dc.contributor.CRUESPUNIVERSIDADE ESTADUAL DE CAMPINASpt_BR
dc.identifier(Broch.)pt_BR
dc.descriptionOrientador: Ana Maria Martinez Nazarpt_BR
dc.descriptionDissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanicapt_BR
dc.format.extent138f. : il.pt_BR
dc.format.mimetypeapplication/pdfpt_BR
dc.languagePortuguêspt_BR
dc.typeDISSERTAÇÃOpt_BR
dc.titleEfeito do tratamento termomecnanico na microssegregação de um aço maraging grau 1900MPapt_BR
dc.contributor.authorRocha, Claudio Jose dapt_BR
dc.contributor.advisorMartinez Nazar, Ana Maria, 1948-pt_BR
dc.contributor.advisorNazar, Ana Maria Martinezpt_BR
dc.contributor.institutionUniversidade Estadual de Campinas. Faculdade de Engenharia Mecânicapt_BR
dc.contributor.nameofprogramPrograma de Pós-Graduação em Engenharia Mecânicapt_BR
dc.subjectAço de alta resistenciapt_BR
dc.subjectAço - Tratamento térmicopt_BR
dc.subjectAço - Metalografiapt_BR
dc.subjectAço - Fundiçãopt_BR
dc.subjectConformação de metaispt_BR
dc.description.abstractResumo: Um dos problemas de processamento dos aços Maraging diz respeito ao bandeamento da microestrutura que prejudica o comportamento mecânico do material. O bandeamento é normalmente decorrente da segregação interdendrítica que persiste em algum grau após os tratamentos termomecânicos. O presente trabalho aborda este problema apresentando um estudo do efeito de tratamentos termomecânicos no grau de microssegregação de um aço Maragin grau 1900MPa, refundido pelo processo eletroescória. Em relação ao processo de refusão, verificou-se que embora não tenham ocorrido macrossegregações, o material apresentou uma microssegregação significativa. A análise do lingote evidenciou também grandes variações nos espaçamentos dendríticos, acarretando variações nos graus de microssegregação e na distribuição do soluto microssegregado. Os resultados dos tratamentos térmicos de homogeneização indicaram que a cinética de homogeneização é pouco afetada pelas diferenças de estrutura de solidificação. O comportamento do material apresentou uma cinética de homogeneização caracterizada por dois estágios: uma taxa de homogeneização mais elevada para tempos de até 6 horas, sendo consideravelmente menor a partir deste tempo. A utilização de modelos matemáticos mostraram, para o caso do titânio, que o comportamento segue o modelo bidimensional com distribuição parabólica. Isto indica que tal comportamento está associado a existência de altos gradientes de concentração de soluto junto aos pontos de máxima concentração e a diferentes espaçamentos entre esses pontos de máxima e os pontos de mínima. Quanto a conformação mecânica, verificou-se que o processo de laminação a quente utilizado provocou uma homogeneização equivalente a 6 horas de tratamento térmico, indicando claramente sua contribuição no processo de homogeneizaçãopt
dc.description.abstractAbstract: One of the main problems in the production of Maraging steels comes from banded structures. This banding is originated by interdendritic segregation during ingot solidification and persists in some degree after thermomechanicaltreatments. In this context, the present work studies the effect of thermomechanical treatments on the microsegregation of an electroslag remelting Maraging steel (1900MPa). Preliminary analysis have not shown any macrosegregation in the material, however, a significant interdendritic microsegregation of alloying elements have been observed. The ingot presents different structures between top and bottom, but homogenization rate is not significantlyaffected by this heterogeneity. The microsegregation curves show that the initial rate of homogenization is very rapid; the rate significantly decreases after approximately 6 hours until complete homogenization. For better understanding this behavior, mathematical models have been applied to titanium. A good agreement can be observed with the parabolic distribution bidimensionalmode!. This result allows to associate the behavior of the homogenization rate to a high solute concentration gradient at the points of maxima, and to different distances between the maxima and minima points. Related to the mechanical treatments, it has been verified that the hot rolling has an effect equivalent to a 6 hours homogenization treatmenten
dc.publisher[s.n.]pt_BR
dc.date.issued1995pt_BR
dc.identifier.citationROCHA, Claudio Jose da. Efeito do tratamento termomecnanico na microssegregação de um aço maraging grau 1900MPa. 1995. 138f. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/263039>. Acesso em: 20 jul. 2018.pt_BR
dc.description.degreelevelMestradopt_BR
dc.description.degreedisciplineMateriais e Processos de Fabricaçãopt_BR
dc.description.degreenameMestre em Engenharia Mecânicapt_BR
dc.contributor.committeepersonalnameGarcia, Amauript_BR
dc.contributor.committeepersonalnameMonteiro, Waldemar Alfredopt_BR
dc.date.defense1995-09-29T00:00:00Zpt_BR
dc.date.available2018-07-20T16:29:37Z-
dc.date.accessioned2018-07-20T16:29:37Z-
dc.description.provenanceMade available in DSpace on 2018-07-20T16:29:37Z (GMT). No. of bitstreams: 1 Rocha_ClaudioJoseda_M.pdf: 34139604 bytes, checksum: d5162c12e520940a51415f7714556a94 (MD5) Previous issue date: 1995en
dc.identifier.urihttp://repositorio.unicamp.br/jspui/handle/REPOSIP/263039-
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Rocha_ClaudioJoseda_M.pdf33.34 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.