Title: Avaliação de processos de deformação plástica, recristalização e envelhecimento de ligas Ti-Nb
Title Alternative: Evoluation of plastic deformation, recrystallization and aging processes of Ti-Nb alloys
Author: Lopes, Juliana Feletto Silveira Costa
Advisor: Caram Junior, Rubens, 1958-
Junior, Rubens Caram
Abstract: Resumo: O controle da composição e a aplicação de tratamentos termo-mecânicos de ligas de titânio tipo ß permite otimizar microestruturas em relação à aplicações como biomaterial ortopédico. Amostras das ligas Ti-30Nb e Ti-35Nb (% em peso) foram preparadas em forno de fusão a arco voltaico, homogeneizadas a 1000 oC por 8 h e resfriadas em água, obtendo-se microestrutura formada pela fase ß combinada com a fase martensita ortorrômbica. Na seqüência, essas amostras seguiram duas rotas de processamento: uma envolvendo deformação plástica, seguida por tratamento térmico de envelhecimento e outra envolvendo deformação plástica seguida por recristalização e envelhecimento. Os resultados mostram que a microestrutura das amostras homogeneizadas é composta por grãos grosseiros, com aproximadamente 3 mm de diâmetro. A caracterização microestrutural das amostras deformadas mostra a presença de heterogeneidades de deformação, tais como bandas de cisalhamento. O tratamento térmico de envelhecimento foi realizado com o objetivo de estudar a precipitação das fases ? e a. A aplicação de tais tratamentos térmicos permitiu a otimização das microestruturas e do comportamento mecânico das ligas estudadas.

Abstract: This work deals with studies of titanium alloys used in orthopedic implants. The control of composition and application of thermo-mechanical treatments allows one to optimize microstructures regarding applications as orthopedic biomaterial. Samples of Ti-30Nb and Ti-35Nb (wt %) alloys were obtained by arc melting, solution heat treated at 1000 ºC for 8 hours and water quenched, resulting in microstructures composed by ß phase and orthorhombic martensite phase. Following, samples followed two processing routes: one involving plastic deformation followed by aging heat treatment and another involving plastic deformation followed by recrystallization and aging heat treatment. In the solution condition, the sample microstructures were formed by coarse grains, with approximate diameter of 3 mm. Microstructural characterization of deformed samples shows the presence of deformation heterogeneity, as shear bands. Aging heat treatment was accomplished with the aim of studying precipitation of ? and a phases. Application of the mentioned heat treatments allowed optimization of microstructure and mechanical behavior of the studied alloys.
Subject: Deformação plástica
Recristalização
Envelhecimento
Ligas de titânio
Language: Português
Editor: [s.n.]
Date Issue: 2010
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Lopes_JulianaFelettoSilveiraCosta_M.pdf9.41 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.