Title: Síntese de carbonos cerâmicos mesoporosos para aplicação como eletrodos em células a combustível a metanol direto
Title Alternative: Synthesis of the novel mesoporous carbon ceramics for application on direct fuel cell electrodes
Author: Gallo, Jean Marcel Ribeiro
Advisor: Pastore, Heloise de Oliveira, 1962-
Abstract: Resumo: Esse trabalho teve como objetivo a aplicação de peneiras moleculares mesoporosas de sílica como suporte para metal em aplicações em eletrodos na Célula a combustível a metanol direto (DMFC). As peneiras moleculares mais importantes, MCM-41, MCM-48 e SBA-15, foram escolhidas. Em um primeiro momento a reprodutibilidade das sínteses foi verificada. Como pesquisa lateral foi estudada a acidez de superfície da SBA-15 contendo alumínio obtida por síntese direta. Além disso, foi desenvolvida a primeira síntese direta para a [Al]-SBA-15 Sílica é um isolante elétrico e, portanto, não pode ser utilizada como um eletrodo, deste modo, uma nova família de compósitos chamada Carbonos Cerâmicos Mesoporosos (MCC) foi preparada pela adição de grafite comercial na síntese das sílicas mesoporosas (MCM-41, MCM-48 ou SBA-15). A grafite não influenciou na formação da mesofase de sílica, de qualquer maneira, a MCC-MCM-41 e a MCC-MCM-48 cresceram na superfície da grafite. As MCCs preparadas com razão em massa sílica/carbono de 1/1 e 1/1.25 apresentaram condutividades elétricas similares enquanto MCCs com menos quantidade de carbono se mostraram isolantes elétricos. As MCCs(1/1) modificadas com 20 % em massa de paládio foram usadas na DMFC chegando no máximo a desempenhos 10 vezes menores que o do sistema usando o suporte comercia Vulcan XC-72R. Esse comportamento foi atribuida a menos condutividade elétrica dos MCCs. Para aumentar a condutividade elétrica dos MCCs(1/1), o agente direcionador orgânico usado na síntese da fase silícica foi carbononizado ( ao invez de calcinado, como feito anteriormente) Alternativamente, os MCCs foram sintetizados com uma razão em massa sílica/carbono de 1/3. Os testes dos MCCs contendo 20 % em massa de platina no cátodo da DMFC mostraram melhores resultados para a MCC-SBA-15(1/3) e a MCC-MCM-48(1/1) pirolisada. Por outro lado, o despenho do sistema usando o suporte Vulcan-XC-72R foi o dobro. Modificados com 60 % em massa da liga PtRu, o MCC-SBA-15(1/3) e o MCC-MCM-48(1/1) pirolisado foram aplicados no ânodo da DMFC, alcançando desempenhos 20 e 40 % maiores que a Vulcan XC-72R.

Abstract: The present work aimed at using mesoporous silica as metal support for Direct Methanol Fuel Cell (DMFC) electrodes. The most important mesoporous silica, MCM-41, MCM-48 and SBA-15, were chosen. In a first moment their synthesis were verified with respect to the reproductibility. As side results, the surface acidity of aluminum containing SBA-15 obtained by direct synthesis was also studied and it is also reported the first [Al]-SBA-16 obtained by direct synthesis was reported. Silica is electrically insulating and thus cannot be used directly in a cell electrode, thus it was reported here the preparation of the novel composite named Mesoporous Carbon Ceramics (MCC) obtained by the addition of commercial graphite into the mesoporous silica synthesis (MCM-41, MCM-48 or SBA-15). The graphite did not influence in the formation of the silica mesophase, however, MCC-MCM-41 and MCC-MCM-48 grow on the graphite surface. The MCCs prepared with silica/carbon weight ratio of 1/1 and 1/1.25 presented similar electrical conductivities while lower carbon loading MCCs were found insulating. The MCCs(1/1) modified with 20 wt % of platinum were used on Direct Methanol Fuel Cell electrodes (DMFC) reaching performances more ten 10 times lower than that of a system using the commercial metal support Vulcan XC-72R, probably due to their lower electrical conductivity. To increase the electrical conductivity of the MCCs(1/1), the surfactant used to synthesize the silica phase was carbonized (instead of calcined as done for the previous materials). Alternatively, MCCs was synthesized with silica/carbon weight ratio of 1/3. The test of 20 wt. % platinum-containing MCCs on the cathode of the DMFC showed that the best results were obtained for the MCC-SBA-15(1/3) and for the template-pyrolysed MCC-MCM-48(1/1), however, the performance was approximately half of that of the system using Vulcan-XC-72R. When modified with 60 wt % of PtRu alloy, MCC-SBA-15(1/3) and to the template-pyrolysed MCC-MCM-48(1/1) and applied on the DMFC anode, the performances at 343 K was ca. 20 and 40 % higher that that obtained for the system using Vulcan XC-72R.
Subject: Peneira molecular mesoporosa
Carbono cerâmico mesoporoso
Células a combustível
Language: Português
Editor: [s.n.]
Date Issue: 2010
Appears in Collections:IQ - Tese e Dissertação

Files in This Item:
File SizeFormat 
Gallo_JeanMarcelRibeiro_D.pdf4.67 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.