Title: Avaliação de revestimentos hibridos organo-inorganicos e de resinas polissiloxanas aplicadas sobre aço galvanizado e sobre camadas de Zn-Fe
Title Alternative: Organic-inorganic hybrid coatings and polysiloxanes resins for corrosion protection of galvanized steel and electroplated ZnFe steel
Author: Souza, Maria Eliziane Pires de
Advisor: Freire, Celia Marina de Alvarenga, 1960-
Freitas, Celia Marian de Alvarenga
Abstract: Resumo: As características protetoras das superfícies de aços galvanizados são geralmente intensificadas através da passivação por cromo hexavalente (Cr+6). Porém, por ser este um elemento tóxico, vários estudos visando a substituição do procedimento de cromatização vêm sendo realizados. As resinas de polissiloxanos e materiais híbridos organo-inorgânicos preparados pelo processo sol-gel, podem vir a ser um excelente substituinte ao processo de cromatização. Neste trabalho, filmes híbridos organo-inorgânico e filmes de silicone foram aplicados em aço galvanizado e em camadas de Zn-Fe. Os revestimentos foram então avaliados através de Espectroscopia de Impedância Eletroquímica. Os dados obtidos pela Espectroscopia foram modelados através de um circuito equivalente, permitindo a obtenção dos parâmetros eletroquímicos para os sistemas avaliados. Além disso, o potencial em circuito aberto, para os diferentes sistemas, foi monitorado durante processo de desgaste em sistema pino-disco em solução de NaCI 3%. Os revestimentos foram comparados em termos de resistência à corrosão e coeficiente de fricção. Os resultados mostram um bom desempenho para os revestimentos como protetores de corrosão e o comportamento destes mostraram-se dependente do tipo de revestimento metálico que foi aplicado no aço

Abstract: Chromating pre-treatments have been widely used to improve galvanized steel corrosion resistance. However, due to the high toxicity of chromate ions, chromatation pre-treatments tend to be banned and, in last years, alternative coating systems are under investigation. Recently, polysiloxanes and hybrids materiais by the sol-gel process have been extensively investigated. These materiais may be considered as promising substitutes for chromatation pre-treatments. In this work organic-inorganic hybrid materiais and silicone films have been prepared and applied on galvanized steel and on steeJ electroplated with a Zn-Fe alloy. Electrochemical Impedance Spectroscopy (EIS) was used as a technique for the evaluation of the corrosion mechanisms of the coating systems and the EIS data was fitted to an equivalent circuit from which the electrochemical parameters were obtained. Additionally, the evolution of open circuit potential, for samples, was monitored during alternative reciprocating sliding against an alumina pin in a 3% NaCl solution. The behaviour of the coatings has been compared in terms of corrosion potential and friction coefficient. Results show the protective character of the hybrid films and silicon resin films, when compared with uncovered specimens. The overall performance of the coating systems appears to be highly dependent on the type of metallic coating applied to the steel
Subject: Silicones
Compostos organosilício
Sílica gel
Polímeros de silício
Desgaste mecânico
Corrosão e anticorrosivos
Aço - Corrosão
Ligas de zinco
Aço galvanizado
Language: Português
Editor: [s.n.]
Date Issue: 2006
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Souza_MariaElizianePiresde_D.pdf6.4 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.