Title: Transformações de fase e microestruturas de ligas no sistema Nb-Cr-Al
Title Alternative: Phase transformations and microstructures of alloys in the Nb-Cr-Al system
Author: Souza, Sandra Andreia Stwart de Araujo
Advisor: Caram Junior, Rubens, 1958-
Junior, Rubens Caram
Abstract: Resumo: O interesse por novos materiais estruturais para aplicação em temperaturas elevadas tem gerado um grande volume de publicações a respeito de ligas à base de metais refratários contendo composto intermetálicos. A baixa tenacidade à fratura dessas ligas leva à busca por combinações de fases que garantam alta resistência e ductilidade. Nesse caso, a melhor opção tem sido os materiais compósitos, principalmente os do tipo in situ, onde a formação das fases se processa dentro de um equilíbrio termodinâmico, como ocorre em uma transformação eutética. Em termos de aplicações em altas temperaturas, o sistema Nb-Cr-Al tem se mostrado como promissor por apresentar reações eutéticas que resultam na formação de compostos intermetálicos. O presentetrabalho trata da obtenção, processamento e caracterização de ligas do sistema Nb-Cr-Al. Amostras desse sistema foram produzidas em forno a arco voltaico. Suas microestruturas foram analisadas no estado bruto de fusão e após tratamentos térmicos. Foi realizada uma intensa investigação a respeito do eutético observado, através da solidificação direcional em fomo tipo Bridgman sob várias taxas de crescimento. Na caracterização das ligas foi empregada microscopia óptica e eletrônica de varredura, difração de raios-x e análise térmica diferencial. Os resultados indicam que a transformação eutética ocorre em temperatura próxima a 1.347,9°Ccom a formação das fases Ah(Nb,Cr) e Cr(Al,Nb). A fase dúctil do eutético, Cr(Al,Nb), durante o decréscimo da temperatura sofre transformação polimórfica (~892,3°C) para Al(Nb)Cr2, seguida de decomposição eutetóide Cr(Al,Nb) - Al(Nb)Cr2+Al8Cr5. Sua morfologia apresenta-se como regular complexa com composição eutética de 49,3Al-39,7Cr-ll,ONb (% at.). Pelo estudo das transformações de fases e microestruturas das amostras obtidas foi possível fazer um levantamento da superfície liquidus na região próxima ao ponto eutético

Abstract: The interest for new structural materiaIs for application in high temperature has created a large volume of publications concerning refractory metal-based alloys that contain intermetallic compounds. The low fracture toughness of those alloys leads to the search of combination of phases that guarantees high strength and ductility. In such a case, the best choice has been the use of composite materiaIs, mainly the in-situ composites, where the formation of the solid phases processes under thermodynamic equilibrium, as in the eutectic transformations. In terms of high temperature applications, the Nb-Cr-AI system is very promising, as it presents several eutectic reactions, that result in the formation of intermetallic compounds. This work deals with obtaining, processing and characterization of alloys in the Nb-Cr-AI system. Samples in such a system were obtained in an arc furnace. Their microstructures were analysed in as-cast condition and after heat-treatments. An investigation conceming eutectic microstructure was carried out through the application of directional solidification using Bridgman equipment at several growth rates. Characterization of samples was performed by employing optical and scanning electron microscopy, X-ray diffraction and thermal analysis techniques. The results obtained indicated the eutectic transformation temperature is near to 1,347.9°C with formation of Ab(Nb,Cr) and Cr(AI,Nb) phases. The ductile phase of eutectic, Cr(AI,Nb) phase, during the decrease of temperature undergoes a polymorphic transformation (-892.3°C) forming the AI(Nb)Cr2 compound, followed by an eutectoid decomposition Cr(AI,Nb)~ AI(Nb)Cr2+AIgCrs.The eutectic microstructure presents is of regular complex type and the eutectic composition is near 49.3%AI- 39.7%Cr-l1.0%Nb (at.%). Through studying the phase transformations and microstructures of the samples obtained, it was possible to establish the liquidus surface in the region around the eutectic point
Subject: Materiais
Ligas euteticas
Compostos intermetálicos
Solidificação
Language: Português
Editor: [s.n.]
Date Issue: 2005
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Souza_SandraAndreiaStwartdeAraujo_M.pdf7.23 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.