Title: Transformações de fases e relação entre microestrutura e propriedades mecânicas de ligas Ti-Nb-Fe para aplicações biomédicas : concepção de implantes ortopédicos com rigidez gradual
Title Alternative: Phase transformation and relationship between microstructure and mechanical properties of Ti-Nb-Fe for biomedical applications : design of orthopedic implants with graded stiffness
Author: Lopes, Éder Sócrates Najar, 1982-
Advisor: Caram Junior, Rubens, 1958-
Junior, Rubens Caram
Abstract: Resumo: Ligas de Ti do tipo ? metaestável exibem comportamento singular no tocante à possibilidade de manipulação de seu comportamento mecânico. Nessas ligas, a rigidez pode ser alterada por meio do controle das fases presentes, o que permite que esses materiais sejam incluídos no seleto grupo dos materiais com gradientes funcionais (functionally graded materials - FGM). Neste trabalho, objetivou-se projetar, produzir, processar, caracterizar e aplicar ligas Ti-Nb com adições do elemento ? estabilizador de baixo custo Fe. As ligas foram produzidas por fusão a arco voltaico e submetidas a diversas condições de tratamento térmico, incluindo solubilização acima da temperatura ?-transus, resfriamento rápido até a temperatura ambiente e tratamentos térmicos de envelhecimento entre 260 °C e 400 °C. A caracterização envolveu calorimetria diferencial de varredura, difração de raios-X e dureza Vickers em alta temperatura, análises metalográficas e de módulo de elasticidade por técnicas acústicas, ensaios de tração e mapeamento de rigidez por meio de nanoindentação. Os resultados obtidos mostram a retenção completa da fase ? para a liga Ti-30Nb-3Fe solubilizada e resfriada rapidamente e permitem também, compreender a decomposição da fase martensita ?" e a nucleação das fases ? e ?. A adição do elemento Fe tornou a cinética de transformação de fases bem mais lenta, propiciando, sob algumas condições, a supressão da fase ?, que é conhecida por aumentar a dureza em detrimento da ductilidade. Tais resultados foram utilizados no estabelecimento de condições ideais de processamento que permitem obter componentes ortopédicos com rigidez gradual. Finalmente, o conhecimento adquiro foi usado na fabricação de placas e parafusos de osteossíntese a partir da liga Ti-30Nb-3Fe com gradientes de funcionalidade

Abstract: Metastable ? Ti alloys exhibit singular behavior regarding the possibility of manipulating their mechanical behavior. In these alloys, the stiffness can be changed by controlling phases, which allows these materials to be included in the select group of functionally graded materials (FGM). This study aimed to design, produce, process, characterize and apply Ti-Nb alloys with addition of Fe, an inexpensive ? stabilizing element. These alloys were produced by arc melting and subjected to different heat treatment conditions, including solution above the ?- transus temperature, quenching to room temperature and aging heat treatments between 260 °C and 400 °C. Characterization involved differential scanning calorimetry, X-ray diffraction and Vickers hardness at high temperature, metallographic analyzes, elastic modulus by acoustic techniques, tensile test and stiffness mapping via nanoindentation. The results obtained show complete retention of the ? phase in the Ti-30Nb-3Fe alloy after solution in the ? field and rapid cooling to room temperature and also allow understanding martensite ?" decomposition and nucleation of the ? and ? phases. It was found that Fe additions make the phase transformation kinetics much slower, providing, for some conditions, suppression of the ? phase precipitation, which is known to increase the hardness at the expense of ductility. These results were used to establish optimal processing conditions, resulting in orthopedic component with graded stiffness. Finally, the knowledge acquired was used in the manufacturing of osteosynthesis plates and screws with functionality graded from the Ti-30Nb-3Fe
Subject: Ligas de titânio
Testes de dureza
Ligas de titânio - Tratamento térmico
Ligas de titanio - Propriedades mecânicas
Implantes ortopédicos
Language: Português
Editor: [s.n.]
Citation: LOPES, Éder Sócrates Najar. Transformações de fases e relação entre microestrutura e propriedades mecânicas de ligas Ti-Nb-Fe para aplicações biomédicas: concepção de implantes ortopédicos com rigidez gradual. 2013. 138 p. Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/263150>. Acesso em: 23 ago. 2018.
Date Issue: 2013
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Lopes_EderSocratesNajar_D.pdf9.06 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.