Title: A Morphological And Tensile Bond Strength Evaluation Of An Unfilled Adhesive With Low-viscosity Composites And A Filled Adhesive In One And Two Coats.
Author: Montes, M A
de Goes, M F
da Cunha, M R
Soares, A B
Abstract: The purpose of this study was to measure the tensile bond strength (TBS) testing of resin composite to dentin of three low-viscosity composites, in association with an unfilled adhesive, and a filled adhesive one and two coats respectively, and to evaluate and compare the SEM morphological observations. The labial surface of 120 bovine lower incisors were ground to obtain a flat dentin surface allowing demarcation of a 4 mm diameter area with adhesive tape. The teeth were randomly divided in six groups of 20 each. The dentin of each ground surface was etched with 35% H(3)PO(4) for 15s, followed by application of the respective adhesive: Single Bond (SB) for Groups 1, 2, 3 and 6; Optibond Solo (OS) for Groups 4 and 5. In Groups 1 and 4, a resin composite rod with a wire loop was luted directly to the adhesive surface with Z100. Group 2 received an intermediate layer of Flow It (FI) composite; Group 3 received an intermediate layer of Protect Liner F (PLF) composite; Group 5 received a second coat of OS; and Group 6 received an intermediate layer of an experimental low-viscosity composite (EM). A resin composite rod was luted to the surface of each specimen with Z100 resin composite. All specimens were stored in distilled water at 37 degrees C for 24h prior to TBS testing. Each specimen was inspected by SEM and classified according to adhesive or cohesive failure mode. One specimen of each group was cut longitudinally, polished and prepared for SEM observation. The TBS values were: Group 1 (7.86MPa+/-2.28), Group 2 (7.62MPa+/-1.85), Group 3 (7.60MPa+/-2.14), Group 4 (7.96MPa+/-2.36), Group 5 (7.50MPa+/-2.70) and Group 6 (7.18MPa+/-2.40). No significant statistical differences were observed among the groups. However, the analyses of the failure mode presented a considerable variation. The use of a filled adhesive or an unfilled adhesive along with a low-viscosity composite as an intermediate layer may provide a stress absorbing layer, whereby improving the preservation of the bonded interface area.
Subject: Adhesives
Analysis Of Variance
Animals
Bisphenol A-glycidyl Methacrylate
Cattle
Composite Resins
Dental Bonding
Dental Marginal Adaptation
Dental Restoration Failure
Dentin Permeability
Dentin-bonding Agents
Elasticity
Materials Testing
Methacrylates
Microscopy, Electron, Scanning
Resin Cements
Silicon Dioxide
Surface Properties
Tensile Strength
Viscosity
Zirconium
Rights: fechado
Identifier DOI: 
Address: http://www.ncbi.nlm.nih.gov/pubmed/11520593
Date Issue: 2001
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File SizeFormat 
pmed_11520593.pdf634.78 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.