Title: Tif4 Varnish - A 19f-nmr Stability Study And Enamel Reactivity Evaluation
Author: Nobrega C.B.C.
Fujiwara F.Y.
Cury J.A.
Rosalen P.L.
Abstract: The aim of this study was to develop a titanium tetrafluoride (TiF 4) varnish and evaluate the stability of the formulation and its reactivity with dental enamel. The varnish was prepared in a resinous matrix using ethanol 96% as solvent. Samples (n=45) were aged at 65°C and 30% of relativity humidity (RE n°01/05 - ANVISA) and after 3, 6, 9 and 12 months, nine samples were removed for evaluation and compared with fresh samples. Chemical stability of TiF4 varnish was determinate by 19F-NMR and the reactivity of the formulation was quantified by formation of fluoride loosely (CaF2) and firmly bound (fluorapatite; FA) to enamel. For reactivity comparisons, a varnish without TiF4 was used as control. The loss of soluble fluoride was about 0.9% after one year of storage. The values of the reactivity (mean±S.D.) of fresh, aged at 3, 6, 9 and 12 months and control samples were: CaF2 (μgF/mm 2): 89.3±27.5a; 54.5±14.3b; 51.2±29.8b; 69.3±21.3a; 48.0±27. 4b; 0.10±0.07c, FA (μg F/g): 2477.5±1044.0a; 2484.8±992.0a; 2580.0±1383.9a; 2517.2±929.9a; 2121.0±1059.2a; 330.0±180.0b, respectively. Means followed by distinct letters were statistically different (p<0.05). After one year of storage, the formulation was chemically stable and the levels of FA were maintained. However there was an initial decrease in the ability to form CaF2. © 2008 Pharmaceutical Society of Japan.
Rights: aberto
Identifier DOI: 10.1248/cpb.56.139
Date Issue: 2008
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File SizeFormat 
2-s2.0-38049188144.pdf77.85 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.