Title: Assessment Of The Polymerization Contraction Stress Of Composites Photoactivated By Halogen Light And Light-emitting Diode.
Author: da Fonseca Roberti Garcia, L
Zago Naves, L
Correr-Sobrinho, L
Consani, S
Abstract: The aim of this study was to compare the polymerization contraction stress of composites photoactivated by two light sources: quartz tungsten halogen light (QTH) and light emitting diode (LED). Glass rods were fabricated (5.0 mm X 5.0 cm) and one of the surfaces was air abraded with aluminum oxide. An adhesive was applied to this surface and photoactivated by LED. The glass rods were assembled to a Universal Testing machine (Instron - 5565) and the composite were applied to the lower rod using a manual instrument. The upper rod was placed closer, at 2 mm, and an extensometer was attached to the rods. The twenty composites were polymerized by either by QTH (N.=10) or LED (N.=10). Polymerization was carried out using two apparatuses positioned in opposite sides, which were simultaneously activated for 30 seconds. Contraction stress was analyzed twice: shortly after polymerization (t30s) and 30 minutes later (t30min). The contraction stress for all composites was higher at t30min than at t30s, regardless of the activation source. Z100 showed lower contraction stress values (P<0.05) compared to the other composites. Regarding to Charisma and TPH, the photoactivation source had no influence on contraction stress, except for Z100 at t30min. It was concluded that composite composition is the factor that most influence the polymerization contraction stress.
Subject: Composite Resins
Curing Lights, Dental
In Vitro Techniques
Light
Light-curing Of Dental Adhesives
Materials Testing
Photochemical Processes
Resin Cements
Silicon Dioxide
Stress, Mechanical
Zirconium
Rights: fechado
Identifier DOI: 
Address: http://www.ncbi.nlm.nih.gov/pubmed/20027128
Date Issue: -1-Uns- -1
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.