
Title: Análise de falhas em instrumentais cirúrgicos metálicos
Title Alternative: Failure analysis in metallic surgical instruments
Author: Lima, Lonetá Lauro, 1982-
Advisor: Zavaglia, Cecília Amélia de Carvalho, 1954-
Abstract: Resumo: Este trabalho foi desenvolvido juntamente com a equipe de enfermagem do HC da Unicamp. O principal objetivo foi avaliar os modos de falhas presentes em pinças hemostáticas retas e curvas de fabricação nacional, que já haviam sido utilizadas pelo Hospital das Clínicas da Unicamp e que falharam prematuramente durante o uso. Os parâmetros avaliados estão relacionados com a qualidade da matéria-prima, propriedades mecânicas e com o processo de fabricação. As pinças foram avaliadas segundo as normas internacionais da ASTM, entre elas a ASTM F 899-09, a ASTM F 1744-96(2008) e a ASTM F 1026-86(2008). As fraturas ocorridas nas pinças falhadas foram analisadas por microscópio eletrônico de varredura-MEV, sendo possível visualizar que o mecanismo de fratura predominante foi o de corrosão sob tensão. Também foi realizado ensaio em pinças sem uso (nacionais e importadas) e os resultados obtidos foram diferentes para ambas, sendo que a pinça nacional sem uso apresentou itens reprovados pela norma. Os resultados obtidos permitiram concluir que existe diferença no processo de fabricação dos materiais nacionais e importados e isso reflete na durabilidade, qualidade e segurança no uso dos instrumentais nacionais. A inspeção por MEV das pinças nacionais indicou problemas no acabamento de superfície como: pontos de corrosão, trincas e rebarbas, reprovando essas pinças segundo os critérios de aceitação das normas ASTM. Através deste estudo foi possível criar um documento para auxiliar a equipe de enfermagem na avaliação da qualidade de instrumentais cirúrgicos metálicos

Abstract: This work was developed together with the team of nursing of the HC of the Unicamp. The objective went to evaluate the failure modes in national hemostatic forceps, that already had been used for the Hospital of the Clinics of the Unicamp and that failed prematurely during the use. The evaluated parameters are related with the quality of the raw material, mechanical properties and with the manufacture process. The hemostatic forceps went evaluated according to international norms of the ASTM, between them ASTM F 899-09, ASTM F 1744-96 (2008) and ASTM F 1026-86 (2008). The fracture occurred in the hemostatic forceps went analyzed by scanning electron microscope-SEM, being possible to visualize that the mechanism of predominant failure was stress corrosion crack. Also assay in hemostatic forceps without use (national and imported) and the results had different for both, being that the national forceps without use presented item disaccord to norm. Through the results went possible to conclude there are differences in the process of manufacture of the national and imported forceps, and this reflects in the durability, quality and security in the use of the national instruments. The inspection for SEM of the national fórceps indicated problems in the surface finishing as: points of corrosion, cracks and burrs, disapproving these forceps according to criteria of acceptance of norms ASTM. Through this study went possible to create a document to assist the nursing team to evaluate the quality of the metallic surgical instruments
Subject: Instrumentos e aparelhos cirúrgicos
Aço inoxidável
Aço - Corrosão
Metais - Propriedades mecânicas
Corrosão
Language: Português
Editor: [s.n.]
Date Issue: 2009
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Lima_LonetaLauro_M.pdf23.96 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.