Please use this identifier to cite or link to this item: http://repositorio.unicamp.br/jspui/handle/REPOSIP/248657
Full metadata record
DC FieldValueLanguage
dc.contributor.CRUESPUNIVERSIDADE ESTADUAL DE CAMPINASpt_BR
dc.identifier(Broch.)pt_BR
dc.descriptionOrientador: Marco-Aurelio De Paolipt_BR
dc.descriptionTese (Doutorado) - Universidade Estadual de Campinas, Instituto de Quimicapt_BR
dc.format.extent77p. : il.pt_BR
dc.format.mimetypeapplication/pdfpt_BR
dc.languagePortuguêspt_BR
dc.typeTESEpt_BR
dc.titleEfeito compatibilizante do polietileno de alta densidade pos-consumo em blendas com poliamida-6pt_BR
dc.title.alternativeCompatibilizing effect of post-consumer high density polyethylene in blends with polyamide-6pt_BR
dc.contributor.authorVallim, Marcio Robertopt_BR
dc.contributor.advisorDe Paoli, Marco-Aurelio, 1949-pt_BR
dc.contributor.advisorPaoli, Marco-Aurelio Dept_BR
dc.contributor.institutionUniversidade Estadual de Campinas. Instituto de Químicapt_BR
dc.contributor.nameofprogramPrograma de Pós-Graduação em Ciênciaspt_BR
dc.subjectBlendaspt_BR
dc.subjectPoliamida-6pt_BR
dc.subjectPolietileno de alta densidade pos-consumopt_BR
dc.subject.otherlanguageBlendaen
dc.subject.otherlanguagePolyamide-6en
dc.subject.otherlanguagePost-consumer high densityen
dc.description.abstractResumo: Blendas poliméricas, geralmente, são imiscíveis, devido à baixa entropia de mistura, e incompatíveis, devido à ausência de interações intermoleculares entre as fases, resultando em propriedades mecânicas inadequadas. O uso de copolímeros bloco ou de enxertia é uma forma de promover a adesão entre as fases e reduzir a tensão interfacial. Neste trabalho foi estudado o efeito da substituição do polietileno de alta densidade pelo polietileno de alta densidade pós-consumo (PEpc) em blendas com a poliamida-6 (PA6), a fim de verificar se o PEpc age como um compatibilizante. As blendas foram preparadas nas composições de 25, 50 e 75 % em massa de PA6, usando extrusora mono- ou dupla-rosca com perfil de temperatura de 230 a 255 °C a 102 rpm. Os ¿espaguetes¿ foram resfriados em banho d¿água, picotados e, posteriormente, injetados com o mesmo perfil de temperatura e os corpos de prova foram resfriados no molde a 20 °C por 20 s. A microscopia eletrônica de varredura das fraturas criogênicas revelou uma redução no diâmetro médio da fase dispersa das blendas contendo PEpc e os ensaios mecânicos mostraram que ocorreram aumentos da tensão na força máxima, do módulo de flexão e da resistência ao impacto. Por outro lado, a estabilidade térmica (temperatura inicial de degradação e temperatura de máxima velocidade de degradação) e as propriedades térmicas (entalpia de fusão e temperaturas de fusão e de cristalização) não sofreram alteração significativa. A hipótese da interação entre o PEpc e a PA6 foi reforçada pela aplicação dos dados de viscosidade aparente dos homopolímeros ao modelo empírico de Wu, pela formação de suspensão coloidal estável durante o teste de Molau e pelo aumento do módulo de armazenamento, verificado pela análise dinâmico-mecânica. Conclui-se que os grupos polares resultantes da degradação da cadeia do PEpc interagem quimicamente com a PA6, desempenhando um efeito compatibilizante, o qual, resulta em redução da tensão interfacial e aumento da adesão entre as fases da blendapt
dc.description.abstractAbstract: Polymer blends are commonly immiscible, due to the small entropy of mixture, and incompatible, caused by the absence of intermolecular interactions between the phases, resulting in poor mechanical properties. The addition of block or graft copolymers is an alternative way to improve the adhesion at the interface and to reduce the interfacial tension. In this work, high density polyethylene or post-consumer high density polyethylene (PEpc) were blended with polyamide-6 (PA6) to verify the supposed compatibilizing effect of PEpc. Blends were prepared with 25, 50 and 75 wt % of PA6, by using a single- or a twin-screw extruder, at a temperature range from 230 to 255 °C and 102 rpm rotational speed. Test specimens were obtained by injection molding at the same conditions of the extrusion. The temperature and the period of molding were 20 °C and 20 s, respectively. The scanning electron microscopy showed a reduction in the size domains of the disperse phase when PEpc was used, in addition the tensile strength, the flexural modulus and the impact strength were improved. The thermal stability (onset degradation temperature and maximum degradation temperature) and the thermal properties (melting and crystallization temperatures and fusion enthalpy) were unaffected by PEpc. The hypothesis of the compatibilizing effect of PEpc was supported by the simulation for domain size using the Wu equation, by the formation of a colloidal suspension in the Molau test and by the increase of storage modulus in the dynamic-mechanical analysis. It could be concluded that PEpc acts as a compatibilizer in PA6 blends, decreasing the interfacial tension and improving the phase adhesion, by the interaction of the amine end groups of PA6 and the polar groups of PEpc, generated from its environmental and thermomechanical degradationen
dc.publisher[s.n.]pt_BR
dc.date.issued2007pt_BR
dc.identifier.citationVALLIM, Marcio Roberto. Efeito compatibilizante do polietileno de alta densidade pos-consumo em blendas com poliamida-6. 2007. 77p. Tese (Doutorado) - Universidade Estadual de Campinas, Instituto de Quimica, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/248657>. Acesso em: 9 ago. 2018.pt_BR
dc.description.degreelevelDoutoradopt_BR
dc.description.degreedisciplineFísico-Químicapt_BR
dc.description.degreenameDoutor em Ciênciaspt_BR
dc.contributor.committeepersonalnameJunior, Sebastião Vicente Canevarolopt_BR
dc.contributor.committeepersonalnameWiebeck, Heliopt_BR
dc.contributor.committeepersonalnameGonçalves, Maria do Carmopt_BR
dc.contributor.committeepersonalnameFelisberti, Maria Isabelpt_BR
dc.date.defense2007-12-19T00:00:00Zpt_BR
dc.date.available2018-08-10T02:43:20Z-
dc.date.accessioned2018-08-10T02:43:20Z-
dc.description.provenanceMade available in DSpace on 2018-08-10T02:43:20Z (GMT). No. of bitstreams: 1 Vallim_MarcioRoberto_D.pdf: 1739419 bytes, checksum: ccd0a1bb0b8347580c6c5296c09efe30 (MD5) Previous issue date: 2007en
dc.identifier.urihttp://repositorio.unicamp.br/jspui/handle/REPOSIP/248657-
Appears in Collections:IQ - Tese e Dissertação

Files in This Item:
File SizeFormat 
Vallim_MarcioRoberto_D.pdf1.7 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.