Please use this identifier to cite or link to this item:
|Type:||Artigo de evento|
|Title:||Rheological Behaviour And Microstructural Evolution Of Semi-solid A356 Alloy Produced By Different Routes|
|Abstract:||Different techniques used to produce semi-solid alloys can result in different structures in the material and, therefore, in distinct rheological behaviours which determine its thixo-forming ability. Suitable raw materials to be used for SSM forming must present non-dendritic, very fine or fragmented structure in order to globularize without excessive agglomeration when re-heated to the semi-solid state. This work analyses the influence of raw material production route on the rheological behaviour of semi-solid A356 alloy. Techniques used were: electromagnetic stirring (EMS) and chemical ultra-refining (UR). Samples were re-heated to 580°C (∼ 0.45 solid fraction) and hold for 0, 90 and 210s to allow the observation of the structure evolution. After structures characterization, the samples were submitted to compression tests, at δH/δt = 10mm/s, in the same temperature/holding time conditions. Viscosity of the differently prepared raw material was related to the grain size, primary particle size, geometrical factor (roundness shape factor and contiguity).|
|Editor:||Trans Tech Publications Ltd|
|Appears in Collections:||Unicamp - Artigos e Outros Documentos|
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.