Title: Effects Of Different Photo-polymerization Protocols On Resin-dentine μtbs, Mechanical Properties And Cross-link Density Of A Nano-filled Resin Composite.
Author: Feitosa, Victor Pinheiro
Fugolin, Ana Paula Piovezan
Correr, Américo Bortolazzo
Correr-Sobrinho, Lourenço
Consani, Simonides
Watson, Timothy F
Sinhoreti, Mário Alexandre Coelho
Sauro, Salvatore
Abstract: To evaluate the effects of four different light-curing protocols on the microtensile bond strength (μTBS), ultimate tensile strength (UTS), Knoop micro-hardness (KH) and cross-link density (CLD) of a nano-filled resin composite. Filtek Supreme XT (3M-ESPE) was used for the entire experiments following four light-curing approaches: ST, standard irradiance; HI, high irradiance; PD, pulse delay; SS, soft start. The specimens were submitted to different storage periods (24h or 6 months), cut into match-sticks and subsequently submitted to μTBS testing. Hourglass specimens were also prepared for UTS and KH. Cylindrical specimens were prepared for the CLD evaluation after absolute ethanol challenge. The results were statistically analyzed with a two-way ANOVA and Tukey's test (α=0.05). For UTS and KH, continuous irradiance (PD and SS) induced statistically higher results (p<0.05) both after 24h and 6 months of water storage compared to ST and HI groups. However, a drop in UTS and KH was obtained after 6 months in all groups. The μTBS was not affected by the different light-curing approaches and, no statistical differences (p>0.05) were observed between 24h and 6 months storage. The CLD evaluation showed a statistical drop in KH after 24h of ethanol storage for PD and SS (step-curing protocols) compared to those attained in continuous mode (ST and HI). The soft-start mode may improve the UTS and KH of nano-filled resin composites without compromising the resin-dentine μTBS. However, both the step-curing protocols may reduce the cross-link density of the composite polymeric network. High irradiances photo-polymerization may be adequate for direct aesthetic restorations such as veneers and onlays. Meanwhile, the soft start protocol would seem more appropriate for the photo-polymerization of high c-factors class I and II restorations.
Subject: Adhesiveness
Composite Resins
Dental Bonding
Dental Materials
Dentin
Ethanol
Hardness
Humans
Light-curing Of Dental Adhesives
Materials Testing
Mechanical Phenomena
Microscopy, Electron, Scanning
Nanocomposites
Polymerization
Radiation Dosage
Solvents
Stress, Mechanical
Surface Properties
Tensile Strength
Time Factors
Water
Rights: fechado
Identifier DOI: 10.1016/j.jdent.2012.05.014
Address: http://www.ncbi.nlm.nih.gov/pubmed/22687576
Date Issue: 2012
Appears in Collections:Artigos e Materiais de Revistas Científicas - Unicamp

Files in This Item:
File SizeFormat 
pmed_22687576.pdf620.87 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.