Title: Obtenção e caracterização de scaffolds de hidroxiapatita utilizando amido de milho como agente porogênico
Title Alternative: Obtainment and characterization of hydroxyapatite scaffolds using corn starch as porogenic agent
Author: Silva, Leonardo Antonio Januario da
Advisor: Zavaglia, Cecília Amélia de Carvalho, 1954-
Abstract: Resumo: As cerâmicas porosas à base de hidroxiapatita possuem grande potencial de aplicação na área de implantes ósseos, devido sua similaridade química com a fase mineral dos tecidos ósseos, porém possuem baixa resistência mecânica, o que causa limitações em suas aplicações. Este trabalho tem como objetivo avaliar as características estruturais de cerâmicas porosas obtidas através da adição de Hidroxiapatita (HA, sintetizada no laboratório e comercial), Amido de Milho (AM, comercial), Al2O3 (3000SG ALCOA e 5SG ALCAN) e TiO2 (VETEC), sinterizadas em diferentes temperaturas. Foram preparadas amostras de HA densa (100% HA), HA porosa (50%HA - 50% de AM e 70% HA - 30% de AM), com adição de 2,5%, 5% e 7,5% de Al2O3 e 7,5% de TiO2 na composição porosa com 30% de AM, como alternativa de comparação dos resultados. As amostras foram sinterizadas à 1250ºC, 1300ºC e 1350ºC e caracterizadas por: FRX, DRX e MEV, distribuição granulométrica e densidade pelo princípio de Arquimedes. Concluiu-se que é possível obter amostras porosas utilizando-se o amido como agente porogênico e que as adições da alumina nas porcentagens utilizadas não aumentaram a resistência mecânica das amostras conforme esperado, devido à temperatura de sinterização trabalhada ser bem inferior do que a temperatura de sinterização da alumina ao contrário das amostras com Titânia

Abstract: The porous ceramics based on hydroxyapatite have great potential for application in bone grafts due to its chemical similarity with the mineral phase of bone tissue, but have poor biomechanical properties, which cause limitations in its applications. This work aims to analyze the structural characteristics of porous ceramics obtained by addition of hydroxyapatite (HA, sintered in the laboratory and commercial), Corn Starch (CS, commercial) and Al2O3 (3000SG ALCOA and 5SG ALCAN), sintered at different temperatures. Samples were made of dense HA (100% HA), HA porous (50%HA - 50%CS and 70% HA - 30% CS) and with addition of 2,5%, 5% and 7,5% Al2O3 and 7,5% TiO2 porous composition with 30% AM, as an alternative to compare the results. The samples were sintered at 1250°C, 1300ºC and 1350°C and characterized by: XRF, XRD, SEM, particle size distribution and density by the Archimedes principle. It concluded that it is possible to obtain porous samples using starch as the agent porogênico and that the additions of alumina used in the percentages did not increase the mechanical resistance properties of samples as expected, due to the sintering temperature worked being much lower than the sintering temperature of alumina as opposed samples with titania
Subject: Hidroxiapatita
Amido de milho
Alumina
Titânio
Language: Português
Editor: [s.n.]
Citation: SILVA, Leonardo Antonio Januario da. Obtenção e caracterização de scaffolds de hidroxiapatita utilizando amido de milho como agente porogênico. 2012. 95 f. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/263513>. Acesso em: 20 ago. 2018.
Date Issue: 2012
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Silva_LeonardoAntonioJanuarioda_M.pdf2.72 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.