Title: Caracterização microestrutural e mecanica de ligas Ti-Cu para aplicações odontologicas
Title Alternative: Microstructure and mechanical characterization of Ti-Cu alloys for dental applications
Author: Andrade, Protasio Nery
Advisor: Caram Junior, Rubens, 1958-
Junior, Rubens Caram
Abstract: Resumo: Em função de características como alta razão resistência/peso, ótima biocompatibilidade, elevada resistência à corrosão e módulo de elasticidade que pode ser controlado pela adição de elementos de liga, o uso de ligas de titânio pela indústria médica e odontológica está em franco crescimento. No presente estudo, ligas do sistema Ti-Cu com teores entre 5 e 15 % em peso de cobre foram fundidas através do processo de fundição por centrifugação em moldes de cobre. A alta taxa de resfriamento imposta pelo molde empregado levou à formação de microestruturas totalmente martensítica. Em seguida, tais microestruturas foram modificadas através tratamentos térmicos, levando a estruturas mais estáveis. A caracterização das amostras obtidas envolveu análise microestrutural através de microscopia óptica e eletrônica de varredura, difração de raios-X, ensaios mecânicos. Os resultados obtidos indicam que as altas taxas de resfriamento envolvidas promoveram a formação da estrutura metaestável _'. O aumento da concentração de cobre levou ao aumento na dureza promovida pela formação do intermetálico Ti2Cu. O Ti2Cu apresentou módulo de elasticidade menor do que a fase _. A fratura dos corpos de prova teve caráter dúctil e é intensamente afetada pela presença de porosidade

Abstract: Due to characteristics like high strength-to-weight ratio, high biocompatibility, enhanced corrosion resistance and the possibility of controlling elastic behavior by proper addition of alloying elements, the use of titanium by medical and dental industries is continuously growing. In this work, Ti-Cu alloys with a Cu content varying from 5% to 15 wt% were prepared by arc melting and cast in copper molds. The high cooling rate imposed by copper mold led to the formation of a completely martensitic structure. Following, the microstructure of these samples were modified by applying proper heat treatments, leading to more stable microstructures. The samples characterization includes microstructure analyzes through optical and scanning electron microscopy, X-ray diffraction method and mechanical tests. The results obtained suggest that application of high cooling rates resulted in the formation of a'metastable phase. As Cu content was increased, hardness also increased due to Ti2Cu intermetallic compound precipitation. The Ti2Cu compound was found to present lower elastic modulus than the modulus of a phase. Finally, it was found that the heat treated samples presented high ductility and their mechanical behavior is affected by porosities
Subject: Ligas de titânio
Fundição de precisão
Prótese dentária
Ligas de titânio - Tratamento térmico
Language: Português
Editor: [s.n.]
Citation: ANDRADE, Protasio Nery. Caracterização microestrutural e mecanica de ligas Ti-Cu para aplicações odontologicas. 2006. p. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/263193>. Acesso em: 8 ago. 2018.
Date Issue: 2006
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Andrade_ProtasioNery_M.pdf8.96 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.