Title: Mechanical And Water Vapor Permeability Properties Of Biodegradables Films Based On Methylcellulose, Glucomannan, Pectin And Gelatin [propriedades Mecânicas E De Permeabilidade Ao Vapor De água De Filmes Biodegradáveis à Base De Metilcelulose, Glucomanana, Pectina E Gelatina]
Author: Chambi H.N.M.
Grosso C.R.F.
Abstract: Mimic biological structures such as the cell wall of plant tissues may be an alternative to obtain biodegradable films with improved mechanical and water vapor barrier properties. This study aims to evaluate the mechanical properties and water vapor permeability (WVP) of films produced by using the solvent-casting technique from blended methylcellulose, glucomannan, pectin and gelatin. First, films from polysaccharides at pH 4 were produced. The film with the best mechanical performance (tensile strength = 72.63 MPa; elongation = 9.85%) was obtained from methylcellulose-glucomannan-pectin at ratio 1:4:1, respectively. Then, gelatin was added to this polysaccharide blend and the pH was adjusted to 4, 5 and 6. Results showed significant improvement in WVP when films were made at pH 5 and at polysaccharides/gelatin ratio of 90/10 and 10/90, reaching 0.094 and 0.118 g.mm/h.m 2.kPa as values, respectively. Films with the best mechanical properties were obtained from the blend of polysaccharides, whereas WVP was improved from the blend of polysaccharides and gelatin at pH 5.
Editor: 
Rights: aberto
Identifier DOI: 10.1590/S0101-20612011000300029
Address: http://www.scopus.com/inward/record.url?eid=2-s2.0-80055000569&partnerID=40&md5=519a04330c63d17f8e4e2a2682167348
Date Issue: 2011
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File SizeFormat 
2-s2.0-80055000569.pdf368.76 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.