Please use this identifier to cite or link to this item: http://repositorio.unicamp.br/jspui/handle/REPOSIP/334315
Type: DISSERTAÇÃO DIGITAL
Degree Level: Mestrado
Title: Influência dos parâmetros de usinagem na integridade superficial da liga biomédica de CoCr ASTM F75
Title Alternative: Influence of machining parameters on the surface integrity of the CoCr ASTM F75 biomedical alloy
Author: Barbosa, Luciano Wallace Gonçalves, 1994-
Advisor: Hassui, Amauri, 1967-
Abstract: Resumo: O objetivo do presente trabalho é analisar a influência dos parâmetros de usinagem na integridade superficial da liga de CoCr ASTM F75 após o torneamento. Entende-se por integridade superficial a descrição da qualidade de uma superfície. Os parâmetros analisados neste trabalho para avaliação da integridade superficial são a rugosidade, microdureza, deformações plásticas e fadiga. Os corpos de prova foram usinados com duas velocidades de corte (20 e 40 m/min) e dois valores de avanços distintos (0,05 e 0,15 mm/rot). A microdureza sofreu um aumento de quase duas vezes após a usinagem, o que indica o encruamento da superfície devido às altas temperaturas na área de corte, somadas ao resfriamento causado pelo fluido de corte. Como era de se esperar, o avanço foi o parâmetro que exerceu maior influência na rugosidade. Já a vida em fadiga do material teve relação direta com as deformações plásticas causadas na superfície pela ferramenta de corte. Observou-se que em velocidades de corte maiores, as deformações foram menos pronunciadas, o que pode ser atribuído à temperatura na área de corte mais elevada, o que facilita a usinagem do material (que é considerado de baixa usinabilidade). Em relação à vida em fadiga do material, ela também teve relação com a velocidade de corte, mas pouca relação com o avanço, que seria o esperado

Abstract: The aim of the present work is to analyze the influence of machining parameters on the surface integrity of the CoCr ASTM F75 alloy after turning. Surface integrity is the description of the quality of a surface. The parameters analyzed in this work to evaluate the surface integrity are roughness, microhardness, plastic deformations and fatigue. The specimens were machined with two cutting speed (20 and 40 m/min) and two different feed rates (0.05 and 0.15 mm/rev). The microhardness has increased almost twice after machining, which indicates work hardening due to high temperatures in the cutting area, added to the cooling caused by the cutting fluid. As expected, the feed rate was the parameter that exerted the greatest influence on the roughness. The fatigue life of the material was directly related to the plastic deformations caused by the cutting tool on the surface. It was observed that at higher cutting speeds, deformations were less pronounced, which can be attributed to the temperature in the higher cutting area, which facilitates the machining of the material (which is considered to be of low machinability). In relation to fatigue life of the material, it also had relation with the speed of cut, but less relation with the feed rate, that would be the expected one
Subject: Medidas de superfície
Usinagem
Torneamento
Ligas de cobalto
Fadiga
Language: Português
Editor: [s.n.]
Citation: BARBOSA, Luciano Wallace Gonçalves. Influência dos parâmetros de usinagem na integridade superficial da liga biomédica de CoCr ASTM F75. 2019. 1 recurso online (130 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica, Campinas, SP.
Date Issue: 2019
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Barbosa_LucianoWallaceGoncalves_M.pdf3.85 MBAdobe PDFView/Open